A self-assembled multidimensional quantum well cspbx 3 Perovskite Nanocrystalline Electroluminescent Diodes

A nanocrystalline and quantum well technology, applied in circuits, electrical components, electric solid devices, etc., can solve the problem of low external quantum efficiency of pure blue light and pure red LED, poor electrical, optical and thermal stability of nanocrystalline, and can not achieve practical Application standards and other issues, to achieve the effect of high luminous efficiency and external quantum efficiency of electroluminescent diode LED, good stability and less defects

Active Publication Date: 2021-02-02
UNIV OF SCI & TECH BEIJING
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This is because CsPbX 3 The nature of the intrinsic ionic crystal, its lattice formation energy is weak, resulting in very poor electrical, optical, and thermal stability of the nanocrystal, and the life of the LED device is very short, which is far from meeting the requirements of practical application standards.
And the external quantum efficiency of pure blue light and pure red LED is very low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A self-assembled multidimensional quantum well cspbx <sub>3</sub> Perovskite Nanocrystalline Electroluminescent Diodes
  • A self-assembled multidimensional quantum well cspbx <sub>3</sub> Perovskite Nanocrystalline Electroluminescent Diodes
  • A self-assembled multidimensional quantum well cspbx <sub>3</sub> Perovskite Nanocrystalline Electroluminescent Diodes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] lead halide (PbX 2 ), oleic acid (OA), and octylamine (OTA) were mixed according to the molar ratio of 1:0.3:0.6, placed in the container of the heating device, stirred, vacuumed, and heated to 100°C to obtain 0.5 mole Concentration of lead precursor solution; cesium carbonate (Cs 2 CO 3 ), oleic acid (OA) was added to octadecene (ODE) according to the molar ratio of 1:0.4, and then placed in a heating device container, stirred, vacuumed, and heated to 100°C to obtain 0.5 molar concentration of Cesium precursor solution; under inert gas protection conditions, the cesium precursor solution is heated to 100°C, and a 0.5 molar concentration of lead precursor solution is injected. Incubate for 60 seconds. During this process, the two-dimensional CsPbX 3 The nanosheets are gradually assembled into nanocrystals with a multidimensional quantum well structure, and the size of the nanocrystals is 20 nanometers. Use an ice bath to quickly cool down the reaction solution to 0°...

Embodiment 2

[0035] lead halide (PbX 2 ), oleic acid (OA), and octylamine (OTA) were mixed according to the molar ratio of 1:0.4:0.8, placed in the container of the heating device, stirred, vacuumed, and heated to 120°C to obtain 1.0 mole Concentration of lead precursor solution; cesium carbonate (Cs 2 CO 3 ), oleic acid (OA) was added into octadecene (ODE) according to the molar ratio of 1:0.5, and then placed in a heating device container, stirred, vacuumed, and heated to 120°C to obtain 0.7 molar concentration of Cesium precursor solution; under inert gas protection conditions, the cesium precursor solution is heated to 120°C, and a lead precursor solution with a concentration of 1.0 molar is injected. Incubate for 40 seconds. During this process, the two-dimensional CsPbX 3 The nanosheets are gradually assembled into nanocrystals with a multidimensional quantum well structure, and the size of the nanocrystals is 30 nanometers. Use an ice bath to quickly cool down the reaction solut...

Embodiment 3

[0039] lead halide (PbX 2 ), oleic acid (OA), and octylamine (OTA) were mixed according to the molar ratio of 1:0.5:1, placed in the container of the heating device, stirred, vacuumed, and heated to 150 ° C to obtain 1.5 moles Concentration of lead precursor solution; cesium carbonate (Cs 2 CO 3 ), oleic acid (OA) was added to octadecene (ODE) according to the molar ratio of 1:0.6, and then placed in a heating device container, stirred, vacuumed, and heated to 150°C to obtain 1.0 molar concentration of Cesium precursor solution; under inert gas protection conditions, the cesium precursor solution is heated to 150°C, and a lead precursor solution with a concentration of 1.5 moles is injected. Incubate for 30 seconds. During this process, the two-dimensional CsPbX 3 The nanosheets are gradually assembled into nanocrystals with a multidimensional quantum well structure, and the size of the nanocrystals is 40 nanometers. Use an ice bath to quickly cool down the reaction soluti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to view more

Abstract

A self-assembled multidimensional quantum well CsPbX 3 The perovskite nanocrystal electroluminescent diode belongs to the field of nanotechnology and light-emitting display. The diode of the present invention is composed of a transparent conductive oxide anode TOC, a hole transport layer material HTL, and a multidimensional quantum well structure CsPbX 3 The nanocrystalline light-emitting layer EL, the electron transport layer material ETL and the metal cathode CL are composed. The present invention first adopts the chemical synthesis method to prepare the self-assembled multidimensional quantum well CsPbX 3 Nanocrystalline solution, and then spin-coat the hole transport layer materials HTL, CsPbX on the TOC by spin-coating technology 3 Self-assembled multi-dimensional quantum well nanocrystalline solution, electron transport layer material ETL, and finally deposited metal cathode CL on the ETL by vacuum evaporation technology. The present invention can control the self-assembled multidimensional quantum well CsPbX 3 The dimension and composition of nanocrystals can realize any emission spectrum in the range of 400-700 nanometers visible light emission; and the multidimensional quantum well structure CsPbX 3 Nanocrystals have high fluorescence quantum yield and few defects; electroluminescent diodes have high luminous efficiency and external quantum efficiency, good stability and long life.

Description

technical field [0001] The invention belongs to the field of nanotechnology and light-emitting display, in particular to the preparation of self-assembled multi-dimensional quantum well cesium lead halide CsPbX 3 The perovskite nanocrystalline electroluminescence diode is applied in the fields of light emission, lighting and display, etc. Background technique [0002] Semiconductor nanocrystals with quantum confinement effects exhibit unique physical and electronic properties, such as size efficiency, adjustable band gap, and multiple excitonic effects, and have important applications and development prospects in the fields of optoelectronics, biology, and energy. Among them, the preparation process of the colloidal semiconductor nanocrystal solution is simple, the raw material cost is low, and the size and dimension can be adjusted through the chemical synthesis process, and the photoelectric characteristics can be well adjusted, showing great application potential. The me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01L51/50H01L51/56
CPCH10K71/12H10K50/115
Inventor 田建军毕成浩姚志伟
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap