A high-efficiency flame-retardant cable material and its preparation method

A flame-retardant cable, high-efficiency technology, applied in the direction of circuits, electrical components, plastic/resin/wax insulators, etc., can solve the problem of poor flame-retardant performance, deterioration of the mechanical properties of cable materials, and the amount of flame retardant added to flame-retardant cable materials Large and other problems, to achieve the effect of solving poor flame retardancy, improving mechanical properties and flame retardancy, and good corrosion resistance

Active Publication Date: 2020-06-23
HEWTECH (LIANYUNGANG) ELECTRONICS CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems that the existing cable materials have poor flame retardant performance, the addition of flame retardant in the flame retardant cable material is large, and the mechanical properties of the cable material are easily deteriorated, and a high-efficiency flame retardant cable material and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A high-efficiency flame-retardant cable material proposed by the present invention includes the following raw materials in parts by weight: 80 parts of low-density polyethylene, 10 parts of ethylene-vinyl acetate copolymer, 0.4 part of modified aluminum hypophosphite, 0.1 part of morpholine guanidine, 0.5 part of ethylene glycol monostearate, 0.5 part of polypropylene wax, 0.4 part of photocatalyst, 1 part of aluminum-magnesium alloy powder, and 0.2 part of antioxidant; the mass ratio of the modified aluminum hypophosphite is 6:2:9 : 1 aluminum hypophosphite, methylene dicarbamate, phenyl silicone oil, polyimide mixed; the antioxidant is antioxidant 168.

[0021] Its preparation method comprises the following steps:

[0022] S1. According to 80 parts of low-density polyethylene, 10 parts of ethylene-vinyl acetate copolymer, 0.4 parts of modified aluminum hypophosphite, 0.1 part of morpholine guanidine, 0.5 parts of ethylene glycol monoester stearate, and 0.5 parts of po...

Embodiment 2

[0027] A high-efficiency flame-retardant cable material proposed by the present invention includes the following raw materials in parts by weight: 100 parts of low-density polyethylene, 13 parts of ethylene-vinyl acetate copolymer, 1.5 parts of modified aluminum hypophosphite, 0.25 parts of morpholine guanidine, 1.5 parts of ethylene glycol monostearate, 2 parts of polypropylene wax, 0.9 parts of photocatalyst, 3 parts of aluminum-magnesium alloy powder, and 0.4 parts of antioxidant; the mass ratio of the modified aluminum hypophosphite is 6:2:9 : 1 aluminum hypophosphite, methylene dicarbamate, phenyl silicone oil, polyimide mixed; the antioxidant is antioxidant 626.

[0028] Its preparation method comprises the following steps:

[0029] S1, according to 100 parts of low-density polyethylene, 13 parts of ethylene-vinyl acetate copolymer, 1.5 parts of modified aluminum hypophosphite, 0.25 parts of morpholine guanidine, 1.5 parts of ethylene glycol monoester stearate, and 2 par...

Embodiment 3

[0034]A high-efficiency flame-retardant cable material proposed by the present invention includes the following raw materials in parts by weight: 120 parts of low-density polyethylene, 15 parts of ethylene-vinyl acetate copolymer, 3.2 parts of modified aluminum hypophosphite, 0.4 parts of morpholine guanidine, 3 parts of ethylene glycol monostearate, 3 parts of polypropylene wax, 1.6 parts of photocatalyst, 4 parts of aluminum-magnesium alloy powder, 0.5 part of antioxidant; the mass ratio of the modified aluminum hypophosphite is 6:2:9 : 1 aluminum hypophosphite, methylene dicarbamate, phenyl silicone oil, polyimide mixed; the antioxidant is antioxidant 1010.

[0035] Its preparation method comprises the following steps:

[0036] S1, according to 120 parts of low-density polyethylene, 15 parts of ethylene-vinyl acetate copolymer, 3.2 parts of modified aluminum hypophosphite, 0.4 parts of morpholine guanidine, 3 parts of ethylene glycol monostearate, and 3 parts of polypropyle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides an efficient flame-retardant cable material and a preparation method thereof, the efficient flame-retardant cable material comprises low-density polyethylene, ethylene-vinyl acetate copolymers, modified aluminum hypophosphite, moroxydine, glycol monostearate, polypropylene wax, photocatalysts, aluminum magnesium alloy powder and antioxidants, the modified aluminum hypophosphite is prepared by mixing aluminum hypophosphite with methylene methylenedicarbamate, phenyl silicone oil and polyimide according to the mass ratio of 6:2:9:1, the preparation method of the efficientflame-retardant cable material includes the following steps of S1, weighing raw materials; S2, dispersing moroxydine into modified aluminum hypophosphite; S3, mixing the raw materials; S4, performingdrawing, dicing, squeezing and pelleting to obtain the efficient flame-retardant cable material, the efficient flame-retardant cable material and the preparation method thereof have the advantages that the formula is reasonable, the addition quantity of the raw materials playing a flame-retardant role is low, the preparation method is simple, and the obtained cable material has high resistance toageing, bacteria, corrosion and fire and excellent mechanical property.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a high-efficiency flame-retardant cable material and a preparation method thereof. Background technique [0002] Cable is a wire product used to transmit electric energy, magnetic energy, information and realize electromagnetic energy conversion. The cable is mainly composed of a conductor, a conductor shield, an insulation layer, an insulation shield, a buffer layer, a metal sheath, and an outer sheath. Most of the outer sheaths are located on the outermost layer of the cable to protect the cable. At present, plastics and rubber are mostly used as the main materials. However, the traditional cables have poor flame retardancy and are prone to fire, causing property damage and casualties. Therefore, researchers are paying more and more attention to the problem of poor flame retardancy of cable materials. At first, the improvement of the flame retardant properties of cabl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/08C08L23/12C08K13/06C08K9/06C08K9/04C08K3/32C08K5/103C08K3/08C08K5/357H01B3/44
CPCC08K2003/0812C08L23/06C08L2201/02C08L2201/08C08L2203/202C08L2205/03C08L2207/066H01B3/441C08L23/0853C08L23/12C08K13/06C08K9/08C08K9/04C08K3/32C08K5/103C08K3/08C08K5/357
Inventor 尚晴
Owner HEWTECH (LIANYUNGANG) ELECTRONICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap