A kind of light-moisture curing composition and preparation method thereof
A moisture-curing, composition technology, applied in the direction of non-polymer organic compound adhesives, polyether adhesives, adhesive types, etc., can solve the deformation of rigid and thin materials, high viscosity, and increased volume shrinkage and other problems, to achieve the effect of small shrinkage stress and low viscosity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] The raw materials and proportions (parts by weight) of the light-moisture curing composition are as follows:
[0027] 20 parts by weight of hydroxyl silicone oil
[0028] 20 parts by weight of polyethylene glycol (200) diacrylate
[0029] 10 parts by weight of hydroxypropyl acrylate
[0030] 15 parts by weight of isobornyl acrylate
[0031] CH 2 =CHCOO(CH 2 CH 2 O) 5 CH 2 Si(OCH 3 ) 3 3 parts by weight
[0032] 1 part by weight of 2-hydroxy-2-methyl-1-phenylacetone (1173)
[0033] 0.5 parts by weight of dibutyltin dilaurate
[0034] Hydroquinone 0.5 parts by weight
[0035] The above-mentioned components are sequentially added into the reaction kettle according to the amount, and the light-moisture curing composition is obtained after stirring evenly.
Embodiment 2
[0037] The raw materials and proportions (parts by weight) of the light-moisture curing composition are as follows:
[0038] 50 parts by weight of hydroxyl silicone oil
[0039] 30 parts by weight of polyethylene glycol (400) diacrylate
[0040] 20 parts by weight of hydroxyethyl acrylate
[0041] 20 parts by weight of isobornyl acrylate
[0042] CH 2 =CHCOO(CH 2 CH 2 O) 2 CH 2 Si(OCH 3 ) 3 5 parts by weight
[0043] 2 parts by weight of 1-hydroxycyclohexyl phenyl ketone (184)
[0044] 1 part by weight of stannous octoate
[0045] 2 parts by weight of p-methoxyphenol.
[0046] The above-mentioned components are sequentially added into the reaction kettle according to the amount, and the light-moisture curing composition is obtained after stirring evenly.
Embodiment 3
[0048] The raw materials and proportions (parts by weight) of the light-moisture curing composition are as follows:
[0049] Hydroxyl silicone oil 25 parts by weight
[0050] 22 parts by weight of polyethylene glycol (600) diacrylate
[0051] 17 parts by weight of hydroxypropyl acrylate
[0052] 17 parts by weight of isobornyl acrylate
[0053] CH 2 =CHCOO(CH 2 CH 2 O) 3 CH 2 Si(OCH 3 ) 3 4 parts by weight
[0054] 2-Methyl-2-(4-morpholinyl)-1-[4-(methylthio)phenyl]-1 acetone (907) 1.5 parts by weight
[0055] 0.8 parts by weight of dibutyltin diacetyl
[0056] Hydroquinone 1.3 parts by weight
[0057] The above-mentioned components are sequentially added into the reaction kettle according to the amount, and the light-moisture curing composition is obtained after stirring evenly.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com