Ocean cable sheath material with high strength and strong corrosion resisting performance

A cable sheath and corrosion-resistant technology, applied in the field of cable materials, can solve problems such as difficult to satisfy people, achieve the effects of improving hardness and corrosion resistance, reasonable composition ratio, and stable performance parameters

Inactive Publication Date: 2019-01-25
TONGLING CITY TONGDOU SPECIAL CABLE CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing submarine sheath cable materials are still difficult to meet people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0011] A marine cable sheath material with high strength and strong corrosion resistance, which is composed of the following raw materials in parts by weight: 61 parts of nitrile rubber, 22 parts of polyvinyl alcohol resin, 20 parts of polytetrafluoroethylene, and 8 parts of ammonium bicarbonate , 5 parts of barium stearate, 3 parts of vinyltrimethoxysilane, 6 parts of polytetramethylene ether glycol, 4 parts of sodium dialkyl sulfonate, 3 parts of manganese acetate, 4 parts of sodium chromate, hexamethylene oxide 3 parts methyltetramine, 4 parts benzyl silicone oil, 8 parts zinc oxide, 3 parts ammonia water, 6 parts borax, 4 parts white carbon black, 5 parts glass fiber, 2 parts talcum powder, 4 parts liquid paraffin, titanium dioxide 5 parts, 3 parts of antioxidant BHT, 4 parts of maleic anhydride graft compatibilizer, 3 parts of vulcanizing agent, 3 parts of antioxidant.

[0012] The vulcanizing agent is one or more mixtures of sulfur, benzoyl peroxide or urethane; the anti...

specific Embodiment 2

[0013] A marine cable sheath material with high strength and strong corrosion resistance, which is composed of the following raw materials in parts by weight: 57 parts of nitrile rubber, 21 parts of polyvinyl alcohol resin, 17 parts of polytetrafluoroethylene, and 5 parts of ammonium bicarbonate , 3 parts of barium stearate, 2 parts of vinyltrimethoxysilane, 4 parts of polytetramethylene ether glycol, 3 parts of sodium dialkyl sulfonate, 2 parts of manganese acetate, 3 parts of sodium chromate, hexamethylene oxide 2 parts methyltetramine, 3 parts benzyl silicone oil, 5 parts zinc oxide, 2 parts ammonia water, 4 parts borax, 3 parts white carbon black, 4 parts glass fiber, 2 parts talcum powder, 3 parts liquid paraffin, titanium dioxide 4 parts, antioxidant BHT 2 parts, maleic anhydride graft compatibilizer 3 parts, vulcanizing agent 2 parts, antioxidant 2 parts.

[0014] The vulcanizing agent is one or more mixtures of sulfur, benzoyl peroxide or urethane; the antiaging agent ...

specific Embodiment 3

[0015] A marine cable sheath material with high strength and strong corrosion resistance, which is composed of the following raw materials in parts by weight: 53 parts of nitrile rubber, 19 parts of polyvinyl alcohol resin, 15 parts of polytetrafluoroethylene, and 3 parts of ammonium bicarbonate , 2 parts of barium stearate, 1 part of vinyltrimethoxysilane, 2 parts of polytetramethylene ether glycol, 1 part of sodium dialkylsulfonate, 1 part of manganese acetate, 2 parts of sodium chromate, hexamethylene oxide 1 part of methyltetramine, 1 part of benzyl silicone oil, 3 parts of zinc oxide, 1 part of ammonia water, 2 parts of borax, 1 part of silica, 1 part of glass fiber, 1 part of talc, 2 parts of liquid paraffin, titanium dioxide 2 parts, 1 part of antioxidant BHT, 2 parts of maleic anhydride graft compatibilizer, 1 part of vulcanizing agent, and 1 part of antioxidant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an ocean cable sheath material with high strength and strong corrosion resisting performance. The ocean cable sheath material is prepared from the following raw materials in parts by weight: 53 to 68 parts of acrylonitrile-butadiene rubber, 19 to 24 parts of polyvinyl alcohol resin, 15 to 21 parts of polytetrafluoroethylene, 3 to 9 parts of ammonium bicarbonate, 2 to 6 parts of barium stearate, 1 to 4 parts of vinyl trimethoxy silane, 2 to 7 parts of polytetramethylene ether glycol, 1 to 5 parts of sodium dialkyl sulfate, 1 to 4 parts of manganese acetate, 2 to 5 partsof sodium chromate, 1 to 4 parts of hexamethylenetetramine, 1 to 5 parts of phenylmethyl silicone oil, 3 to 10 parts of zinc oxide, 1 to 4 parts of ammonia water, 2 to 7 parts of borax, 1 to 5 parts of white carbon black, 1 to 6 parts of glass fibers, 1 to 2 parts of talcum powder, 2 to 5 parts of liquid paraffin wax, 2 to 6 parts of titanium white powder, 1 to 4 parts of an antioxidant BHT, 2 to5 parts of a maleic anhydride grafted compatibilizer, 1 to 4 parts of a vulcanizing agent and 1 to 4 parts of an anti-ageing agent. By adopting the ocean cable sheath material, the rigidity and the corrosion resisting performance of a cable sheath are improved. The cable sheath material is reasonable in component ratio and has good chemical stability and corrosion resisting performance; parametersare not greatly changed under acid, alkali and salt and damp and hot conditions, and the performance parameters are stable.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to a marine cable sheath material with high strength and strong corrosion resistance. Background technique [0002] The ocean can provide human beings with material resources, space resources and energy for survival and development. my country is a big maritime country with a coastline of more than 18,000 kilometers, more than 6,500 coastal islands, and over 3 million square kilometers of sea area under its jurisdiction. my country has abundant marine resources and a booming marine industry, but the marine environment is very harsh and highly corrosive. Seawater itself is a strong corrosive medium. At the same time, waves, waves, tides, and currents generate low-frequency reciprocating stress and Shock, coupled with marine microorganisms, attached organisms and their metabolites, all directly or indirectly accelerate the corrosion process. Marine corrosion is mainly localiz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/02C08L29/04C08L27/18C08K13/04C08K7/14C08K5/098C08K3/38C08K3/36
CPCC08K2003/387C08L9/02C08L2203/202C08L2205/035C08L29/04C08L27/18C08K13/04C08K7/14C08K5/098C08K3/38C08K3/36
Inventor 赵家玉
Owner TONGLING CITY TONGDOU SPECIAL CABLE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products