Cationic resin catalyst, preparation method thereof and catalytic application thereof in preparation of glycolic acid by methyl glycolate hydrolysis method

A technology of cationic resin and methyl glycolate, which is applied in chemical instruments and methods, physical/chemical process catalysts, organic compound/hydride/coordination complex catalysts, etc., can solve the problem of increased separation cost and conversion of methyl glycolate Low efficiency and other problems, to achieve the effect of increasing conversion rate, promoting complete hydrolysis, and shortening the process flow

Pending Publication Date: 2019-04-12
丹东明珠特种树脂有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the hydrolysis of methyl glycolate is a reversible reaction, restricted by chemical balance, a large amount of unhydrolyzed methyl glycolate in the reaction system needs to be recovered, resulting in inc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cationic resin catalyst, preparation method thereof and catalytic application thereof in preparation of glycolic acid by methyl glycolate hydrolysis method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1 Catalyst A

[0020] Suspension copolymerization system: mix 100g of styrene and 7g of divinylbenzene, wash twice with 1mol / l NaOH solution, and then wash twice with water to remove the polymerization inhibitor in the raw material; the porogen is cyclohexane, The initiator is cumene hydrogen peroxide, and the mass ratio of styrene to porogen and initiator is 1:0.1:0.005. The porogen and initiator are added to the mixture of styrene and divinylbenzene. After the initiator is dissolved, the whole is poured into a stirred tank containing a dispersant of 0.5% polyvinyl alcohol aqueous solution. The quality of the polyvinyl alcohol aqueous solution is the total mass of styrene, divinylbenzene, porogen and initiator 3 times

[0021] Copolymerization reaction: the speed is 80r / min, the temperature is first heated to 60°C, held for 2h, then heated to 70°C, held for 3h, finally heated to 90°C, held for 2h, then the polymer white balls are cooled and filtered;

[0022] Pore ​...

Example Embodiment

[0024] Example 2 Catalyst B

[0025] Suspension copolymerization system: mix 100g of styrene and 7g of divinylbenzene, wash twice with 1mol / l NaOH solution, and then wash twice with water to remove the polymerization inhibitor in the raw material; the porogen is benzene, initiator It is azobis-isoheptanitrile, and the mass ratio of styrene to porogen and initiator is 1:0.1:0.005. The porogen and initiator are added to the mixture of styrene and divinylbenzene. After dissolving, pour the whole into a stirred tank filled with a dispersant of 1.0% methylcellulose aqueous solution. The mass of methylcellulose aqueous solution is the total mass of styrene, divinylbenzene, porogen and initiator 4 times of

[0026] Copolymerization reaction: the speed is 120r / min, the temperature is first heated to 60°C, held for 4h, then heated to 70°C, held for 6h, finally heated to 90°C, held for 1h, then the polymer white balls are cooled and filtered;

[0027] Pore ​​purification: Place the polymer w...

Example Embodiment

[0029] Example 3 Catalyst C

[0030] Suspension copolymerization system: mix 100g of styrene and 7g of divinylbenzene, wash twice with 1mol / l NaOH solution, and then wash twice with water to remove the polymerization inhibitor in the raw material; the porogen is benzene, initiator It is benzoyl peroxide, and the mass ratio of styrene to porogen and initiator is 1:0.05:0.02. Add porogen and initiator to the mixture of styrene and divinylbenzene, and wait for the initiator to dissolve Then, the whole is poured into a stirred tank that has been filled with a 0.5% concentration of sodium dodecylbenzene sulfonate aqueous solution. The quality of the sodium dodecylbenzene sulfonate solution is styrene, divinylbenzene, and 3 times the total mass of porogen and initiator;

[0031] Copolymerization reaction: the speed is 80r / min, the temperature is first heated to 60°C, held for 2h, then heated to 70°C, held for 3h, finally heated to 90°C, held for 2h, then the polymer white balls are cool...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a cationic resin catalyst, a preparation method thereof and a catalytic application of thereof in preparation of glycolic acid by a methyl glycolate hydrolysis method. The cationic resin catalyst is prepared from styrene as a monomer and divinylbenzene as a cross-linking agent, the styrene and the divinylbenzene are copolymerized with a pore-forming agent, an initiator and adispersing agent to prepare copolymer white balls, the copolymer white balls are subjected to pore purification and sulfonation to prepare the cationic resin catalyst, wherein the mass ratio of the styrene to the divinylbenzene is 100:7, the mass ratio of the pore-forming agent to the initiator is 1: (0.05-0.3) : (0.005-0.03), and the ratio of the total mass of the styrene, divinylbenzene, pore-forming agent and initiator to the weight of the dispersing agent is 1: (3-4). The catalytic application of the methyl glycolate hydrolysis method for preparing glycolic acid in a catalytic distillation tower has the advantages of short process flow, complete hydrolysis of the methyl glycolate, improvement of the conversion rate of the methyl glycolate, overcoming the technical problem of reverse decomposition of the glycolic acid, long service life of the catalyst and low energy consumption.

Description

technical field [0001] This patent application relates to a cationic resin catalyst, its preparation method and its catalytic application, and its characteristics relate to a catalyst that can ensure the industrial application of glycolic acid produced by hydrolysis of methyl glycolate, its preparation method and its industrial production of ethanol by hydrolysis of methyl glycolate Catalyzed reactions of acids. Background technique [0002] Glycolic acid, also known as glycolic acid, contains both carboxyl and hydroxyl groups in its molecule, and has dual properties of organic acid and alcohol. Under certain reaction conditions, glycolic acid can undergo oxidation reaction, hydrogenation reaction, polymerization reaction, and esterification reaction. Etc. Therefore, glycolic acid is an important chemical product and an intermediate product of organic synthesis. In daily life and industrial production of products, glycolic acid also has a wide range of application value and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J31/10C07C59/06C07C51/09
CPCC07C51/09B01J31/10C07C59/06Y02P20/10
Inventor 吕晓东王义成冷东斌张伟段宏毅管秀明彭慧敏刘晓林何罡
Owner 丹东明珠特种树脂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap