Super-hydrophobic paint and preparation method thereof

A super-hydrophobic coating and coating technology, which is applied in the direction of antifouling/underwater coatings, anti-corrosion coatings, coatings, etc., can solve the problems of poor wear resistance of coatings, achieve strong binding force, simple preparation equipment, and convenient operation

Active Publication Date: 2020-07-10
TAIAN LEBANG ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the superhydrophobic coating prepared by the traditional method has a high hydrophobic angle and a low sliding angle, the coating has poor wear resistance and is not suitable for application on the interface with flowing media such as ships and sandstorm environments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The embodiments of the present invention provide a high wear-resistant super-hydrophobic composite coating, a preparation method and a coating made thereof.

[0039] The coating is composed of the following components in parts by mass:

[0040] 10 parts of vinyltrimethoxysilane as organosilane, 5 parts of zirconium n-propoxide and 1 part of zirconium nitrate as inorganic wear agent, N-(β-aminoethyl)-γ-aminopropyltrimethyl(ethyl)oxy 6 parts of silane as a catalyst, 1 part of perfluorooctyltriethoxysilane as a hydrophobic agent, 1 part of carbon fiber with a length of 100-500um, 1 part of glass flake powder with a particle size of D50 of 10um, tetraethylenepentamine and tetraethylenetriamine 2 parts, 75 parts of absolute ethanol and 9 parts of deionized water as solvents.

[0041] The composition of the above mass ratio is prepared according to the following preparation method:

[0042] (1) Weigh the carbon fiber, glass flake powder and absolute ethanol according to the...

Embodiment 2

[0048] The embodiments of the present invention provide a high wear-resistant super-hydrophobic composite coating, a preparation method and a coating made thereof.

[0049] The coating is composed of the following components in parts by mass:

[0050] 2.5 parts each of vinyl trimethoxysilane and γ-glycidyl etheroxypropyl trimethoxysilane as organosilane, 9 parts of zirconium n-propoxide and 1 part of zirconium nitrate as inorganic anti-wear agent, N-(β-aminoethyl base)-γ-aminopropyltrimethyl(b)oxysilane 9 parts as a catalyst, 3 parts of perfluorooctyltriethoxysilane as a hydrophobic agent, 3 parts of carbon fiber with a length of 100-500um, and a particle size D50 of 10um glass flakes 2 parts of powder, 2 parts of tetraethylenepentamine, 56 parts of absolute ethanol and 8 parts of deionized water as solvents.

[0051] The composition of the above mass ratio is prepared according to the following preparation method:

[0052] (1) Weigh the carbon fiber, glass flake powder and ...

Embodiment 3

[0058] The embodiments of the present invention provide a high wear-resistant super-hydrophobic composite coating, a preparation method and a coating made thereof.

[0059] The coating is composed of the following components in parts by mass:

[0060] 15 parts of γ-glycidyl etheroxypropyltrimethoxysilane as organosilane, 8 parts of zirconium n-propoxide and 1 part of zirconium nitrate as inorganic wear agent, N-(β-aminoethyl)-γ-aminopropyl 2 parts of trimethyl(ethyl)oxysilane and 1 part of ammonia water as catalyst, 2 parts of perfluorooctyltriethoxysilane as hydrophobic agent, 1 part of carbon fiber with a length of 100-500um, 2 parts of glass flake powder with particle size D50 of 10um, 1.5 parts of tetraethylenepentamine, 4 parts of tetraethylenetriamine, 64 parts of absolute ethanol and 8 parts of deionized water are used as solvents.

[0061] The composition of the above mass ratio is prepared according to the following preparation method:

[0062] (1) Weigh the carbon ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a super-hydrophobic paint, which is composed of the following components by mass: 5-15 parts of organosilane, 1-10 parts of an inorganic wear-resistant agent, 2-9 parts of a catalyst, 1-3 parts of a hydrophobic agent, 2-8 parts of one or two of tetraethylenepentamine and tetraethylenetriamine and 60-90 parts of a solvent. The beneficial effects of the invention are that: acoating continuous phase of the paint provided by the invention has high hardness, high wear resistance, high smoothness and super-hydrophobicity, at the same time the coating has high compactness andstrong combing power to a matrix. The paint provided by the invention can be coated and cured at room temperature, realizes scouring resistance, fouling resistance, corrosion resistance, aging resistance and other effects, is suitable for steel, glass, rubber and other matrixes, can be used for high-voltage cables, outdoor high-voltage equipment, ships, automobile glass and the like, and reducesthe scouring and shearing of seawater, silt and sandstorm to the coating to the maximum extent.

Description

[0001] This case is a divisional application. The invention name of the original application is: a high wear-resistant super-hydrophobic composite coating, its preparation method and the coating made of it. The filing date of the original application is: 2018-03-22. The application number is: 201810239657.1. technical field [0002] The invention relates to the technical field of paint coatings, in particular to a superhydrophobic paint and a preparation method thereof. Background technique [0003] Superhydrophobic surface refers to a surface with a contact angle greater than 150° and a rolling angle less than 10° and has a special wetting effect. It has special functions such as anti-icing, anti-corrosion, and anti-fouling. Self-cleaning and anti-flashover of electrical equipment, application of biomedical and bionic materials, waterproofing and anti-corrosion of pipelines, power transmission towers and cables against ice and snow in winter, and many other fields have broa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/14C09D5/08C09D5/16C09D7/61C08G77/58
CPCC08G77/58C08K2201/003C08K2201/004C09D5/08C09D5/1675C09D5/1687C09D183/14C08K13/04C08K7/06C08K3/40
Inventor 冯立明尹晓彤
Owner TAIAN LEBANG ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com