A preparation method of high current-carrying multi-core bi-2223 superconducting tape under magnetic field

A technology of bi-2223 and superconducting tape, which is applied in the usage of superconducting elements, superconducting devices, superconducting/high-conducting conductors, etc., can solve the problems of fast performance decay, weak vortex pinning force, and current-carrying Poor capacity and other problems, to achieve the effect of improving orientation and grain boundary quality, improving current carrying capacity, and improving orientation and connection characteristics

Active Publication Date: 2020-06-05
NORTHWEST INSTITUTE FOR NON-FERROUS METAL RESEARCH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the main problem in the preparation process of Bi-2223 tape is that due to the short coherence length and large penetration depth in Bi-2223, its vortex pinning force is weak, and its performance decays quickly in a magnetic field.
The Bi-2223 tape prepared by the conventional powder tube method has too few effective flux pinning centers, resulting in poor current-carrying capacity of the Bi-2223 tape in the liquid nitrogen temperature region and high field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of high current-carrying multi-core bi-2223 superconducting tape under magnetic field

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] This embodiment includes the following steps:

[0030] Step 1. In a glove box with an oxygen partial pressure content of 7.5% and a balance gas of argon with a mass purity of 99.995%, under the condition of a vibration frequency of 40Hz, a vibrating table is used to vibrate the tube, and the Bi-2223 precursor powder is first introduced into the glove box. In the metal funnel, start the vibrating table to vibrate the silver sleeve at the same time, so that the Bi-2223 precursor powder is filled into the gap formed by the inner silver tube and the outer silver tube of the silver sleeve, and then the CaCuO prepared by the co-precipitation method 2 The powder is filled into the inner silver tube of the silver sleeve. During the process of vibrating the tube, the positions of the inner silver tube and the outer silver tube in the silver sleeve are fixed, and then the inner silver tube is taken out and the outer silver tube is sealed to obtain the first silver tube. A tube co...

Embodiment 2

[0037] This embodiment includes the following steps:

[0038] Step 1. In a glove box with an oxygen partial pressure content of 7.5% and a balance gas of argon with a mass purity of 99.995%, under the condition of a vibration frequency of 40Hz, a vibrating table is used to vibrate the tube, and the Bi-2223 precursor powder is first introduced into the glove box. In the metal funnel, start the vibrating table to vibrate the silver sleeve at the same time, so that the Bi-2223 precursor powder is filled into the gap formed by the inner silver tube and the outer silver tube of the silver sleeve, and then the CaCuO prepared by the co-precipitation method 2 The powder is filled into the inner silver tube of the silver sleeve. During the process of vibrating the tube, the positions of the inner silver tube and the outer silver tube in the silver sleeve are fixed, and then the inner silver tube is taken out and the outer silver tube is sealed to obtain the first silver tube. A tube co...

Embodiment 3

[0045] This embodiment includes the following steps:

[0046] Step 1. In a glove box with an oxygen partial pressure content of 7.5% and a balance gas of argon with a mass purity of 99.995%, under the condition of a vibration frequency of 40Hz, a vibrating table is used to vibrate the tube, and the Bi-2223 precursor powder is first introduced into the glove box. In the metal funnel, start the vibrating table to vibrate the silver sleeve at the same time, so that the Bi-2223 precursor powder is filled into the gap formed by the inner silver tube and the outer silver tube of the silver sleeve, and then the CaCuO prepared by the co-precipitation method 2 The powder is filled into the inner silver tube of the silver sleeve. During the process of vibrating the tube, the positions of the inner silver tube and the outer silver tube in the silver sleeve are fixed, and then the inner silver tube is taken out and the outer silver tube is sealed to obtain the first silver tube. A tube co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a high-current-carrying multi-core Bi-2223 superconducting tape under a magnetic field. The method comprises the following steps: 1, adding Bi-2223 precursor powder and CaCuO2 power into a silver sleeve so as to obtain a first tube loading composite; 2, drawing and assembling the first tube loading composite so as to obtain a second tube loading composite; 3, drawing the second tube loading composite into a multi-core Bi-2223 tape; 4, preserving the heat of the multi-core Bi-2223 tape so as to obtain the pretreated multi-core Bi-2223 tape; and 5,thermally treating the pretreated multi-core Bi-2223 tape so as to obtain a multi-core Bi-2223 superconducting tape. The powder tube loading process improves the Bi-2223 grain orientation and grain boundary quality and improves the grain orientation and bonding properties so that the current carrying capacity of the Bi-2223 superconducting tape under the magnetic field can be enhanced and the application in magnets and other fields can be facilitated.

Description

technical field [0001] The invention belongs to the technical field of superconducting material preparation, in particular to a preparation method of a high-carrying multi-core Bi-2223 superconducting tape under a magnetic field. Background technique [0002] Bi-2223 tapes prepared by powder-in-tube method (PIT) are characterized by their high critical current density (J c ) and easy processing of long strips, it has become one of the most promising high-temperature superconducting materials for high-power applications in the liquid nitrogen temperature region, and its potential applications include power transmission cables, transformers, fault current limiters, motors and motors. Wait. [0003] The critical current density of Bi-2223 tape is the most important parameter for its application, especially its engineering current density under a magnetic field. Obtaining high-performance Bi-2223 tape will significantly promote the development of high-field magnet technology, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B12/02H01B13/00
CPCH01B12/02H01B13/00H01B13/0006H01B13/0016Y02E40/60
Inventor 马小波李成山张平祥张胜楠冯建情刘国庆黄英建
Owner NORTHWEST INSTITUTE FOR NON-FERROUS METAL RESEARCH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More