Grafted chitosan, and preparation method and application thereof

A chitosan and graft technology, applied in the field of materials, can solve the problems of little anti-clogging, general anti-clogging performance, environmental pollution, etc., and achieve good sustainability, environmental protection, and good environmental protection. , the effect of reducing production costs

Inactive Publication Date: 2019-01-22
WUHAN INSTITUTE OF TECHNOLOGY
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Once such a huge rock and soil mass fails, it will cause major disasters such as landslides and debris flows, causing heavy casualties, property losses and environmental pollution.
[0003] The silting of tailings dams is mainly physical silting and chemical silting. At present, the treatment of silting at home and abroad is mainly carried out by physical methods. Through tailings dam simulation experiments, fluid experiments and establishment of mathematical models, this situation can be changed. A porous media filtration system, which has problems such as low applicability (depending entirely on the internal conditions of the tailings dam), general anti-silting performance, and poor economy, which limits the application of anti-silting in tailings dams
However, there are few researches on anti-silting by chemical methods.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Grafted chitosan, and preparation method and application thereof
  • Grafted chitosan, and preparation method and application thereof
  • Grafted chitosan, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The preparation of graft monomer EDTAD, its preparation steps are as follows:

[0039] Suspend 18g of EDTA (acid) in 31ml of anhydrous pyridine, then add 25ml of anhydride under nitrogen protection, and stir at 65°C for a certain period of time. According to this, the product is cooled and filtered under a stable nitrogen flow, washed with 200ml of anhydrous acetic anhydride and anhydrous acetic anhydride, and finally dried in a vacuum oven at 50-60°C to obtain the grafted monomer EDTAD. The EDTAD obtained by the reaction was tested by infrared.

[0040] The infrared spectrum of the present embodiment gained EDTAD sees figure 1 , in the infrared spectrum of EDTAD at 1809cm -1 and 1765cm -1 Absorption characteristic peaks appear and the low-frequency peak is slightly stronger than the high-frequency peak, which are two characteristic absorption peaks of the C=O stretching vibration absorption of the acid anhydride. These are the characteristic peaks of the cyclic anhy...

Embodiment 2

[0042] Suspend 30g of EDTA (acid) in 50m of anhydrous pyridine, then add 50ml of acid anhydride under nitrogen protection, and stir at 65°C for a certain period of time. According to this, the product was cooled and filtered under a stable nitrogen flow, washed with 200ml of anhydride and ether, and finally dried in a vacuum oven at 50-60°C to obtain the grafted monomer EDTAD. The EDTAD obtained by the reaction was tested by infrared.

[0043] The infrared spectrum of the present embodiment gained EDTAD sees figure 1 , in the infrared spectrum of EDTAD at 1796cm -1 and 1749cm -1 Absorption characteristic peaks appear and the low-frequency peak is slightly stronger than the high-frequency peak, which are two characteristic absorption peaks of the C=O stretching vibration absorption of the acid anhydride. These are the characteristic peaks of the cyclic anhydride. at 1252cm -1 The stretching vibration peak at is the C-O-C stretching vibration peak of the cyclic anhydride, at...

Embodiment 3

[0045] 1g chitosan monomer is completely dissolved with 2ml glacial acetic acid, after a certain period of time, after dissolving, solution is added in 50mlN, in the N-dimethylformamide, then add 1g embodiment 1 gained EDTAD grafting monomer, and at 65 Polymerization reaction was carried out at ℃ and in a nitrogen-enclosed environment until the reaction was complete. After the reaction was completed, it was washed with 50ml of N,N-dimethylformamide and filtered, then washed with 100ml of distilled water for centrifugation, and then washed with 100ml of saturated sodium bicarbonate solution for centrifugation. , then wash with 100ml of distilled water and carry out centrifugation, finally wash with 50ml of 95% ethanol and carry out centrifugation, place it in a vacuum oven and dry it at 70°C to obtain the chitosan graft of the present invention.

[0046] The chitosan graft obtained is placed in the calcium solution of configuration and adsorbed for 2h, and the solution after ads...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a grafted chitosan, and a preparation method and an application thereof. The method comprises the following steps: dissolving chitosan in an acidic solution, and mixing the obtained solution with an organic solvent; adding an ethylenediamine tetraacetic dianhydride graft monomer (EDTAD), and carrying out a grafting polymerization reaction at 60-80 DEG C under the protectionof an inert gas; and washing and drying the obtained reaction product after the completion of the reaction in order to obtain the grafted chitosan. The grafting reaction is an acylation reaction of chitosan, and the reaction process is simple, and is easy to handle. The adsorption performance of the above chelated adsorbent can be controlled by changing a mass ratio of a host to the graft monomerand the reaction conditions. Metal ions adsorbed by the adsorbent can be recovered by an elution process and the adsorbent can be continuously used, and has good sustainability and a good environmental protection property.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a chitosan graft and its preparation method and application. Background technique [0002] The tailings dam is a dam formed by stacking and rolling the tailings. It is mainly used to store the tailings or industrial waste discharged from metal and non-metal mines after sorting ore. Under normal circumstances, the height of the dam body can reach tens of meters or even hundreds of meters. The tailings reservoir is different from the reservoir in the usual concept. The reservoir needs to raise the water level, so the dam body is mainly used for seepage prevention, while the tailings reservoir needs seepage drainage, otherwise the water level will be raised and the dam will easily break. There are stagnation ions (such as calcium ions and ferrous ions) in the waste liquid in the dam, which precipitate in a specific chemical environment to form water-insoluble compound...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More