Silica gel curing agent for preparation of thermal insulation material and preparation method thereof
A thermal insulation material and silica gel technology, applied in the direction of silicon oxide, silicon dioxide, etc., can solve problems such as practical impact and complicated preparation methods, and achieve the effects of eliminating gas-liquid dispersion, simple preparation methods, and optimized preparation processes
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] Embodiment 1 A kind of silicone gel curing agent for preparing thermal insulation material
[0029] The silicone gel curing agent used for preparing the thermal insulation material is composed of the following components and their parts by weight: 20 parts of silicon-based skeleton material, 0.1 part of filler, 3 parts of initiator, 25 parts of sodium bicarbonate, 4 parts sodium lauryl sulfate and 48 parts water.
[0030] The silicon-based framework material is composed of methanol silane triol, epoxy silane and amino silane in a weight ratio of 1:4:3.
[0031] The filler is composed of hydroxyapatite and aluminum chloride in a weight ratio of 3:7.
[0032] The initiator is composed of sodium persulfate and dimethylaniline in a weight ratio of 1:1:1.
[0033] The preparation method of the silicone gel curing agent for preparing the thermal insulation material comprises the following steps:
[0034] The silicon-based skeleton material, filler, initiator, sodium bicar...
Embodiment 2
[0035] Embodiment 2 A kind of silicone gel curing agent for preparing thermal insulation material
[0036] The silicone gel curing agent used for preparing the thermal insulation material is composed of the following components and their parts by weight: 2.5 parts of silicon-based skeleton material, 0.1 part of filler, 1 part of initiator, 12 parts of ammonia water, 12 parts of 1 part of sodium alkyl sulfonate and 30 parts of water.
[0037] The silicon-based framework material is composed of potassium triethylsiliconate and potassium butyldimethylsiliconate in a weight ratio of 1:4.
[0038] The filler is composed of hydrated aluminum salt, potassium chloride and water-based titanium dioxide in a weight ratio of 1:5:3.
[0039] The initiator is composed of methyl lithium and magnesium peroxide in a weight ratio of 1:1.
[0040] The preparation method of the silicone gel curing agent for preparing the thermal insulation material comprises the following steps:
[0041]The ...
Embodiment 3
[0042] Embodiment 3 A kind of silicone gel curing agent for preparing thermal insulation material
[0043] The described silicone gel curing agent for preparing thermal insulation material is composed of the following components and their parts by weight: 30 parts of potassium triethylsiliconate, 0.2 parts of calcium chloride, 4 parts of methyl zinc chloride, 30 parts of potassium hydroxide, 6 parts of Span 20 and 62 parts of ethanol.
[0044] The preparation method of the silicone gel curing agent for preparing the thermal insulation material comprises the following steps:
[0045] Mix potassium triethylsiliconate, calcium chloride, methylzinc chloride, potassium hydroxide and ethanol in the reaction kettle, set the temperature to 350°C and the pressure to 2.0Mpa, react for 5h, dilute with water, filter, After the filtrate was allowed to stand for 24 hours, the corresponding amount of Span 20 was added, stirred and filtered to obtain the result.
PUM
Property | Measurement | Unit |
---|---|---|
specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com