A kind of fluorescent perovskite nanocrystal and its preparation method and application

A perovskite and nanocrystal technology, applied in the field of semiconductor nanomaterial preparation, can solve the problems of limited practical application, inability to meet the storage and protection of confidential information, photoinduced phase transformation can not be repeated, etc., to increase security and fluorescence performance. Excellent, easy-to-synthesize results

Active Publication Date: 2021-12-03
SHANGHAI JIAOTONG UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method and material still cannot meet the needs of storage and protection of confidential information, because as the ink for recording information, the two-dimensional perovskite material itself still has blue fluorescence characteristics, which leads to the fact that the information recorded by it is in the light. It can still be recognized by the naked eye under excitation; secondly, this photoinduced phase inversion process cannot be repeated, which also limits its practical application
At present, there are no reports on the application of fluorescent perovskite nanocrystals in the field of confidential information storage and protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of fluorescent perovskite nanocrystal and its preparation method and application
  • A kind of fluorescent perovskite nanocrystal and its preparation method and application
  • A kind of fluorescent perovskite nanocrystal and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Synthesis of methylaminolead bromide (MAPbBr) based on Pb-MOF 3 )Nanocrystalline

[0037] (1) Synthesis of Pb-MOF: 90mL 1,3,5-H 3 BTC aqueous solution (0.01M) and 10mL Pb(NO 3 ) 2 The aqueous solution (0.09M) was mixed and stirred continuously for 30 minutes, the obtained powder was washed three times with deionized water and methanol, and finally dried in vacuum at 150°C for 12 hours;

[0038] (2) MAPbBr 3 Synthesis of nanocrystals: Disperse 200 mg of synthesized Pb-MOF powder in 10 mL of n-hexane to form a suspension, and stir to make it uniformly dispersed. Dissolve 10 mg of aminobromide (MABr) in 1 mL of n-butanol, and sonicate to dissolve it completely. Add 0.5mL of the above MABr solution to the Pb-MOF suspension quickly, and keep stirring for 30s, then filter or centrifuge the above dispersion, and wash with butanol once to remove the unreacted MABr, then the MOF embedded in MAPbBr 3 Nanocrystalline powder. The Pb-MOF prepared in this example is as figur...

Embodiment 2

[0040] Synthesis of cesium lead bromide (CsPbBr) based on Pb-MOF 3 )Nanocrystalline

[0041] (1) Synthesis of Pb-MOF: same as the preparation method in Example 1;

[0042] (2) CsPbBr 3 Synthesis of nanocrystals: similar to the preparation method in Example 1, the difference is that the Pb-MOF dispersion solvent is selected as toluene, and 10 mg of cesium bromide (CsBr) is dissolved in 1 mL of methanol during the preparation of the cationic halide salt solution for the conversion reaction . CsPbBr embedded in MOF prepared in this example 3 The fluorescence spectra of nanocrystalline powders are as follows: Figure 5 It is shown that the fluorescence emission wavelength is 529nm, indicating that the method has good versatility.

Embodiment 3

[0044] Synthesis of mixed halogen perovskites (MAPbI) based on Pb-MOF conversion x Br 3-x-y Cl y )Nanocrystalline

[0045] (1) Synthesis of Pb-MOF: same as the preparation method in Example 1;

[0046] (2) MAPbI x Br 3-x Synthesis of nanocrystals: similar to the preparation method in Example 1, the difference lies in the preparation of the cationic halide salt solution used for the conversion reaction. For x=0, y=3, dissolve 10 mg MACl in 1 mL n-butanol; for x=0, y=1, dissolve 2.32 mg MACl and 7.68 mg MABr in 1 mL n-butanol; for x=0, For y=2, dissolve 5.47 mg MACl and 4.53 mg MABr in 1 mL n-butanol; for x=1, y=0, dissolve 4.15 mg MAI and 5.85 mg MABr in 1 mL n-butanol, for x=2, y =0, 7.40 mg MAI and 2.60 mg MABr were dissolved in 1 mL n-butanol. The mixed halogen perovskite (MAPbI x Br 3-x-y Cl y ) Fluorescence spectra of nanocrystals such as Figure 6 As shown, the fluorescence emission wavelength can be tuned from 406 nm to 746 nm with the change of halogen from C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a kind of fluorescent perovskite nanocrystal and its preparation method and application, and its structure is MOF‑ABX 3 , where MOF and ABX 3 The mass ratio is (1~50):(0.1~5), and the cationic halide salt solution used for perovskite synthesis is added to the metal-organic framework dispersion liquid, and the obtained perovskite nanocrystals are uniformly dispersed in the metal-organic framework crystal, and has good fluorescence properties, and this method is versatile. The synthesis method of the perovskite nanocrystal provided by the invention can be directly used in the storage and protection application of confidential information. Compared with the prior art, the operation process of the present invention is simple and repeatable, the metal-organic framework material and its recorded information are very safe (no absorption and fluorescence characteristics in the visible light range, and cannot be recognized by naked eyes) and the fluorescence characteristics of perovskite nanocrystals Good, so that it can be directly applied in the field of confidential information storage and protection.

Description

technical field [0001] The invention belongs to the technical field of semiconductor nanomaterial preparation, and in particular relates to a perovskite nanocrystal synthesized through repeated conversion of a metal organic framework, a preparation method thereof and an application in storage and protection of confidential information. Background technique [0002] Smart fluorescent materials with stimuli responses have a wide range of applications in fields such as information security. This kind of material generally regulates the arrangement mode of molecules through external stimuli (such as light, electricity, heat, mechanical force, etc.), so as to achieve the purpose of changing the fluorescent signal of the material. Fluorescent materials currently used in this field include various organic compounds, metal complexes, inorganic quantum dots, up-conversion nanoparticles, and so on. However, these materials still have many disadvantages, such as: poor fluorescence per...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/06C09K11/66C09K11/74
CPCC09K11/06C09K11/665C09K11/7435B82Y40/00C01G21/16C09K11/66C09K11/74
Inventor 李良张从阳
Owner SHANGHAI JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com