Flame-retarding type PVC (Polyvinyl Chloride) foaming board and preparation method thereof

A foamed board and flame retardant technology, applied in the field of flame retardant PVC foam board and its preparation, can solve the problems of potential safety hazards, poor flame retardancy, inability to achieve flame retardant effect, etc., and achieve no adverse effects on mechanical properties , good flame retardancy and excellent thermal stability

Inactive Publication Date: 2019-04-09
山东源邦新材料股份有限公司
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the flame retardancy of PVC foam board is poor, and it cannot achieve effective flame retardancy in case of fire, and there are safety hazards in use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A flame-retardant PVC foam board is prepared from the following raw materials in parts by weight:

[0024] 100 parts of PVC with an average degree of polymerization of 700-800, 5 parts of foam regulator, 0.6 parts of foaming agent, 5 parts of brominated polyphenylene ether, 3 parts of urea, 4 parts of calcium-zinc composite stabilizer, 3.5 parts of barium stearate , 8 parts of nano light calcium carbonate, 30 parts of wood flour, 0.5 parts of aluminum stearate, 0.7 parts of oxidized polyethylene wax, 45 parts of dioctyl phthalate.

[0025] The foaming agent is AC foaming agent. The foam regulator is an acrylate foam regulator. The acrylate foam regulator is prepared by emulsion polymerization of the following raw materials in parts by weight: 60 parts of methyl methacrylate, 23 parts of butyl acrylate, 1.2 parts of sodium pyrophosphate, lauryl sulfuric acid 1.8 parts of sodium, 1.2 parts of potassium persulfate, and 150 parts of water.

[0026] The above-mentioned pr...

Embodiment 2

[0033] A flame-retardant PVC foam board is prepared from the following raw materials in parts by weight:

[0034] 100 parts of PVC with an average degree of polymerization of 700-800, 7 parts of foam regulator, 0.8 parts of foaming agent, 3 parts of brominated polyphenylene ether, 2 parts of urea, 3 parts of calcium-zinc composite stabilizer, 2 parts of barium stearate , 5 parts of nano light calcium carbonate, 25 parts of wood flour, 0.4 parts of aluminum stearate, 0.6 parts of oxidized polyethylene wax, 40 parts of dioctyl phthalate.

[0035] The foaming agent is AC foaming agent. The foam regulator is an acrylate foam regulator. The acrylate foam regulator is prepared by emulsion polymerization of the following raw materials in parts by weight: 60 parts of methyl methacrylate, 23 parts of butyl acrylate, 1.2 parts of sodium pyrophosphate, lauryl sulfuric acid 1.8 parts of sodium, 1.2 parts of potassium persulfate, and 150 parts of water.

[0036] The above-mentioned prep...

Embodiment 3

[0043] A flame-retardant PVC foam board is prepared from the following raw materials in parts by weight:

[0044] 100 parts of PVC with an average degree of polymerization of 700-800, 2 parts of foaming regulator, 0.5 parts of foaming agent, 8 parts of brominated polyphenylene ether, 5 parts of urea, 5 parts of calcium-zinc composite stabilizer, 5 parts of barium stearate , 12 parts of nano light calcium carbonate, 35 parts of wood flour, 0.6 parts of aluminum stearate, 0.8 parts of oxidized polyethylene wax, and 50 parts of dioctyl phthalate.

[0045] The foaming agent is AC foaming agent. The foam regulator is an acrylate foam regulator. The acrylate foam regulator is prepared by emulsion polymerization of the following raw materials in parts by weight: 60 parts of methyl methacrylate, 23 parts of butyl acrylate, 1.2 parts of sodium pyrophosphate, lauryl sulfuric acid 1.8 parts of sodium, 1.2 parts of potassium persulfate, and 150 parts of water.

[0046] The above-mentio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flame-retarding type PVC (Polyvinyl Chloride) foaming board and a preparation method thereof and belongs to the technical field of PVC foaming boards. The flame-retarding type PVC foaming board is prepared from the following raw materials in parts by weight: 100 parts of PVC with the average degree of polymerization, 2-7 parts of foaming regulator, 0.5-0.8 part of foamingagent, 3-8 parts of brominated polyphenyl ether, 2-5 parts of urea, 3-5 parts of calcium-zinc stabilizer, 2-5 parts of barium stearate, 5-12 parts of nanometer light calcium carbonate, 25-35 parts ofwood meal, 0.4-0.6 part of aluminium stearate, 0.6-0.8 part of oxidized polyethlene wax and 40-50 parts of dioctyl phthalate. The flame-retarding type PVC foaming board and the preparation method disclosed by the invention has the beneficial effects that by addition of the flame-retarding agent brominated polyphenyl ether and urea into a production formula of the PVC foaming board, the prepared PVC foaming board has good flame-retarding property, and the safety property of the PVC foaming board is improved; simultaneously, by combination with other additives, the toughness and the mechanicalstrength of the PVC foaming board are also improved.

Description

technical field [0001] The invention relates to the technical field of PVC foam board production, in particular to a flame-retardant PVC foam board and a preparation method thereof. Background technique [0002] PVC foam board, also known as Chevron board and Andy board, uses polyvinyl chloride (PVC) as the main raw material and adds various additives. It is a new type of green and environmentally friendly material. At present, the PVC industry is developing rapidly all over the world with broad prospects. All countries are optimistic about the potential of PVC and its benefits to the ecological environment. PVC is proving to the world with its superior and unique performance that its role and status cannot be replaced by any other products at present. of. PVC foam board is widely used in shipbuilding, train manufacturing, furniture making, decoration, silk screen printing of advertising industry, making and other industries. When it is processed at the same level as wood, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L71/12C08L97/02C08L23/30C08L33/12C08K13/02C08K5/21C08K5/098C08K3/26C08K5/12C08J9/10
CPCC08J9/0023C08J9/0028C08J9/0061C08J9/0071C08J9/0085C08J9/0095C08J9/103C08J2203/04C08J2327/06C08J2423/30C08J2433/12C08J2471/12C08J2497/02C08K5/098C08K5/12C08K5/21C08K13/02C08K2003/265
Inventor 朱兰明
Owner 山东源邦新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com