Preparation method of slump-retaining type polycarboxylic acid water reducing agent mother liquor

A technology of water reducer and polycarboxylic acid, which is applied in the field of preparation of slump-preserving polycarboxylate water reducer mother liquor, which can solve the problems of dangerous use and low explosion limit, and achieve convenient transportation, good activity, raw materials and preparation process simple effect

Active Publication Date: 2019-03-01
安徽海螺材料科技股份有限公司 +1
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the explosion limit of ethylene oxide or propylene oxide is extremely low, it is particularly dangerous to use. It is not possible to use epoxy monomers such as ethylene oxide or propylene oxide to react directly with polycarboxylate water reducers. suitable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of slump-retaining type polycarboxylic acid water reducing agent mother liquor
  • Preparation method of slump-retaining type polycarboxylic acid water reducing agent mother liquor
  • Preparation method of slump-retaining type polycarboxylic acid water reducing agent mother liquor

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036]The present invention proposes a method for preparing a slump-preserving polycarboxylate superplasticizer mother liquor, which uses the by-product epoxy compound and polycarboxylate superplasticizer prepolymer in the production process of organosilane coupling agent to directly carry out Ring-opening esterification reaction (ring-opening esterification of carboxylic acid groups and epoxy groups) to generate polycarboxylate superplasticizers, thereby adjusting the length and density of the side chains of polycarboxylate superplasticizers, giving polycarboxylate water-reducing agents The effect of anti-slump agent, in which organosilane coupling agent includes but not limited to γ-(2,3-epoxypropoxy)hydrocarbyl silane coupling agent including KH560, also includes γ-(2,3-epoxy Propoxy)-Propyltriethoxysilane, γ-(2,3-Glycidoxy)-Propylmethyldimethoxysilane, γ-(2,3-Glycidoxy)-Propyl Methyldiethoxysilane. When producing these organosilane coupling agents, the by-products used fo...

Embodiment 1

[0054] (1) Preparation of polycarboxylate superplasticizer prepolymer: 0.082mol 3-methyl-3-butyl-1-polyethylene glycol (2500g / mol) and 0.115mol acrylic acid in unsaturated polyether monomer Under the action of 0.00082mol ammonium persulfate, 0.00246mol ferrous sulfate and 0.00082mol mercaptoacetic acid, keep 80°C for water phase free radical polymerization for 3 hours to obtain polycarboxylate superplasticizer prepolymer;

[0055] (2) Preparation method of slump-preserving polycarboxylate water reducer: add 23.65g (a total of 0.19mol epoxy compound) of the by-product epoxy compound in the industrial production process of organosilane coupling agent KH560 to the polycarboxylate pre- Polymer (based on carboxyl content of 0.29mol) carries out epoxy ring-opening esterification reaction with carboxyl group, wherein the molar ratio of carboxyl group contained in polycarboxylic acid prepolymer to by-product epoxy compound is 1.54, and the reaction temperature is kept at 80 ℃ for two ...

Embodiment 2

[0057] (1) Preparation of polycarboxylate superplasticizer prepolymer: 0.082mol 3-methyl-3-butyl-1-polyethylene glycol (2500g / mol) and 0.31mol acrylic acid in unsaturated polyether monomer Under the action of 0.0028mol ammonium persulfate, 0.0012mol ferrous sulfate and 0.0074mol mercaptoacetic acid, keep 60°C for water phase free radical polymerization for 4.5 hours to obtain polycarboxylate superplasticizer prepolymer;

[0058] (2) Preparation method of slump-preserving polycarboxylate water reducer: add 23.65g (a total of 0.19mol epoxy compound) of the by-product epoxy compound in the industrial production process of organosilane coupling agent KH560 to the polycarboxylate pre- Polymer (based on carboxyl content of 0.31mol) carries out epoxy ring-opening esterification reaction with carboxyl group, wherein the molar ratio of carboxyl group contained in polycarboxylic acid prepolymer to by-product epoxy compound is 100:62, keep the reaction temperature At 85°C for two hours, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of slump-retaining type polycarboxylic acid water reducing agent mother liquor. The preparation method of the slump-retaining type polycarboxylic acid water reducing agent mother liquor comprises the following steps that 1, unsaturated macromonomer and unsaturated acid are subjected to water phase free radical polymerization reaction for 3-5 hours at heat preservation of 25-80 DEG C under the action of an initiator, a reducing agent and a chain transfer agent to obtain a polycarboxylic acid water reducing agent prepolymer; and 2, a byproduct epoxycompound in the industrial production process of an organosilane coupling agent is added into the polycarboxylic acid water reducing agent prepolymer, epoxy ring-opening esterification reaction is carried out on carboxyl groups for two hours at 80-90 DEG C, strong alkali is added to adjust a pH value of polymer to 5-6 after the reaction is completed, and water is added to obtain the slump-retaining type polycarboxylic acid water reducing agent with the mass concentration of 10-60%. According to the preparation method of the slump-retaining type polycarboxylic acid water reducing agent mother liquor, the byproduct epoxy compound in the generation process of the organosilane coupling agent and the polycarboxylic acid water reducing agent prepolymer are directly subjected to ring-opening esterification reaction so as to adjust the length and density of a side chain of the polycarboxylic acid water reducing agent and endow the polycarboxylic acid water reducing agent with a slump retainingeffect, and the preparation method of the slump-retaining type polycarboxylic acid water reducing agent mother liquor has the advantages of simple raw materials and preparation process and low cost.

Description

technical field [0001] The invention relates to the technical field of polycarboxylate concrete water-reducer, in particular to a method for preparing a slump-retaining polycarboxylate water-reducer mother liquor. Background technique [0002] The new polycarboxylate superplasticizer is more and more widely used in my country. Its main mechanism of action mainly includes two aspects: one is to adsorb the surface of cement particles through the negatively charged carboxylic acid groups on the main chain of the polymer, so that the cement particles are The second is that the uncharged polymeric side chains are not adsorbed to form a steric repulsion effect. This steric repulsion effect is affected by the number of side chains on the main chain and the length of the side chains. Various polycarboxylate water reducers are prepared based on this mechanism by adjusting the side chain length and side chain density of the copolymer. [0003] But many problems follow, one of the most...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F283/06C08F220/06C08F222/02C08F8/00C04B24/26C04B103/30
CPCC04B24/2605C04B2103/302C08F8/00C08F283/065C08F220/06C08F222/02
Inventor 张瑞涛明金龙江元华陈文韬
Owner 安徽海螺材料科技股份有限公司