A kind of Cu-doped cobalt hydroxide nanosheet array structure material and its preparation method and application

A technology of nanosheet array and structural material, which is applied in the field of Cu-doped cobalt hydroxide nanosheet array structural material and its preparation, can solve the problem of further improvement of catalytic activity, and achieve excellent catalytic activity and stability, and the preparation process environment Friendly, low-cost effect

Active Publication Date: 2022-04-12
ANHUI NORMAL UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, cobalt-based materials are rarely used in UOR and total urea electrolysis processes, and their catalytic activity needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of Cu-doped cobalt hydroxide nanosheet array structure material and its preparation method and application
  • A kind of Cu-doped cobalt hydroxide nanosheet array structure material and its preparation method and application
  • A kind of Cu-doped cobalt hydroxide nanosheet array structure material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A Cu-doped Co(OH) 2 A method for preparing a nanosheet array structure material, comprising the following steps:

[0048] Soak 2×3cm foam nickel in 6M hydrochloric acid solution for 15 minutes, wash the foam nickel three times with deionized water and absolute ethanol, and dry naturally to obtain foam nickel with a clean surface. Accurately measure 20mL deionized water and 15mL methanol into a clean beaker, then weigh 0.2mmol Cu(NO 3 ) 2 ·3H 2 O, 2mmol Co(NO 3 ) 2 ·6H 2 O and 5 mmol of hexamethylenetetramine were added into the beaker to obtain a homogeneous solution. Transfer the solution to a 50mL polytetrafluoroethylene-lined stainless steel reaction kettle, insert the pre-treated nickel foam obliquely into the solution, seal it and react in an oven at 120°C for 6 hours, and cool it naturally to room temperature after the reaction is over. The nickel foam covering the sample was washed three times with deionized water and absolute ethanol, and then the nickel ...

Embodiment 2

[0057] Cu-doped Co(OH) 2 A method for preparing a nanosheet array structure material, comprising the following steps:

[0058] Accurately measure 20mL deionized water and 15mL methanol into a clean beaker, then weigh 0.1mmol or 0.3mmol Cu(NO 3 ) 2 ·3H 2 O, 2mmol Co(NO 3 ) 2 ·6H 2 O and 5mmol hexamethylenetetramine were added into the beaker and stirred evenly. Insert the dried nickel foam obliquely into a 50mL polytetrafluoroethylene-lined stainless steel reaction kettle, transfer the solution to the reaction kettle after the solution is fully dissolved, and react in an oven at 120°C for 6 hours after sealing. After the reaction was finished, it was naturally cooled to room temperature, and the nickel foam covering the sample was washed three times with deionized water and absolute ethanol, and then the nickel foam covering the sample was dried in an oven at 60°C for 8 hours. Cu(NO 3 ) 2 ·3H 2 When the amount of O added is 0.1 mmol, the Cu-doped Co(OH) with a Cu dopi...

Embodiment 3

[0063] A Cu-doped Co(OH) 2 Application of nanosheet array structure materials as catalysts for urea oxidation reaction (UOR).

[0064] The specific application method is: doping Co(OH) with Cu with an area of ​​0.5×0.5cm 2 The nanosheet array structure material was used as the working electrode, and the Pt wire and Ag / AgCl electrode were used as the counter electrode and reference electrode, respectively. The CHI760E electrochemical workstation was used for testing in 1.0M KOH and 0.33M urea electrolyte solutions. Co(OH) prepared on nickel foam and nickel foam supported by commercial Pt / C, respectively 2 Nanosheets were used as working electrodes, and their UOR properties were measured for comparison, Co(OH) 2 The preparation is to omit the Cu(NO in the raw material on the basis of embodiment 1 3 ) 2 ·3H 2 O prepared. Using linear sweep voltammetry (LSV) at 5.0mV s -1 Polarization curves were obtained at a scan rate of 90% and an ohmic compensation of 90%.

[0065] F...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a Cu-doped cobalt hydroxide nanosheet array structure material and its preparation method and application; dissolving copper salt, cobalt salt and hexamethylenetetramine in a mixed solvent of water and methanol, and transferring the solution Put the nickel foam into the reaction kettle, place the nickel foam in the solution, and carry out solvothermal reaction. After the reaction is completed, cool to room temperature, wash and dry the product, and then Cu-doped Co(OH) can be prepared. 2 Nanosheet array structure material; Cu-doped Co(OH) of the present disclosure 2 Nanosheet array structure, Co(OH) can be effectively tuned by Cu doping 2 The electronic structure reduces resistance, increases active sites, improves hydrophilicity, and accelerates electron transfer rate; the Cu-doped Co(OH) 2 As an electrocatalyst for urea oxidation reaction, hydrogen evolution reaction and total urea electrolysis reaction, the nanosheet array structure material has the advantages of high activity, good durability, simple preparation process and low cost. have value.

Description

technical field [0001] The invention belongs to the field of nanomaterial preparation methods and electrocatalysis applications, and in particular relates to a Cu-doped cobalt hydroxide nanosheet array structure material and its preparation method and application. Background technique [0002] Currently, hydrogen is considered as one of the most attractive energy sources to replace traditional fossil fuels because of its high energy density and environmental protection. Water electrolysis for hydrogen production has been considered as a sustainable and promising pathway, but a considerable potential is usually required for sustained hydrogen production due to the slow kinetics of the anodic oxygen evolution reaction (OER). And in the whole water electrolysis process, H 2 and O 2 Simultaneously, explosive H may be formed 2 / O 2 mixture. Therefore, it is very necessary to develop feasible methods to replace OER with a more facile oxidation reaction to achieve efficient, s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G11/30H01G11/86H01G11/24
CPCH01G11/24H01G11/30H01G11/86
Inventor 吴正翠王相宇高峰
Owner ANHUI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com