A kind of sponge type directional conductive rubber and preparation method thereof

A technology of conductive rubber and sponge, which is applied in the field of conductive rubber, can solve the problems of adverse effects of long-term use of equipment, failure to meet lightweight requirements, and unbalanced compression ratio, and achieve the effects of avoiding electrical performance reduction, reducing density, and improving mechanical strength

Active Publication Date: 2022-02-18
NO 33 RES INST OF CHINA ELECTRONICS TECHNOOGY GRP
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the problem of high density of conductive rubber with a solid structure, it cannot meet the lightweight requirements of modern information equipment; on the other hand, the rubber composite material with a solid structure has a low compression rate. There will be unbalanced compression ratio at the screw fastening part and the screw interval part, resulting in warping of the cover plate, which will have an adverse effect on the long-term use of the equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sponge type directional conductive rubber and preparation method thereof
  • A kind of sponge type directional conductive rubber and preparation method thereof
  • A kind of sponge type directional conductive rubber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) Wire arrangement: fix the wavy Monel wires on the frame at equal distances, the diameter of the Monel wires is 0.12mm, the distance between the metal wires is 1mm, and the thickness of the fixed frame is 1mm.

[0037] (2) Pretreatment: Use the spraying process to evenly spray the prepared coupling agent solution on the surface of the Monel silk, the spray gun pressure is 0.2MPa, and the spraying time is 30s. After the spraying is completed, put the Monel silk into the oven and set the temperature at 125°C. Dry for 2 hours, the coupling agent is silane coupling agent kh560, and the concentration of the configuration solution is 5%.

[0038] (3) Frame fixing: The pretreated Monel wire frames are tightly stacked in the mold along the same direction, the stacking length is 0.8m, and the gaps are sealed with a sealant after sealing.

[0039] (4) Pouring molding: Inject silicone rubber into the mold with a glue injection machine. After pouring, vulcanize at room temperatu...

Embodiment 2

[0042] (1) Arranging wires: fix the wavy tinned phosphor bronze wires on the frame at equal distances, the diameter of the tinned phosphor bronze wires is 0.1mm, the distance between the wires is 1mm, and the thickness of the fixed frame is 1mm.

[0043] (2) Pretreatment: Spray the prepared coupling agent solution evenly on the surface of tin-plated phosphor bronze wire by spraying process, the spray gun pressure is 0.2MPa, and the spraying time is 30s. After spraying, put the tin-plated phosphor bronze wire into the oven to set The temperature is 130°C, and it is dried for 3 hours. The coupling agent is silane coupling agent kh560, and the concentration of the configuration solution is 5%.

[0044] (3) Frame fixing: The pretreated tin-plated phosphor bronze wire frames are tightly stacked in the mold along the same direction, the stacking length is 1m, and the gaps are sealed with a sealant after sealing.

[0045] (4) Pouring molding: Inject silicone rubber into the mold with...

Embodiment 3

[0048] (1) Wire arrangement: fix the wavy aluminum alloy wires on the frame at equal distances, the diameter of the aluminum alloy wires is 0.15mm, the distance between the aluminum alloy wires is 1mm, and the thickness of the fixed frame is 1mm.

[0049] (2) Pretreatment: Spray the prepared coupling agent solution evenly on the surface of the aluminum alloy wire by spraying process, the spray gun pressure is 0.2MPa, and the spraying time is 30s. Dry for 4 hours, the silane coupling agent kh560 is used as the coupling agent, and the concentration of the configuration solution is 5%.

[0050] (3) Frame fixing: The pretreated aluminum alloy wire frames are tightly stacked in the mold along the same direction, the stacking length is 1m, and the gaps are sealed with a sealant after sealing.

[0051] (4) Pouring molding: Inject silicone rubber into the mold with a glue injection machine. After pouring, vulcanize at room temperature for 48 hours. The silicone rubber is Hangzhou Zhij...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of conductive rubber, in particular to a sponge-type directional conductive rubber and a preparation method thereof, comprising using liquid foamed silicone rubber as a rubber matrix, and the liquid foamed silicone rubber contains a foaming agent, a vulcanizing agent, and a color paste and other additives, the rubber matrix forms a spongy structure after vulcanization, metal wires are uniformly arranged inside the rubber matrix as a conductive carrier, and the surface of the continuous metal wires is sprayed with a coupling agent. A sponge-type The preparation method of directional conductive rubber includes five steps of wire arrangement, pretreatment, frame fixing, casting molding and cutting. The sponge-type directional conductive rubber prepared by the present invention has low density, good flexibility, good corrosion resistance and stable electrical properties. And other advantages, it can be widely used in consumer electronics, military communications, aerospace and other fields to realize the electromagnetic protection function of the product.

Description

technical field [0001] The invention relates to the field of conductive rubber, in particular to a sponge-type oriented conductive rubber and a preparation method thereof. Background technique [0002] Conductive rubber refers to a kind of conductive functional material prepared by mixing conductive filler and rubber matrix and then vulcanized. Among them, the conductive rubber prepared by filling silicone rubber with silver-plated metal powder as conductive filler has been industrialized, and its volume resistivity is ≤ 0.01Ω·cm, at the same time, it has the characteristics of high and low temperature resistance and corrosion resistance of silicone rubber, and has been widely used in aerospace, automotive industry, consumer electronics, military communications and other fields that require electromagnetic protection. [0003] Traditional conductive rubber products are compounded by rubber matrix materials, conductive fillers (including metal silver powder, carbon black, sil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/04C08K9/00C08K9/10C08K7/24C08K7/26C08J9/04B29C39/10B29C35/02B29C39/22
CPCC08J9/04B29C39/10B29C35/02B29C39/22C08J2383/04C08K9/00C08K9/10C08K7/24C08K7/26
Inventor 董春雨王月祥王执乾杨晓炯
Owner NO 33 RES INST OF CHINA ELECTRONICS TECHNOOGY GRP
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com