Super-absorbent silk fibroin material and production method thereof

A technology of super absorbent material and silk fibroin, applied in the field of super absorbent silk fibroin, can solve the problems of low water absorption rate, high reaction temperature, polluted environment, etc., achieve good biocompatibility, improve swelling ability, and reduce reaction effect of temperature

Active Publication Date: 2019-11-01
NANTONG TEXTILE & SILK IND TECH RES INST +1
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Before the patent of the present invention, such as the Chinese Patent Application No. CN201110202099.X, the invention patent titled "Preparation method of a cellulose-based water-absorbing material" disclosed a water-absorbing material, which used a large amount of acrylic acid, etc. Chemical raw materials, highly toxic, and cannot be degraded, polluting the environment
Another example is the Chinese Patent Application No. CN201811370358.8, which is titled "A Skin-Friendly Super Absorbent Material for Infant Diapers and Its Preparation Method". Further improve
There is also a Chinese patent application number CN201811006464.8, titled "A Photocurable Silk Fibroin Hydrogel and Its Preparation Method". In this patent, the reaction temperature is too high during the photocurable crosslinking process, which leads to the formation of a partial crystalline structure. , which greatly limits the reswellability of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-absorbent silk fibroin material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The preparation of embodiment 1 silk fibroin solution

[0026] Select fresh silkworm cocoons produced in the current year, remove silkworm chrysalis and other sundries, and obtain silkworm cocoon shells. Weigh 80 g silkworm cocoon shells with a precision balance, prepare 4000 mL of sodium bicarbonate / sodium carbonate aqueous solution with a mass fraction of 0.01M and pH=9.5, heat it to boiling with an induction cooker, add the cocoon shells, and adjust the power of the induction cooker to keep the aqueous solution slightly boiling for 30 minutes , take out the cocoons and clean them with deionized water.

[0027] The above test was repeated three times to remove the sericin, and then the cocoon silk was taken out and dried in an oven at 60° C. to obtain pure silk fibroin fibers. Dissolve pure silk fibroin fibers in a lithium bromide solution with a concentration of 9.3mol / L at a bath ratio of 20:150, and dissolve in a constant temperature magnetic stirrer at 60±2°C for...

Embodiment 2

[0028] The preparation of embodiment 2 silk fibroin superabsorbent material

[0029] (1) Adjust the concentration of the pure silk fibroin solution in Example 1 to 30 mg / mL with deionized water to obtain an aqueous silk fibroin solution.

[0030] (2) Add riboflavin and horseradish peroxidase solution to the silk fibroin aqueous solution to obtain a reaction solution. The riboflavin concentration in the reaction solution was 0.3 mM, and the horseradish peroxidase concentration was 20 U / mL.

[0031] Most of the cross-linking points in traditional silk fibroin hydrogel are physical cross-linking points, which are easy to slide along the molecular chain during the drying process to produce a large number of crystal structures, which greatly limits its water absorption capacity. Under the irradiation of ultraviolet light, riboflavin generates active oxygen free radicals that can react with tyrosine on the molecular chain of silk fibroin, induce chemical cross-linking of amino grou...

Embodiment 3

[0040] The preparation of embodiment 3 silk fibroin superabsorbent material

[0041] (1) Adjust the concentration of the pure silk fibroin solution in Example 1 to 20 mg / mL with deionized water to obtain an aqueous silk fibroin solution.

[0042] (2) Add riboflavin and horseradish peroxidase solution to the silk fibroin aqueous solution to obtain a reaction solution. The riboflavin concentration in the reaction solution was 0.1 mM, and the horseradish peroxidase concentration was 10 U / mL.

[0043] Most of the cross-linking points in traditional silk fibroin hydrogel are physical cross-linking points, which are easy to slide along the molecular chain during the drying process to produce a large number of crystal structures, which greatly limits its water absorption capacity. Under the irradiation of ultraviolet light, riboflavin generates active oxygen free radicals that can react with tyrosine on the molecular chain of silk fibroin, induce chemical cross-linking of amino grou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a super-absorbent silk fibroin material and a production method thereof. The production method comprises the following steps of pouring reaction liquid, which is obtained aftera silk fibroin solution, riboflavin and horse radish peroxidase are mixed evenly, into a transparent mould, and introducing oxygen into the reaction liquid; irradiating the reaction liquid by means of ultraviolet light to form silk fibroin hydrogel, and controlling temperature of the reaction liquid in an irradiation process to be 0-8 DEG C; drying the silk fibroin hydrogel to obtain silk fibroinxerogel; and after the silk fibroin xerogel is crushed, conducting screening to obtain the super-absorbent silk fibroin material. According to the production method, by conducting cross-linking in alow-temperature environment, the reaction temperature can be effectively reduced, and a random coil structure of the formed hydrogel in a solution is maintained, so that crystal structures are effectively inhibited, and the swelling capability of the material is greatly improved. The produced super-absorbent silk fibroin material has high water absorption capacity and a high water retention rate.

Description

technical field [0001] The invention relates to the technical field of superabsorbent materials, in particular to a method for preparing a silk fibroin superabsorbent material and the silk fibroin superabsorbent material prepared by the preparation method. Background technique [0002] Super absorbent material is a kind of super absorbent material, which refers to a substance that can absorb water tens to hundreds of times its own mass. Widely used in baby diapers, women's sanitary napkins and pet pads and other fields. Traditional superabsorbent materials are generally divided into the following two types. One is natural and modified polymer superabsorbent resins. The raw materials are generally starch or cellulose. By grafting hydrophilic functional groups to natural macromolecules In order to achieve the purpose of high water absorption modification. The other is artificial synthetic water-absorbent resins, such as polyvinyl salts, polyvinyl alcohol, polyoxyethylene, et...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J3/12C08J3/24C08L89/00
CPCC08J3/12C08J3/245C08J2389/00
Inventor 卢神州温壮壮姜福建刘海娟刘诗喆邹婷
Owner NANTONG TEXTILE & SILK IND TECH RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap