High-toughness polyester resin and its synthesis method

A technology of polyester resin and synthesis method, which is applied in the field of high-toughness polyester resin and its synthesis, can solve the problems of increased resin and filler ratio, increased cost, and more resins, etc., and achieves good wettability, high chemical resistance, The effect of high elongation at break

Active Publication Date: 2021-04-13
山东凯威尔新材料有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the resin and quartz are mixed evenly, during the curing process of the resin, the quartz of various particle sizes must be kept in suspension to avoid deposition and stratification. If the viscosity value of the selected unsaturated polyester resin is low, the quartz stone particles are easy to sink to form components layer state; if the viscosity value of the selected unsaturated polyester resin is too high, the ratio of resin to filler consumed in the production of quartz stone plates will increase, which will consume more resin and increase the cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness polyester resin and its synthesis method
  • High-toughness polyester resin and its synthesis method
  • High-toughness polyester resin and its synthesis method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068]The high tough polyester resin of this Example 1, according to a percentage of mass, as follows:

[0069]

[0070]The laboratory of this Example 1 synthesized 5 kg of high tough polyester resin, composed of the following steps:

[0071](1) Turning into the reaction bottle, 506 g of ethylene glycol, propylene glycol 135g, a strain diethylene glycol 843 g, phosphite 2.5 g, phthalic anhydride 1518 g, maleic acid anhydride 607g, 34g of diacid, nitrogen gas, temperature rise to temperature 60 ° C, the chlorhydride is substantially dissolved in the alcohol, and the stirring continues to heat up.

[0072](2) The amount of water rapidly increased to 156 ° C glycolic condensation, and the phase temperature starts to rise to 97 ± 2 ° C, which is charged 1.5 h at this effluent temperature.

[0073](3) Take the temperature of 205 ° C to 205 ° C in 4.5 ° C / 10min, and test the viscosity of the acid value and 150 ° C after insulation, to 29 mgKOH / g, the tapered viscosity of 1.57 MPa · S, start cooling,...

Embodiment 2

[0094]The high tough polyester resin of this Example 2, according to the mass percentage, the material composition is as follows:

[0095]

[0096]In this Example 2, a 30-ton high tough polyester resin was produced, composed of the following steps:

[0097](1) Trim: 310 kg of ethylene glycol, propylene glycol 810 kg, a decades of ethylene glycol 5060 kg, then phenyl phosphate phosphate 12 kg, then thrombohydride 9110 kg, maleic acid anhydride 3644kg, two Acid 202kg.

[0098](2) Nitrogen blowing: 1 to the nitrogen gas in the reaction kettle 15 minutes, then adjust the small nitrogen gas, enter the heating state.

[0099](3) Even the temperature: 90 ° C, the vertical condenser is cooled to the vertical condenser, and the temperature is raised to the water, the reference temperature is 155 to 160 ° C, heat insulation 0.5 h, and the phase temperature is controlled at 100 ± 1 ° C, then Press 15 ± 1 ° C / h to warm (control the temperature above the condition), warmed to 205 ° C.

[0100](4) Insulation: 20...

Embodiment 3

[0114]The high tough polyester resin of this Example 3, according to a percentage of mass, as follows:

[0115]

[0116]In this first embodiment, 30 tons of high tough polyester resin produced, composed of the following steps:

[0117](1) Trim: 3600kg of ethanol, propylene glycol 850kg, a strain diethylene glycol 5400 kg, trihydrol 530kg, tetrahydrol 1053 kg, new pentanediol 220kg, then vitrous phosphate 3kg, 6624 kg of phthalic anhydride, transluenaic acid anhydride 3283 kg, 600 kg of adipate, 1165 kg of fumarate, 540 kg of amphiphenylenedic acid.

[0118](2) Nitrogen blowing: 1 to the nitrogen gas in the reaction kettle 15 minutes, then adjust the small nitrogen gas, enter the heating state.

[0119](3) Even the temperature: 90 ° C, the vertical condenser is cooled to the vertical condenser, and the temperature is raised to the water, the reference temperature is 155 to 160 ° C, heat insulation 0.5 h, and the phase temperature is controlled at 100 ± 1 ° C, then Press 15 ± 1 ° C / h to warm (cont...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of polymer polyester materials, and in particular relates to a high-toughness polyester resin and a synthesis method thereof. In terms of mass percentage, the raw material composition consists of 20%-40% of glycol, 30%-50% of dibasic acid and / or acid anhydride, 20%-40% of dilute solvent and 0.01%-0.1% of auxiliary agent. The high-toughness polyester resin described in the present invention has low viscosity and high reactivity, strong bonding performance, high heat distortion temperature and elongation at break, and high strength of the resin cast body; it is used for making artificial marble chips Material bonding and artificial quartz stone plates, etc., have good wettability with fillers, good toughness, and excellent mechanical strength.

Description

Technical field[0001]The present invention belongs to the technical field of high molecular polyester materials, and in particular, a high tough polyester resin and a synthetic method thereof.Background technique[0002]With the improvement of people's living standards and the development of aesthetics, the decorative countertops are also gradually replaced by various colors of marble and artificial stone, but natural granites and marbles have a radioactive element. Micropores make it poorly polluting. Nowadays, people are more preferred in the decoration. Artificial stone is made of unsaturated polyester resin as a binder, equipped with a variety of natural stone powder, silica sand, glass powder and other inorganic powders and an appropriate amount of additives, color materials, and the like. They have natural stone unparalleled advantages in moisture-proof, antisocism, and planarity.[0003]The polyester resin is one of the basic raw materials of artificial quartzstones, and the bond...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/676C08G63/78C08F283/01C08F212/08
CPCC08F283/01C08G63/676C08G63/78C08F212/08C08F212/06
Inventor 邓金标闫晗谷成玉臧伟莉石卫民张培文苏旭
Owner 山东凯威尔新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com