Foaming ceramic damp-proof wood plastic plate and preparation method thereof

A technology for foaming ceramics and wood-plastic panels, which is used in ceramic products, ceramic material production, clay products, etc., can solve problems such as compression resistance, unsatisfactory wear resistance, low service life, decay and failure, etc., to improve environmental adaptability. Ability, long service life, not easy to crack effect

Inactive Publication Date: 2019-03-26
LIUZHOU LIUJING TECH CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, existing wood-plastic panel products have some deficiencies in the actual use process, such as unsatisfactory compressive and wear-resistant properties, and low service life; in addition, wood-plastic panels are prone to mild

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A foamed ceramic moisture-proof wood-plastic board, comprising 10 parts of coal gangue, 10 parts of ceramic brick waste residue, 8 parts of wood powder, 3 parts of glass beads, 4 parts of calcined talc, 3 parts of fluorite, 5 parts of silicon carbide, and expanded graphite 2 parts, 2 parts of zirconia, 1 part of polypropylene fiber, 1 part of antibacterial agent, of which:

[0030] The antibacterial agent is composed of silicone resin with a weight ratio of 3:2:3:2, nano silver oxide, calcium carbonate nano particles, and graphene.

[0031] The preparation method of the foamed ceramic moisture-proof wood-plastic board of this embodiment includes the following steps:

[0032] (1) Add coal gangue and ceramic tile waste residue into the atomization drying tower according to the raw material components to atomize and dry to obtain mixture A, then add mixture A to a ball mill for ball milling, and obtain mixture B after passing through a 100-mesh sieve;

[0033] (2) In the mixture B...

Embodiment 2

[0039] A foamed ceramic moisture-proof wood-plastic board, comprising 20 parts of coal gangue, 20 parts of ceramic brick waste residue, 18 parts of wood powder, 9 parts of glass beads, 12 parts of calcined talc, 10 parts of fluorite, 15 parts of silicon carbide, and expanded graphite 6 parts, 8 parts of zirconia, 4 parts of polypropylene fiber, 3 parts of antibacterial agent, of which:

[0040] The antibacterial agent is composed of silicone resin with a weight ratio of 3:2:3:2, nano silver oxide, calcium carbonate nano particles, and graphene.

[0041] The preparation method of the foamed ceramic moisture-proof wood-plastic board of this embodiment includes the following steps:

[0042] (1) Add coal gangue and ceramic tile waste residue into the atomization drying tower according to the raw material components to atomize and dry to obtain mixture A, then add mixture A to a ball mill for ball milling, and obtain mixture B after passing through a 100-mesh sieve;

[0043] (2) In the mix...

Embodiment 3

[0049] A foamed ceramic moisture-proof wood-plastic board, comprising 12 parts of coal gangue, 12 parts of ceramic brick waste residue, 10 parts of wood powder, 4 parts of glass beads, 6 parts of calcined talc, 5 parts of fluorite, 7 parts of silicon carbide, and expanded graphite 3 parts, 3 parts of zirconia, 2 parts of polypropylene fiber, 1 part of antibacterial agent, of which:

[0050] The antibacterial agent is composed of silicone resin with a weight ratio of 3:2:3:2, nano silver oxide, calcium carbonate nano particles, and graphene.

[0051] The preparation method of the foamed ceramic moisture-proof wood-plastic board of this embodiment includes the following steps:

[0052] (1) Add coal gangue and ceramic tile waste residue into the atomization drying tower according to the raw material components to atomize and dry to obtain mixture A, then add mixture A to a ball mill for ball milling, and obtain mixture B after passing through a 100-mesh sieve;

[0053] (2) In the mixture...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Wear coefficientaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of building materials and especially relates to a foaming ceramic damp-proof wood plastic plate and a preparation method thereof. The foaming ceramic damp-proof wood plastic plate provided by the invention comprises the following raw materials in parts by weight: 10-20 parts of coal gangue, 10-20 parts of ceramic tile residue, 8-18 parts of wood powder,3-9 parts of glass beads, 4-12 parts of calcined talc, 3-10 parts of fluorite, 5-15 parts of silicon carbide, 2-6 parts of expanded graphite, 2-8 parts of zirconium oxide, 1-4 parts of polypropylenefibers and 1-3 parts of antibacterial agent. The preparation method for the foaming ceramic damp-proof wood plastic plate provided by the invention comprises the following steps: (1) spray-drying andsieving; (2) mixing and quickly stirring; (3) mixing and grinding; (4) mixing and pelletizing; (5) die-filling and calcining. The foaming ceramic damp-proof wood plastic plate has excellent compression-resisting and wear-resisting properties, has damp-proof and antibacterial properties, is free from mildewing and deformation after long-term use, is long in service life and has excellent comprehensive mechanical properties. The preparation method is simple and the end product is high in quality.

Description

Technical field [0001] The invention relates to the technical field of building materials, in particular to a foamed ceramic moisture-proof wood-plastic board and a preparation method thereof. Background technique [0002] Wood-plastic composite board is a kind of wood (wood cellulose, plant cellulose) as the basic material, thermoplastic polymer materials (plastics) and processing aids, etc., mixed uniformly and then heated and extruded by mold equipment. The new high-tech, green and environmentally-friendly decorative materials have both the properties and characteristics of wood and plastic. They are new composite materials that can replace wood and plastic. Therefore, the market demand is very large. [0003] However, the existing wood-plastic board products have some shortcomings in the actual use process, such as unsatisfactory compression resistance and wear resistance, and low service life; in addition, the wood-plastic board is prone to mold in a humid environment, resulti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/132C04B33/13C04B33/32C04B38/06
CPCC04B33/131C04B33/1324C04B33/1328C04B33/32C04B38/068C04B2235/3244C04B2235/3291C04B2235/36C04B2235/3826C04B2235/425C04B2235/442C04B2235/445C04B2235/483C04B2235/6567C04B2235/96C04B38/0675Y02P40/60
Inventor 任文强
Owner LIUZHOU LIUJING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka