Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A preparation method of a zinc oxide varistor ceramic precursor for a surge arrester

A technology of ceramic precursors and varistor valves, which is applied in the direction of varistor cores, varistors, and manufacturing resistor chips, can solve the problems of complex process and poor applicability, and achieve the promotion of reactivity, Effect of improving structural performance and increasing strength

Active Publication Date: 2022-05-03
ANHUI JINHUA ZINC OXIDE CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the currently used molding methods are mainly thermal cross-linking and isostatic cross-linking or based on mercapto-vinyl photocuring technology, which still have the defects of poor applicability and complicated process. In order to solve the above problems, it is urgent for those skilled in the art to develop A preparation method and application of a zinc oxide varistor ceramic precursor for surge arresters to meet existing market demands and performance requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Firstly, the ceramic precursor of the arrester zinc oxide varistor valve is prepared, including the following steps:

[0026] 1. In parts by weight, 90 parts of oxidation, 7 parts of bismuth trioxide whiskers, and 23 parts of polycarbosilane are dispersed in 91 parts of a mixed solvent composed of tetrahydrofuran and xylene at a volume ratio of 1:1, and magnetically stirred at a uniform speed for 15 minutes , to make it evenly mixed, and then slowly dropwise add 0.1 parts of cumene hydroperoxide and 1.6 parts of tetramethyltetravinylcyclotetrasiloxane, keep continuous magnetic stirring at a constant speed, and react at 80°C for 6h, After the reaction is over, remove tetrahydrofuran and xylene solvents in the mixture by cooling, filtering, and distillation under reduced pressure to obtain a mixture of zinc oxide and polycarbosilane; 2. polycarbosilane, trimethoxyvinylsilane, nickel triacetylacetonate, Triallyl cyanurate is uniformly mixed and transferred to the reactor a...

Embodiment 2

[0029] Firstly, the ceramic precursor of the arrester zinc oxide varistor valve is prepared, including the following steps:

[0030] 1. In parts by weight, 4 parts of bismuth trioxide whiskers, 19 parts of polycarbosilane and 85 parts of zinc oxide are dispersed in 85 parts of a mixed solvent composed of tetrahydrofuran and xylene in a volume ratio of 1:1, and magnetically stirred at a uniform speed Mix well for 15 minutes, then slowly add 0.05 parts of cumene hydroperoxide and 0.8 parts of tetramethyltetravinylcyclotetrasiloxane dropwise, keep continuous magnetic stirring at a constant speed, and react for 4 hours at 65°C , after the reaction is over, remove tetrahydrofuran and xylene solvents in the mixture by cooling, filtering, and distillation under reduced pressure, and combine to obtain a mixture of zinc oxide and polycarbosilane; Nickel acetone and triallyl cyanurate were evenly mixed and transferred to the reaction kettle according to the ratio of parts by weight of 7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
densityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of zinc oxide materials, in particular to a method for preparing a ceramic precursor of a zinc oxide pressure-sensitive valve sheet for lightning arresters. The process is introduced, and the polymer ceramic precursor is obtained by electron beam irradiation cross-linking, and then under the protection of pressureless nitrogen, the zinc oxide varistor valve sheet of the arrester is obtained by pyrolysis, which has strong surge resistance, high potential gradient and non-toxic The advantages of good linearity are suitable for the manufacture of valve plates and overvoltage protection for large and small zinc oxide arresters, and are suitable for arrester applications.

Description

technical field [0001] The invention belongs to the technical field of zinc oxide materials, in particular to a method for preparing a ceramic precursor of a zinc oxide pressure-sensitive valve plate for lightning arresters. Background technique [0002] Surge arrester is a protective device that can absorb overvoltage energy and limit the magnitude of overvoltage. When in use, install the arrester near the protected equipment and connect it in parallel with the protected equipment. The protective characteristics of surge arresters are the basis of insulation coordination for power transmission and distribution equipment. A surge arrester with excellent performance can limit the overvoltage in the power system to a level that is harmless to the insulation. Improving the protection performance of lightning arresters can not only improve the operational reliability of power transmission and distribution systems, but also reduce the insulation level of electrical equipment, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/453C04B35/81C04B35/626C04B35/622C04B35/634C04B41/86C03C8/00H01C7/112H01C17/00H01C17/30C08F283/00C08F230/08C08F226/06
CPCC04B35/453C04B35/62605C04B35/622C04B35/63448C04B41/86C04B41/5022C03C8/00H01C7/112H01C17/006H01C17/30C08F283/00C04B2235/5276C04B2235/3298C04B2235/6562C04B2235/6565C04B2235/6567C08F230/085C08F226/06C04B41/4539C04B41/0072
Inventor 刘艺
Owner ANHUI JINHUA ZINC OXIDE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com