Antirust coating for mechanical device and preparation method of antirust coating

A technology for anti-rust coatings and mechanical equipment, applied in the direction of anti-corrosion coatings, anti-fouling/underwater coatings, epoxy resin coatings, etc., can solve the problems of poor heat resistance and poor corrosion resistance of anti-rust coatings, and achieve stable performance, Strong adhesion and prolonging the service life

Inactive Publication Date: 2018-10-16
ANHUI TONGSHENG RING
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are problems such as poor corrosion resistance and poor heat resistance in the anti-rust coating.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antirust coating for mechanical device and preparation method of antirust coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This embodiment relates to a kind of antirust paint for mechanical equipment, including the following raw materials in parts by weight: 20 parts of phenolic resin, 15 parts of epoxy resin, 10 parts of silicon acrylic emulsion, 4 parts of tetraethylamine tetrafluoroborate, cellulose acetate 2 parts of prime, 3 parts of dibutyl phthalate, 2 parts of strontium chromate, 3 parts of rosin, 2 parts of iron oxide, 1 part of nano-silver, 2 parts of modified bamboo powder, 1 part of dispersant, 2 parts of thickener , 3 parts of stabilizer and 15 parts of deionized water.

[0029] Wherein, the preparation method of described modified bamboo powder is as follows:

[0030] First soak the bamboo powder in a dilute nitric acid solution with a mass fraction concentration of 4% for 4 hours, then ultrasonically treat it at an ultrasonic frequency of 22kHz and a power of 758W for 20min, then add an equivalent amount of sodium polyacrylate under stirring, heat up to 80°C for 45min, and re...

Embodiment 2

[0042] This embodiment relates to a kind of antirust paint for mechanical equipment, including the following raw materials in parts by weight: 30 parts of phenolic resin, 25 parts of epoxy resin, 20 parts of silicon acrylic emulsion, 8 parts of tetraethylamine tetrafluoroborate, cellulose acetate 3 parts of prime, 6 parts of dibutyl phthalate, 5 parts of strontium chromate, 9 parts of rosin, 4 parts of iron oxide, 3 parts of nano-silver, 7 parts of modified bamboo powder, 4 parts of dispersant, 4 parts of thickener , 5 parts of stabilizer and 25 parts of deionized water.

[0043] Wherein, the preparation method of described modified bamboo powder is as follows:

[0044] First soak the bamboo powder in a dilute nitric acid solution with a mass fraction concentration of 4% for 4 hours, then ultrasonically treat it at an ultrasonic frequency of 22kHz and a power of 758W for 20min, then add an equivalent amount of sodium polyacrylate under stirring, heat up to 80°C for 45min, and ...

Embodiment 3

[0056] This embodiment relates to a kind of antirust paint for mechanical equipment, including the following raw materials in parts by weight: 22 parts of phenolic resin, 17 parts of epoxy resin, 13 parts of silicon acrylic emulsion, 5 parts of tetraethylamine tetrafluoroborate, cellulose acetate 2.1 parts of prime, 4 parts of dibutyl phthalate, 3 parts of strontium chromate, 4 parts of rosin, 2.4 parts of iron oxide, 1.5 parts of nano-silver, 3 parts of modified bamboo powder, 2 parts of dispersant, 2.6 parts of thickener parts, 3.4 parts of stabilizer and 18 parts of deionized water.

[0057] Wherein, the preparation method of described modified bamboo powder is as follows:

[0058] First soak the bamboo powder in a dilute nitric acid solution with a mass fraction concentration of 4% for 4 hours, then ultrasonically treat it at an ultrasonic frequency of 22kHz and a power of 758W for 20min, then add an equivalent amount of sodium polyacrylate under stirring, heat up to 80°C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses antirust coating for a mechanical device. The antirust coating is prepared from the following raw materials in parts by weight: 20 to 30 parts of phenolic resin, 15 to 25 partsof epoxy resin, 10 to 20 parts of silicone acrylic emulsion, 4 to 8 parts of tetraethylammonium tetrafluoroborate, 2 to 3 parts of cellulose acetate, 3 to 6 parts of dibutyl phthalate, 2 to 5 parts of strontium chromate, 3 to 9 parts of rosin, 2 to 4 parts of iron oxide, 1 to 3 parts of nano silver, 2 to 7 parts of modified bamboo powder, 1 to 4 parts of dispersing agent, 2 to 4 parts of thickening agent, 3 to 5 parts of stabilizer, and 15 to 25 parts of deionized water. By controlling the original types and proportion, the prepared antirust coating is low in cost, good in heat dissipation performance, excellent in heat resistance and salt resistance, and capable of effectively prolonging the service life of the machinery.

Description

technical field [0001] The invention belongs to the technical field of mechanical equipment, and in particular relates to an antirust coating for mechanical equipment and a preparation method thereof. Background technique [0002] The rust prevention of mechanical equipment has always been a problem that needs to be paid attention to in the process of industrial production and use. Mechanical equipment mostly uses steel as the material. The main matrix component of steel is iron. Iron is a very active element that is easily oxidized in humid air to form iron oxides. Once oxidized, it not only affects the appearance, but also may seriously affect the function of the product. The anti-corrosion ability of iron element in saline environment is also very unoptimistic. The main cause of corrosion is the pitting effect of chloride ions. In practice, the oxidation of iron and the corrosion of salt often work together, so that the corrosion resistance of steel is very poor. This ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/06C09D163/00C09D133/04C09D5/10C09D5/14C08H8/00
CPCC09D161/06C08H8/00C08K2003/0806C08K2003/2272C08K2201/011C08L2205/035C09D5/10C09D5/14C08L63/00C08L43/04C08L97/02C08K13/02C08K5/12C08K3/22C08K3/08
Inventor 蔡锟赵卓
Owner ANHUI TONGSHENG RING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More