Catalysts for Synthesis of Metaanhydrides
A catalyst and partial anhydride technology, which is applied in the field of catalysts for the synthesis of partial anhydride, can solve the problems of low partial anhydride yield and high partial anhydride yield, and achieve the effect of increasing yield and improving catalyst performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0030] Weigh 55g of oxalic acid and 180ml of distilled water in a flask, stir and raise the temperature to 85°C, after the oxalic acid is completely dissolved, make an oxalic acid solution. Add 1 mole fraction of vanadium pentoxide into the prepared oxalic acid solution and continue stirring to obtain ammonium vanadyl oxalate solution. Dissolve 0.4 mole fractions of magnesium acetate in 48ml of distilled water and add it into the solution, and continue the reaction at 60°C for 1 hour. Grinding 5 mole parts of titanium tetrachloride and 20 ml of distilled water was added to the reaction system, and stirred thoroughly to form a slurry to obtain a precursor. Load the catalyst precursor into a spraying machine, and evenly spray it on the inert carrier silicon carbide. The catalyst was calcined at 520°C in a muffle furnace and cooled naturally. Catalyst at a reaction temperature of 400°C and a space velocity of 3400h -1 Next, unimethylene trimethylbenzene: water vapor = 0.05, ev...
Embodiment 2
[0032] Weigh 55g of oxalic acid and 180ml of distilled water in a flask, stir and raise the temperature to 85°C, after the oxalic acid is completely dissolved, make an oxalic acid solution. Add 1 mole fraction of vanadium pentoxide into the prepared oxalic acid solution and continue stirring to obtain ammonium vanadyl oxalate solution. Dissolve 0.4 molar parts of scandium chloride in 48ml of distilled water and add it into the solution, and continue the reaction at 60°C for 1 hour. Grinding 5 mole parts of titanium tetrachloride and 20 ml of distilled water was added to the reaction system, and stirred thoroughly to form a slurry to obtain a precursor. Load the catalyst precursor into a spraying machine, and evenly spray it on the inert carrier silicon carbide. The catalyst was calcined at 520°C in a muffle furnace and cooled naturally. Catalyst at a reaction temperature of 400°C and a space velocity of 3400h -1 Next, unimethylene trimethylbenzene: water vapor = 0.05, evalu...
Embodiment 3
[0037] Weigh 55g of oxalic acid and 180ml of distilled water in a flask, stir and raise the temperature to 85°C, after the oxalic acid is completely dissolved, make an oxalic acid solution. Add 1 mole fraction of ammonium metavanadate into the prepared oxalic acid solution and continue stirring to obtain ammonium vanadyl oxalate solution. Dissolve 0.4 mole fractions of barium acetate in 48ml of distilled water and add it into the solution, and continue to react at 60°C for 1 hour. Grinding 5 mole fractions of titanium dioxide and 20 ml of distilled water was added to the reaction system, and stirred thoroughly to form a slurry to obtain a precursor. Load the catalyst precursor into a spraying machine, and evenly spray it on the inert carrier silicon carbide. The catalyst was calcined at 520°C in a muffle furnace and cooled naturally. Catalyst at a reaction temperature of 400°C and a space velocity of 3400h-1 Next, unimethylene trimethylbenzene: water vapor = 0.05, evaluated ...