Electrolyzed water hydrogen production catalyst and preparation method thereof

A catalyst and water hydrogen production technology, applied in chemical instruments and methods, physical/chemical process catalysts, electrolysis process, etc., can solve a large number of environmental pollution problems, achieve advanced technology, high product yield, detailed and accurate data.

Active Publication Date: 2019-05-28
SHENYANG NORMAL UNIV
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The composite material of metal sulfide and porous carbon is an efficient catalyst for hydrogen production in electrolysis of water. However, the synthesis process of this material requires a large amount of solvent, which will pollute the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrolyzed water hydrogen production catalyst and preparation method thereof
  • Electrolyzed water hydrogen production catalyst and preparation method thereof
  • Electrolyzed water hydrogen production catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] figure 1 and figure 2 As shown in the figure, it is a state diagram of the synthesis and preparation of the hydrogen production catalyst for electrolysis of water.

[0041] Quantities of the chemical substances used in the preparation are determined according to a preset range, with grams and milliliters as measurement units.

[0042] The synthesis of electrolyzed water hydrogen production catalyst is carried out in agate grinding and tube furnace, which is completed by room temperature grinding process and high temperature calcination under inert atmosphere;

[0043] figure 1 As shown, the reaction precursors (cobalt chloride, thiourea and glucose) were added to the agate mortar and manually ground for 30 min.

[0044] figure 2 As shown, the high-temperature calcination is carried out in a tube, using nitrogen as a protective gas, and the calcination temperature is 800-1000°C. figure 2 The medium carbonization device includes: air inlet 1, vacuum port 2, flange...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of preparation and application of catalyst materials, in particular to a preparation method of an electrolyzed water hydrogen production catalyst. The preparation method adopts a molten salt synthesis method, cobalt chloride is used as a template and a cobalt source, thiourea is used as a nitrogen source and a sulfur source, glucose is used as a carbonsource, under the condition of a room temperature, manual grinding is performed for 30 min in an agate grinding bowl, obtained blue powder is used for preparing the electrolyzed water hydrogen production catalyst by high temperature calcination in a tube furnace, and the pore passage structure and heteroatom content of the material can be adjusted by controlling the calcination temperature. The preparation method is high in product yield of 41%, the material can be used as the electrolyzed water hydrogen production catalyst, and the preparation method is an ideal method for preparing the electrolyzed water production catalyst.

Description

technical field [0001] The invention relates to the technical field of preparation and application of catalyst materials, in particular to a preparation method of a hydrogen production catalyst for electrolysis of water. Background technique [0002] Nowadays, science and technology not only promote the progress of society and bring a lot of convenience to our life, but also bring some adverse effects. For example, the continuous consumption of non-renewable energy such as fossil energy has caused human beings to suffer from an energy crisis. At the same time, its combustion product CO 2 , SO 2 The greenhouse effect and air pollution caused by the discharge of these gases into the air are gradually eroding human homes. [0003] In order to meet the world's increasing energy demand, more sustainable energy sources need to be discovered to replace the current fossil fuels. As a clean, non-polluting, high-calorific and widely distributed energy source in the world, hydrogen ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/043C25B1/04C25B11/06
CPCY02E60/36
Inventor 汤兑海于欢赵震张文婷
Owner SHENYANG NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap