Method used for preparing transparent zinc oxide liquid phase dispersion

A technology of transparent zinc oxide and liquid phase dispersion, which is applied in chemical instruments and methods, zinc oxide/zinc hydroxide, dyed organosilicon compound treatment, etc. It can solve the problems of poor compatibility and achieve easy operation, simple process flow, good stability effect

Active Publication Date: 2019-01-11
BEIJING UNIV OF CHEM TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The method adopts a high-gravity rotating packed bed, which can greatly enhance mass transfer and micro-mixing. The morphology of the prepared zinc oxide particles is controllable and the particle size distribution is uniform. The transparent zinc oxide particles prepared by this method are further modified. The solid content of the zinc oxide liquid phase dispersion can reach 70wt%, the zinc oxide crystal particle size is small and evenly distributed, and the one-dimensional size is 3-10nm; in addition, the product has good dispersion effect and good stability, and there is no sedimentation after standing for several months. And water and various organic solvents are used as the liquid phase dispersion medium, which has a wide range of applications; this method solves the problem of poor dispersion performance and compatibility of nano-zinc oxide in the application, thus endowing the product with higher application performance and added value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method used for preparing transparent zinc oxide liquid phase dispersion
  • Method used for preparing transparent zinc oxide liquid phase dispersion
  • Method used for preparing transparent zinc oxide liquid phase dispersion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A kind of preparation of transparent zinc oxide liquid phase dispersion, comprises the steps:

[0055] 1) Add 1000 g of zinc acetate methanol mixed solution A with a mass concentration of 11% into the reactant storage tank A, stir and dissolve and heat to 70° C.; add 1000 g of potassium hydroxide ethanol mixed solution B with a mass concentration of 5.26% into the reactant storage tank In tank B, stir to dissolve and heat to 55°C;

[0056] 2) Turn on the circulating water at 70°C to heat the bed body of the supergravity rotary bed. After the temperature stabilizes, turn on the rotary bed and adjust the rotation speed to 1800rpm; turn on the feed pump, and the feed flow rate is 200ml / min, and the two reactants are simultaneously transported to React in a rotating bed;

[0057] 3) After the feeding of mixed solution A and mixed solution B is completed, all the suspension obtained from the reaction flows out of the supergravity rotating device and enters the modified tank...

Embodiment 2

[0061] A kind of preparation of transparent zinc oxide liquid phase dispersion, comprises the steps:

[0062] 1) Add 1000 g of zinc acetate and 0.4% gallium nitrate methanol mixed solution A with a mass concentration of 8% into the reactant storage tank A, stir and dissolve and heat to 50°C; Add 1000g of B into the reactant storage tank B, stir and dissolve at room temperature;

[0063] 2) Turn on the circulating water at 50°C to heat the bed body of the supergravity rotary bed. After the temperature stabilizes, turn on the rotary bed and adjust the rotation speed to 1000rpm; turn on the feed pump, and the feed flow rate is 500ml / min, and the two reactants are simultaneously transported to React in a rotating bed;

[0064] 3) After the zinc salt solution and lye are fed, all the suspension obtained from the reaction flows out of the supergravity rotating device and enters the modified tank, then closes the supergravity rotating device, and gradually adds 24g of mixing coating...

Embodiment 3

[0068] A kind of preparation of transparent zinc oxide liquid phase dispersion, comprises the steps:

[0069] 1) Add 1000 g of zinc acetate and 0.4% gallium nitrate methanol mixed solution A with a mass concentration of 8% into the reactant storage tank A, stir and dissolve and heat to 50°C; Add 1000g of B into the reactant storage tank B, stir and dissolve at room temperature;

[0070] 2) Turn on the circulating water at 50°C to heat the bed body of the supergravity rotary bed. After the temperature stabilizes, turn on the rotary bed and adjust the rotation speed to 1600rpm; turn on the feed pump, and the feed flow rate is 400ml / min, and the two reactants are simultaneously transported to React in a rotating bed;

[0071] 3) After the zinc salt solution and lye are fed, all the suspension obtained from the reaction flows out of the supergravity rotating device and enters the modified tank, then close the supergravity rotating device, and gradually add butyl titanate to the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method used for preparing a transparent zinc oxide liquid phase dispersion. The method comprises following steps: 1, a salt is dissolved in a liquid phase medium A so as to obtain a salt solution, an alkali is dissolved in a liquid phase medium B so as to obtain an alkali solution, an adopted salt is a zinc salt or a mixed zinc salt, wherein the mixed zinc salt is prepared through mixing of a zinc salt and a doping element at a molar ratio of 10-100:1; 2, the salt solution and the alkali solution are introduced into a hypergravity rotation packed bed reactor, reactionis carried out a certain temperature so as to obtain a zinc oxide suspending liquid; 3, a surface coating agent is added into the zinc oxide suspending liquid for a certain time of modifying coatingat a certain temperature; and 4, an obtained modifying solution is allowed to stand, is subjected to precipitation, centrifugation, and washing, and is dispersed in a liquid phase medium C so as to obtain the transparent zinc oxide liquid phase dispersion. The preparation process is completed in the hypergravity rotation packed bed reactor, mass transfer and microscopic mixing are reinforced greatly; the obtained product is transparent, and excellent in dispersibility and stability; and no precipitation is caused after longer than 12 months of standing.

Description

technical field [0001] The invention belongs to the technical field of chemical industry and relates to a preparation method of a liquid phase dispersion, in particular to a method for preparing a transparent zinc oxide liquid phase dispersion. Background technique [0002] As an important inorganic nanomaterial, nano-zinc oxide research started in the 1990s. Zinc oxide is widely used nowadays. In addition to being widely used in the rubber industry, petrochemical industry, and paint industry, it can also be used in electronic laser materials, phosphor additives, magnetic materials, piezoelectric materials, ceramics, etc. In the rubber industry, nano-zinc oxide is an important inorganic active material, which can not only reduce the amount of ordinary zinc oxide, but also improve the wear resistance and anti-aging properties of rubber products, and prolong the service life; in the coating industry, nano-zinc oxide Zinc can greatly improve the hiding power and tinting power ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/04C09C3/04C09C3/06C09C3/08C09C3/10C09C3/12C01G9/02B82Y30/00
CPCB82Y30/00C01G9/02C01P2004/64C09C1/043C09C3/006C09C3/04C09C3/06C09C3/08C09C3/10C09C3/12
Inventor 陈建峰黄谢君曾晓飞王洁欣
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap