Color explosion-proof glass film

An explosion-proof glass film and color technology, applied in the coating and other directions, can solve the problems of single function and insufficient viscosity of the glass film, and achieve the effects of various colors, increased aesthetics, and good thermal insulation.

Inactive Publication Date: 2019-04-16
合肥市老兵玻璃有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a color explosion-proof glass film to solve the defects of insufficient viscosity and single function of the existing glass film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A colored explosion-proof glass film according to the present invention is made of the following raw materials in parts by weight: 2-4 parts of coupling agent, 2-4 parts of dyeing agent, 4-6 parts of auxiliary agent, and 6-10 parts of coupling agent , 4-6 parts of hollow glass microspheres, 4-6 parts of methyl cellulose, 2-5 parts of film-forming aids, 6-10 parts of dichlorotetrafluoroethane, 4-10 parts of trinitrotoluene, di 4-10 parts of antimony, 4-10 parts of formic acid methacrylate, 2-6 parts of nicotinic acid, 3-10 parts of iron orthophosphate, 2-6 parts of starch, 4-10 parts of dodecyl glucoside, 4 parts of glycerol -8 parts, 4-10 parts of 1,4-cyclohexanedimethanol, 4-10 parts of sodium peroxide.

[0016] Further, the coupling agent is one of KH550, KH560, KH570, KH792, DL602, DL171.

[0017] Further, the dyeing agent is Cr 2 0 3 , ferric oxide, ferrous oxide, lead oxide in one.

[0018] Further, the auxiliary agent includes magnesium oxide and aluminum oxid...

Embodiment 2

[0021] A colored explosion-proof glass film according to the present invention is made of the following raw materials in parts by weight: 3 parts of coupling agent, 3 parts of dyeing agent, 5 parts of auxiliary agent, 8 parts of coupling agent, 5 parts of hollow glass microspheres, 5 parts of base fiber, 3 parts of film-forming aid, 8 parts of dichlorotetrafluoroethane, 5 parts of trinitrotoluene, 6 parts of antimony trioxide, 6 parts of methacrylic acid formic acid, 4 parts of nicotinic acid, iron orthophosphate 4 parts, 3 parts starch, 6 parts lauryl glucoside, 5 parts glycerol, 6 parts 1,4-cyclohexanedimethanol, 7 parts sodium peroxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a color explosion-proof glass film, which is prepared, by weight, from the following raw materials: 2-4 parts of a coupling agent, 2-4 parts of a coloring agent, 4-6 parts of an auxiliary agent, 6-10 parts of a coupling agent, 4-6 parts of hollow glass microspheres, 4-6 parts of methyl fiber, 2-5 parts of a film-forming auxiliary agent, 6-10 parts of dichlorotetrafluoroethane, 4-10 parts of trinitrotoluene, 4-10 parts of antimony trioxide, 4-10 parts of methacrylic acid formic acid, 2-6 parts of nicotinic acid, 3-10 parts of ferric orthophosphate, 2-6 parts of starch, 4-10 parts of dodecyl glycoside, 4-8 parts of glycerol, 4-10 parts of 1,4-cyclohexanedimethanol and 4-10 parts of sodium peroxide. The glass film overcomes the defects of the prior art, an auxiliary agent and a coloring agent are added, which improves the mechanical strength of the glass film and the stability of the glass film subjected to wind blowing and sun drying all the year round, the glassfilm has firm texture and various colors, has good effects of heat insulation and heat preservation and glass self-explosion prevention, can increase the beauty degree of the glass and is obviously suitable for popularization.

Description

technical field [0001] The invention relates to the technical field of chemical engineering, in particular to a colored explosion-proof glass film. Background technique [0002] With the development of the economy, people's requirements for the quality of life are getting higher and higher. Glass can not only bring beauty to the building, but also have a good effect of increasing the space, but people's requirements are not only that, the glass film is very Quick to be welcomed. Glass film can not only change the monotonous and transparent image of ordinary glass, but also add beauty to indoors and outdoors. However, the existing sticking films are generally not viscous enough, and have a single function simultaneously, which cannot satisfy people's needs. Contents of the invention [0003] The object of the present invention is to provide a colored explosion-proof glass film to solve the defects of insufficient viscosity and single function of the existing glass film. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/61C09D7/63C09D7/65
CPCC09D4/06C09D7/61C09D7/63C09D7/65C09D7/70
Inventor 杨延国余华梅
Owner 合肥市老兵玻璃有限公司