An occlusal pad that reduces bacterial adhesion

A technology of adhesion rate and occlusal pad, applied in the field of oral medicine, can solve problems such as oral micro-ecological imbalance, achieve the effects of reduced bacterial adhesion, strong adhesion, and increased hydrophobicity

Active Publication Date: 2020-12-29
温州医科大学附属口腔医院
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Topical antimicrobials may cause oral microecological imbalance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A kind of occlusal pad that reduces bacterial adhesion rate, comprises PMMA resin and is coated on the coating on PMMA resin, and described coating is made up of following composition by weight percentage:

[0045] 53 parts of tetraethyl orthosilicate;

[0046] 6 parts of silane coupling agent;

[0047] 83 parts of absolute ethanol;

[0048] 178 parts of deionized water;

[0049] 8 parts of dilute hydrochloric acid;

[0050] 13 parts of vinyltrimethylsilane;

[0051] 8 parts of vinyl chloride;

[0052] 4 parts of bisphenol alpha dimethacrylate;

[0053] 2.5 parts of trimethyl (1-methylvinyloxy) silane;

[0054] 0.5 parts of azobisisobutyronitrile;

[0055] 7 parts of antibacterial agent.

[0056] Described antibacterial agent is made up of following composition by weight percentage:

[0057] 55 copies of carrier;

[0058] 5 loads;

[0059] The carrier is silicon-aluminum oxide microsphere particles, which consist of the following components:

[0060] silicon...

Embodiment 2

[0079] A kind of occlusal pad that reduces bacterial adhesion rate, comprises PMMA resin and is coated on the coating on PMMA resin, and described coating is made up of following composition by weight percentage:

[0080] 28 parts of tetraethyl orthosilicate;

[0081] 1 part of silane coupling agent;

[0082] 52 parts of absolute ethanol;

[0083] 82 parts of deionized water;

[0084] 6 parts of dilute hydrochloric acid;

[0085] 10 parts of vinyltrimethylsilane;

[0086] 6 parts of vinyl chloride;

[0087] 2 parts of bisphenol alpha dimethacrylate;

[0088] 1 part of trimethyl (1-methylvinyloxy) silane;

[0089] 0.1 part of azobisisobutyronitrile;

[0090] 6 parts of antibacterial agent.

[0091] Described antibacterial agent is made up of following composition by weight percentage:

[0092] 20 copies of carrier;

[0093] 5 loads;

[0094] The carrier is silicon-aluminum oxide microsphere particles, which consist of the following components:

[0095] silicon sourc...

Embodiment 3

[0114] A kind of occlusal pad that reduces bacterial adhesion rate, comprises PMMA resin and is coated on the coating on PMMA resin, and described coating is made up of following composition by weight percentage:

[0115] 50 parts of tetraethyl orthosilicate;

[0116] 10 parts of silane coupling agent;

[0117] 114 parts of absolute ethanol;

[0118] 192 parts of deionized water;

[0119] 10 parts of dilute hydrochloric acid;

[0120] 16 parts of vinyltrimethylsilane;

[0121] 10 parts of vinyl chloride;

[0122] 6 parts of bisphenol alpha dimethacrylate;

[0123] 4 parts of trimethyl (1-methylvinyloxy) silane;

[0124] 1 part of azobisisobutyronitrile;

[0125] 8 parts of antibacterial agent.

[0126] Described antibacterial agent is made up of following composition by weight percentage:

[0127] 90 copies of carrier;

[0128] 10 loads;

[0129] The carrier is silicon-aluminum oxide microsphere particles, which consist of the following components:

[0130] silicon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an occlusal pad for reducing bacterial attach rate. The technical scheme of the occlusal pad is characterized in that the occlusal pad comprises PMMA resin and a coating applied to the PMMA resin, wherein the coating is prepared from the following components by weight: 28-50 parts of ethyl orthosilicate, 0.98-10 parts of a silane coupling agent, 52-114 parts of absolute ethyl alcohol, 82-192 parts of deionized water, 6-10 parts of dilute hydrochloric acid, 10-16 parts of vinyl trimethylsilane, 6-10 parts of vinyl chloride, 2-6 parts of bisphenol alpha dimethacrylate, 1-4 parts of trimethyl[(1-methylvinyl)oxy]silane, 0.1-1 part of azobisisobutyronitrile and 6-8 parts of an antibacterial agent. Hydrophobic antibacterial paint is prepared with the sol-gel method, the surface of the occlusal pad is covered with a hydrophobic antibacterial coating, and accordingly, the bacterial attach rate is reduced.

Description

technical field [0001] The invention relates to the field of oral medicine, in particular to an occlusal pad which reduces the bacteria adhesion rate. Background technique [0002] Polymethyl methacrylate (PMMA) is a common material for occlusal pads because of its stable performance, beautiful color, easy processing and repair, and low price. However, the porosity and water absorption of PMMA materials also make it easy for pathogenic bacteria to adhere to its surface, causing dental caries, periodontitis, denture stomatitis and other oral diseases. [0003] In order to reduce the bacterial adhesion on the surface of the occlusal pad, mechanical cleaning, chemical soaking and local application of antibacterial drugs are often used clinically. The commonly used physical cleaning method is to mechanically scrub the occlusal pad with a toothbrush and toothpaste, but the effect of this method is not very satisfactory: the hyphae of Candida albicans easily extend into the pores...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61C7/36C09D183/02C09D135/02C09D5/14C09D7/63
Inventor 王海燕林紫燕胡荣党倪振宇曹真胜秦化祥
Owner 温州医科大学附属口腔医院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap