A kind of one-component reactive polyurethane hot melt adhesive and preparation method thereof

A polyurethane hot-melt adhesive and reactive technology, applied in the field of polyurethane hot-melt adhesive, can solve the problems of insufficient high and low temperature resistance and chemical pollution resistance, achieve good low temperature flexibility, improve high and low temperature resistance, and improve elasticity and flexibility. sexual effect

Active Publication Date: 2021-07-09
JIANGSU RUIDE NEW ENERGY TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned copolymer has good compatibility with the polyurethane prepolymer, and the obtained hot melt adhesive has excellent initial adhesion and final bonding strength, but its high and low temperature resistance and chemical pollution resistance are not enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of one-component reactive polyurethane hot melt adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0042] The composition of embodiment 1-4 and comparative example 1 sees the following table:

[0043] Component / part A B C D E F G H Example 1 55 13 0.5 10 6 1 1 0 Example 2 60 17 0.35 6 12 3 2 0 Example 3 40 12 0.65 15 10 2 3 0 Example 4 50 15 0.5 12 8 2 5 0 Example 5 50 15 0.5 12 8 2 5 2 Comparative example 1 50 15 0.5 12 8 2 0 0 Comparative example 2 50 15 0.5 12 8 2 0 2

[0044] In the table above: A stands for polyol, B stands for polyisocyanate, C stands for catalyst, D stands for chain extender, E stands for tackifying resin, F stands for latent curing agent, G stands for plasticizer, H stands for vinyl unsaturated mono body.

[0045] In Examples 1-5 and Comparative Examples 1-2, the polyester polyol is XCP-3000H commercially available from Jiangsu Xuchuan Chemical Company, the polyisocyanate is 4,4'-diphenylmethane diisocyanate, and the catalyst is dilauric aci...

Embodiment 6

[0051] Embodiment 6-10 is based on embodiment 5, difference is, the polyester polyol of embodiment 6 is polyethylene adipate diol, polyisocyanate is toluene diisocyanate, and catalyst is dimethylethanolamine; Embodiment 7 The plasticizer is dioctyl phthalate; the ethylenically unsaturated monomer of embodiment 8 is 1,2-dimethyl-3-(1-methylvinyl) cyclopentanol, the ethylene of embodiment 9 The base unsaturated monomer is 1,2-epoxy-4-vinylcyclohexane.

[0052] In the preparation process, the end point of the reaction between the polypolyol and the polyisocyanate is controlled so that the isocyanate content reaches 2.4%.

[0053] Peel strength (GB / T2791-95), thermal shock (ASTM D-746-40~80 ℃, 15 days), water resistance test ( 85°C 85% test before and after 1000 hours of shear strength) and salt spray resistance test (500 hours salt spray box sodium chloride 5%, test temperature 45°C), the test results are shown in the following table:

[0054]

Embodiment 8

[0056] In Example 8, the shear strength of the hot-melt adhesive coating film in the water resistance test increased significantly, indicating that the epoxy group in the 1,2-epoxy-4-vinylcyclohexane also played the role of a hydrolysis stabilizer to prevent ester bond Fracture and degradation of polymers. Therefore, preferred ethylenically unsaturated monomers are 1,2-epoxy-4-vinylcyclohexane and 1,2,8,9-bisepoxy-4-vinylcyclohexane with epoxy groups alkene.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a one-component reactive polyurethane hot-melt adhesive. The raw material composition includes a polyurethane prepolymer, a chain extender, a tackifying resin, a latent curing agent, and a filler. The polyurethane prepolymer has a molecular weight of 500- 3000 polyol, polyisocyanate and catalyst are polymerized; the raw material composition also includes a plasticizer, and the plasticizer is dioctyl phthalate and / or diethylene glycol dibenzoate. In the component of one-component reactive polyurethane hot-melt adhesive of the present invention, by adding plasticizer, plasticizer is dioctyl phthalate and / or diethylene glycol dibenzoate, and above-mentioned two kinds of materials are for polyurethane The plasticizing efficiency is high, the volatility is low, and it has good low-temperature flexibility. The addition of plasticizers weakens the interaction between the polymer chains and improves the elasticity and flexibility of the polymer material. , Improve the high and low temperature resistance of hot melt adhesives.

Description

technical field [0001] The invention relates to the technical field of polyurethane hot-melt adhesives, in particular to a one-component reactive polyurethane hot-melt adhesive and a preparation method thereof. Background technique [0002] Traditional hot-melt adhesives are generally composed of thermoplastic substances, which are not heat-resistant and easily soluble in organic solvents. They are mainly used in products that do not require high heat resistance and bonding strength. In order to improve the bonding strength of the hot melt adhesive, the improved reactive polyurethane hot melt adhesive is made of isocyanate-terminated polyurethane prepolymer as the base material, and is prepared with tackifying resin, antioxidant, catalyst, filler, etc. The curing process of reactive polyurethane hot melt adhesive (PUR) is carried out in two stages, namely cooling condensation and moisture curing. In the first stage, PUR is the same as ordinary thermoplastic hot-melt adhesiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J175/06C09J11/06C09J11/08C09J4/06
CPCC09J4/06C09J11/06C09J11/08C09J175/06C08L45/00C08K5/12
Inventor 戈士勇
Owner JIANGSU RUIDE NEW ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap