Construction waste building block for filling wall and production process thereof

A technology of construction waste and filling walls, which is applied in the field of building blocks, can solve the problems that the retarding effect of the retarder needs to be improved, and achieve the effects of slowing down the setting time, wide sources of materials, and simple production processes

Inactive Publication Date: 2019-03-08
谢世琴
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] There are also many reusable resources in construction waste, and we can reprocess them into building blocks for reuse; at the same time, current building blocks will be added with retarders during processing to slow down the solidification of concrete slurry Time is convenient for operation, but the retarding effect of the current retarder needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A construction waste building block for filling walls, consisting of the following raw materials in parts by weight: construction waste 20kg / m 3 , cement 10kg / m 3 , Lime powder 5kg / m 3 , Cinder 5kg / m 3 , gravel 3kg / m 3 , Glycine two retarder 10g / m 3 , foaming agent 15g / m 3 , water reducer 20g / m 3 , tackifier 100g / m 3 .

[0043] The glycine two retarder is specifically a compound formed by the chemical reaction of glycine, phosphorous acid, hydrochloric acid, formaldehyde and liquid caustic soda, wherein the ratio of glycine, phosphorous acid and hydrochloric acid is 1:2.1:2. The prepared buffer is the most effective.

[0044] The specific synthetic method of described glycine two retarders is as follows:

[0045] (1) Add glycine, phosphorous acid and hydrochloric acid into the reaction vessel, add a small amount of water, heat, and keep the reaction temperature between 100-108°C until the reaction liquid is clear and transparent;

[0046] (2) then add formalde...

Embodiment 2

[0068] A construction waste building block for filling walls, consisting of the following raw materials in parts by weight: construction waste 35kg / m 3 , cement 12kg / m 3 , Lime powder 7kg / m 3 , Cinder 9kg / m 3 , gravel 6kg / m 3 , Glycine two retarder 15g / m 3 , foaming agent 20g / m 3 , water reducer 25g / m 3 , tackifier 200g / m 3 .

[0069] The glycine two retarder is specifically a compound formed by the chemical reaction of glycine, phosphorous acid, hydrochloric acid, formaldehyde and liquid caustic soda, wherein the ratio of glycine, phosphorous acid and hydrochloric acid is 1:2.1:2. The prepared buffer is the most effective.

[0070] The specific synthetic method of described glycine two retarders is as follows:

[0071] (1) Add glycine, phosphorous acid and hydrochloric acid into the reaction vessel, add a small amount of water, heat, and keep the reaction temperature between 100-108°C until the reaction liquid is clear and transparent;

[0072] (2) then add formalde...

Embodiment 3

[0094] A construction waste building block for filling walls, consisting of the following raw materials in parts by weight: construction waste 50kg / m 3 , cement 15kg / m 3 , Lime powder 10kg / m 3 , Cinder 12kg / m 3 , Gravel 9kg / m 3 , Glycine two retarder 20g / m 3 , foaming agent 25g / m 3 , water reducing agent 30g / m 3 , viscosifier 300g / m 3 .

[0095]The glycine two retarder is specifically a compound formed by the chemical reaction of glycine, phosphorous acid, hydrochloric acid, formaldehyde and liquid caustic soda, wherein the ratio of glycine, phosphorous acid and hydrochloric acid is 1:2.1:2. The prepared buffer is the most effective.

[0096] The specific synthetic method of described glycine two retarders is as follows:

[0097] (1) Add glycine, phosphorous acid and hydrochloric acid into the reaction vessel, add a small amount of water, heat, and keep the reaction temperature between 100-108°C until the reaction liquid is clear and transparent;

[0098] (2) then ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a construction waste building block for a filling wall and a production process thereof. The construction waste building block is prepared from the following raw materials in parts by weight: 20 to 50 kg / m<3> of construction waste, 10 to 15 kg / m<3> of cement, 5 to 10 kg / m<3> of lime powder, 5 to 12 kg / m<3> of col slag, 3 to 9 kg / m<3> of gravel, 10 to 20g / m<3> of foaming agents, 15 to 25g / m<3> of glycine 2 retarders, 20 to 30g / m<3> of water reducing agents and 100 to 300g / m<3> of tackifiers. The construction waste is prepared from concrete waste materials, waste mortar,waste metal, brick and tile fragments, muck and waste asbestos boards. The glycine 2 retarders used in the process can retard the slurry solidification time; the sufficient time is provided for the slurry shaping; the phenomenon of slurry solidification before the slurry is used up cannot occur; the shaped building block is subjected to sufficient reaction, so that the intensity and the toughnessof the building block can be improved.

Description

technical field [0001] The invention relates to the technical field of building blocks, in particular to a construction waste block for filling walls and a production process thereof. Background technique [0002] Construction waste refers to the dregs, spoils, waste materials, silt and other wastes generated during the construction, laying or demolition, and repair of various buildings, structures, and pipe networks by construction units or individuals. Classified by source, construction waste can be divided into engineering dregs, decoration waste, demolition waste, engineering mud, etc.; classified by composition, construction waste can be divided into muck, concrete blocks, crushed stones, brick fragments, Waste mortar, mud, asphalt block, waste plastic, waste metal, waste bamboo and wood, etc. [0003] With the acceleration of industrialization and urbanization, the construction industry is also developing rapidly, and the accompanying construction waste is increasing....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C04B38/10C04B40/02
CPCC04B28/02C04B2111/00017C04B18/16C04B22/064C04B18/103C04B14/02C04B22/165C04B24/008C04B24/123C04B22/122C04B24/26C04B2103/0068C04B2103/302C04B38/10C04B40/0263
Inventor 于海峰吕广宏曹文祥张健
Owner 谢世琴
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com