Composite wastewater treatment medicament and preparation method thereof
A waste water treatment and medicament technology, applied in the direction of adsorption water/sewage treatment, oxidized water/sewage treatment, water/sludge/sewage treatment, etc., can solve the problems of complex process, expensive equipment, harsh conditions, etc., and shorten the residence time , The removal ability is obvious, the effect of the treatment process is rapid
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0036] Example 1
[0037] A preparation method of a composite wastewater treatment agent of POM and carbon nanotube modified activated carbon powder:
[0038] Weigh 50g of sodium tungstate dihydrate and 25g of disodium hydrogen phosphate and dissolve them in 250g of water. Stir at 100r / min for 1h at 60°C until a thin crystalline film begins to appear, and solution A is obtained; Add 250ml to A, the mass fraction is 24% and the density is 1.12g / cm 3 Hydrochloric acid, then add 26.9g of sodium hypochlorite, 26.9g of cobalt nitrate and 13.4g of potassium persulfate, stir for 2h on a water bath at 60℃ at a speed of 50r / min for reaction to obtain solution B; then add 20.75g of carboxylated carbon to solution B Nanotubes, 2.08g double dispersion stabilizer and 51.88g polymeric iron salt, and under the protection of inert gas, the reaction was carried out with continuous stirring at 100°C at a speed of 150r / min to obtain solution C; 40g activated carbon powder was added to 133.3g Mix in ...
Example Embodiment
[0039] Example 2
[0040] A preparation method of a composite wastewater treatment agent of POM and carbon nanotube modified activated carbon powder:
[0041] Weigh 50g of sodium tungstate dihydrate and 25g of disodium hydrogen phosphate and dissolve in 250g of water, stir for 1.5h at a speed of 200r / min at 70℃ and evaporate until a thin crystalline film begins to appear, to obtain solution A; then to solution A While stirring, add 250mL with a mass fraction of 24% and a density of 1.12g / cm 3 Add 42.8g of sodium hypochlorite, 42.8g of cobalt nitrate and 21.4g of potassium persulfate, and stir for 3h at a speed of 100r / min on a 70℃ water bath to obtain solution B; then add 30.7g of hydroxylation to solution B Carbon nanotubes, 3.07g double-dispersion stabilizer, 46.1g polymeric iron salt and 46.1g polymeric aluminum salt, and under the protection of inert gas, react with continuous stirring at 150°C and 200r / min to obtain solution C; 40g activated carbon powder was added to 150g de...
Example Embodiment
[0042] Example 3
[0043] A preparation method of a composite wastewater treatment agent of POM and carbon nanotube modified activated carbon powder:
[0044] Weigh 50g of sodium tungstate dihydrate and 25g of disodium hydrogen phosphate and dissolve in 500g of water, stir for 2h at 80°C at 300r / min and evaporate until a thin crystalline film begins to appear, obtaining solution A; then in solution A While stirring, add 500ml with a mass fraction of 24% and a density of 1.12g / cm 3 Add 113.5g of sodium hypochlorite, 113.5g of cobalt nitrate and 56.75g of potassium persulfate to the solution, stir for 4h at a speed of 150r / min on a water bath at 80℃ for reaction to obtain solution B; then add 77.1 to solution B g hydroxylated carbon nanotubes, 7.7g double-dispersion stabilizer and 269.9g polyaluminum salt, and under the protection of inert gas, the reaction is carried out at a temperature of 200°C and a stirring speed of 250r / min to obtain solution C; Add 40g of activated carbon pow...
PUM
Property | Measurement | Unit |
---|---|---|
Density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap