A kind of sound insulation hollow brick and preparation method thereof

A technology of hollow bricks and foamed materials, applied in the field of building materials, can solve the problems of few researches on sound insulation effect, hollow bricks only focus on weight, etc., and achieve the effect of improving bonding strength and mechanical stability, good sound insulation effect and saving resources.

Active Publication Date: 2022-02-01
ANHUI KUNMENG NEW TYPE BUILDING MATERIAL CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, with the progress of society, people's requirements for building materials are also constantly improving. Traditional hollow bricks only focus on weight and toughness, but little research has been done on their sound insulation effects. Therefore, the purpose of the present invention is to further improve the quality of finished hollow bricks. quality, enhanced sound insulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A soundproof hollow brick, which includes the following raw materials in parts by weight:

[0024] Mineral wool fiber 5, slag 30, modified polyurethane foam material 6, bentonite 10, limestone 20, straw powder 10, acetate fiber 2, coal gangue 20, vermiculite powder 10, chitosan 2, fatty alcohol polyoxyethylene ether 1 .

[0025] Described modified polyurethane foam material is made up of the raw material of following weight part:

[0026] Triethanolamine 2, polycarbonate diol 80, isophorone diisocyanate 60, azodicarbonamide 2, oleic acid 3, isooctyl tin dimethyl dimercaptoacetate 0.1, tetraethyl orthosilicate 50, hard Calcium fatty acid 3.

[0027] The preparation method of described modified polyurethane foam material, comprises the following steps:

[0028] (1) Mix oleic acid and tetraethyl orthosilicate, add it to deionized water 60 times the weight of the mixture, stir for 3 hours, send it into the reaction kettle, raise the temperature to 240°C, add calcium stea...

Embodiment 2

[0037] A soundproof hollow brick, which includes the following raw materials in parts by weight:

[0038] Mineral wool fiber 8, slag 40, modified polyurethane foam material 9, bentonite 20, limestone 25, straw powder 14, acetate fiber 5, coal gangue 27, vermiculite powder 17, chitosan 4, fatty alcohol polyoxyethylene ether 2 .

[0039] Described modified polyurethane foam material is made up of the raw material of following weight part:

[0040] Triethanolamine 4, polycarbonate diol 100, isophorone diisocyanate 70, azodicarbonamide 3, oleic acid 5, dimethyldithioglycolate isooctyl tin 0.14, tetraethyl orthosilicate 60, hard Calcium fatty acid 3.

[0041] The preparation method of described modified polyurethane foam material, comprises the following steps:

[0042] (1) Mix oleic acid and tetraethyl orthosilicate, add it to deionized water 70 times the weight of the mixture, stir for 5 hours, send it into the reaction kettle, raise the temperature to 255°C, add calcium stear...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sound-insulating hollow brick, which comprises the following raw materials in parts by weight: mineral wool fiber 5-8, slag 30-40, modified polyurethane foam material 6-9, bentonite 10-20, limestone 20-25 , straw powder 10-14, cellulose acetate 2-5, coal gangue 20-27, vermiculite powder 10-17, chitosan 2-4, fatty alcohol polyoxyethylene ether 1-2, the hollow brick of the present invention has very good Strength, and good sound insulation effect, high quality.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a sound-insulating hollow brick and a preparation method thereof. Background technique [0002] Coal gangue is one of the largest industrial solid wastes in China. Moreover, the annual discharge of coal gangue is equivalent to about 10% of the coal production in that year. The annual emission rate will be greater than 160 million tons. Stacking coal gangue not only takes up a lot of land, but also pollutes the environment and affects people's life and health. In addition, the spontaneous combustion of coal gangue can release a variety of harmful gases, etc., and at the same time it is accompanied by a large amount of smoke and dust and has the risk of explosion. Therefore, the spontaneous combustion of coal gangue has different degrees of impact on the surrounding atmospheric environment, human health, and animal and plant growth. Fly ash is one of the largest in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/132C04B33/138C04B33/36C04B38/06
CPCC04B33/138C04B33/1305C04B33/131C04B33/132C04B33/1324C04B33/36C04B38/067C04B2235/5216C04B2235/442C04B2235/77C04B2235/96C04B38/0067Y02P40/60
Inventor 刘林李军陈贤超张章
Owner ANHUI KUNMENG NEW TYPE BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap