APAO-modified water-based alkyd resin and preparation method thereof

A water-based alkyd resin, modified technology

Active Publication Date: 2020-03-06
UNION FOSHAN CHEM +1
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The invention of the above-mentioned modified water-based alkyd resin has improved water resistance to a certain extent, but the adhesion an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An APAO modified water-based alkyd resin, which consists of the following formula in parts by weight: 26.0 parts of soybean oil, 7.5 parts of maleic anhydride grafted APAO, 28.0 parts of phthalic anhydride, 10.0 parts of terephthalic acid, and 18.0 parts of butanediol , 24.0 parts of trimethylolpropane, 15.0 parts of xylene, 3.5 parts of n-heptanoic acid, 5.0 parts of dimethylolpropionic acid, 8.0 parts of triethylamine, and 130.0 parts of deionized water.

[0027] A kind of preparation method of APAO modified water-based alkyd resin in the present embodiment, comprises the following steps:

[0028] a) In the multifunctional reaction kettle, add soybean oil, phthalic anhydride, terephthalic acid, butanediol, trimethylolpropane, dimethylol propionic acid and xylene in sequence according to the weight of the formula, and stir at a low speed Access to N 2 , to remove the O in the reactor 2 ;

[0029] b) Heat up to 110°C, keep it warm for 0.5h, remove free water, quickly...

Embodiment 2

[0032]An APAO modified water-based alkyd resin, in parts by weight, consists of the following formula: 22.0 parts of palm oil, 7.0 parts of maleic anhydride grafted APAO, 20.0 parts of acetic anhydride, 12.0 parts of isophthalic acid, neopentyl glycol 18.0 parts, 10.0 parts of pentaerythritol, 8.0 parts of diethylene glycol, 16.0 parts of xylene, 4.0 parts of n-heptanoic acid, 4.5 parts of dimethylolpropionic acid, 7.0 parts of ammonia water, and 125.0 parts of deionized water.

[0033] A kind of preparation method of APAO modified water-based alkyd resin in the present embodiment, comprises the following steps:

[0034] a) In the multifunctional reactor, add palm oil, acetic anhydride, isophthalic acid, neopentyl glycol, pentaerythritol, diethylene glycol, dimethylol propionic acid and diethylene glycol in sequence according to the weight of the formula Toluene, N was introduced under low-speed stirring 2 , to remove the O in the reactor 2 ;

[0035] b) Heat up to 120°C, k...

Embodiment 3

[0038] An APAO modified water-based alkyd resin, which consists of the following formula in parts by weight: 20.0 parts of castor oil, 9.0 parts of maleic anhydride grafted APAO, 20.0 parts of maleic anhydride, 10.0 parts of adipic acid, trimethylol 22.0 parts of propane, 9.5 parts of neopentyl glycol, 14.0 parts of xylene, 3.5 parts of n-heptanoic acid, 5.2 parts of dimethylolpropionic acid, 8.2 parts of triethylamine, and 115.0 parts of deionized water.

[0039] A kind of preparation method of APAO modified water-based alkyd resin in the embodiment, comprises the following steps:

[0040] a) In the multifunctional reaction kettle, add castor oil, maleic anhydride, adipic acid, trimethylolpropane, neopentyl glycol, dimethylol propionic acid and xylene in sequence according to the weight of the formula, at a low speed N was introduced under stirring 2 , to remove the O in the reactor 2 ;

[0041] b) Heat up to 110°C, keep it warm for 0.5h, remove free water, quickly raise t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to APAO-modified water-based alkyd resin and a preparation method thereof. The APAO-modified water-based alkyd resin is composed of the following components in parts by weight: 20.0-35.0 parts of vegetable oil fatty acid, 5.0-10.0 parts of maleic anhydride grafted APAO, 20.0-42.0 parts of a polyacid, 25.0-60.0 parts of a polyol, 10.0-20.0 parts of xylene, 2.5-5.0 parts of n-heptanoic acid, 3.5-7.0 parts of dimethylolpropionic acid, 4.0-12.0 parts of a neutralizing agent, and 100.0-150.0 parts of deionized water. The APAO modified water-based alkyd resin prepared by the method has the characteristics of good adhesion, water resistance, good fullness, and good sagging resistance, can be used for interior and exterior wall coatings, water-based industrial coatings, water-based floor coatings, water-based wood coatings and the like, and has huge application potential.

Description

technical field [0001] The invention relates to a modified water-based alkyd resin, in particular to an APAO modified water-based alkyd resin and a preparation method thereof, belonging to the technical field of water-based resin synthesis. Background technique [0002] Traditional solvent-based alkyd resins contain a large amount of organic solvents, especially benzene solvents, which volatilize into the atmosphere after drying, causing a large amount of first pollution to the air. A large amount of hydrocarbon solvents are used in alkyd resins, which can promote Photochemical smog causes secondary pollution to the air and is also a massive waste of resources and energy. Therefore, water-based alkyd resin is the development direction of alkyd resin, and it also meets the requirements of environmental protection. Water-based alkyd resin uses water as the dispersion medium, which is the most effective environment-friendly resin for reducing pollution and saving resources. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G63/91C08G63/78C08G63/49C09D167/08
CPCC08G63/48C08G63/78C08G63/918C09D167/08
Inventor 张武谢义鹏康伦国姚东生
Owner UNION FOSHAN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap