Epoxy self-leveling antistatic topcoat and preparation method thereof
A self-leveling and antistatic technology, applied in epoxy resin coatings, conductive coatings, coatings, etc., can solve problems such as being susceptible to friction or impact, reduced electrical conductivity, and ignition of explosives, so as to avoid safety accidents and structural Increased strength and good electrical conductivity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0053] Example 1: An epoxy self-leveling antistatic topcoat, including component A and component B that are stored separately and mixed at a weight ratio of 5:1 when used, and the raw materials of each component and their corresponding The parts by weight are shown in Table 1, and are prepared by the following steps:
[0054] Step 1: Mix the corresponding parts by weight of bisphenol A epoxy resin, reactive diluent AGE and benzyl alcohol, then stir at 300rpm for 15 minutes, and continue to add the corresponding parts by weight of Disponer 9250 wetting and dispersing agent and poly 2 Methylsiloxane, polyacrylic acid and epoxy color paste, after 7.5 minutes of continuous stirring, add the corresponding parts by weight of wax powder and organic bentonite, disperse at a high speed for 15 minutes, the stirring speed is 700rpm, and continue to add the corresponding parts by weight of silicon For barium powder, increase the stirring speed to 1500rpm and disperse at high speed for 65min ...
Example Embodiment
[0061] Embodiment 2: An epoxy self-leveling antistatic top coating, which is different from Embodiment 1 in that it specifically includes the following steps:
[0062] Step 1: Mix the corresponding parts by weight of bisphenol A epoxy resin, reactive diluent AGE and benzyl alcohol, then stir at 200rpm for 20 minutes, and continue to add the corresponding parts by weight of Disponer 9250 wetting and dispersing agent and poly 2 Methylsiloxane, polyacrylic acid and epoxy color paste, after continuous stirring for 10 minutes, add the corresponding parts by weight of wax powder and organic bentonite, disperse at a high speed for 10 minutes, the stirring speed is 800rpm, continue to add the corresponding parts by weight of silicon barium Increase the stirring speed to 1800rpm and disperse at high speed for 50min to obtain slurry;
[0063] Step 2: Grind the slurry obtained in Step 1, and grind it to a fineness of 50μm, then add the epoxy color paste of corresponding parts by weight, and d...
Example Embodiment
[0066] Embodiment 3: An epoxy self-leveling antistatic top coating, which is different from Embodiment 1 in that it specifically includes the following steps:
[0067] Step 1: Mix the corresponding parts by weight of bisphenol A epoxy resin, reactive diluent AGE and benzyl alcohol, then stir at 400rpm for 10 minutes, and continue to add the corresponding parts by weight of Disponer 9250 wetting and dispersing agent and poly 2 Methylsiloxane, polyacrylic acid and epoxy color paste, after continuous stirring for 5 minutes, add the corresponding weight parts of wax powder and organic bentonite, disperse at high speed for 20 minutes, stirring speed of 600rpm, continue to add the corresponding weight parts of silicon barium Increase the stirring speed to 1200rpm and disperse at high speed for 80min to obtain slurry;
[0068] Step 2: Grind the slurry obtained in Step 1, and grind it to a fineness of 40 μm, and then add the epoxy color paste of corresponding parts by weight, and disperse ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap