Deep thread sealing slurry line and manufacturing method and device thereof

A thread sealing and manufacturing method technology, applied in textile and papermaking, liquid/gas/vapor textile processing, fiber processing, etc., can solve the problems of cutting damage to raw material tape, increased workload, and reduced viscose wettability. , to achieve the effect of preventing thread seal leakage, maintaining stability and good tensile strength

Pending Publication Date: 2020-12-04
四会市昊天密封材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the anaerobic thread sealant has the following deficiencies in the actual installation process: 1. The anaerobic adhesive only cures the metal; Cooling with lubricating oil or water will cause impurities of lubricating oil or water to adhere to the teeth. The installation of anaerobic adhesive needs to clean the oil, which will increase the workload and affect the installation efficiency; 3. The installation of anaerobic thread sealant requires up to 24 hours to fully cure (If the temperature is low, the curing time will be longer); 4. If the pipe fittings installed with anaerobic thread sealant need to be disassembled, the residue needs to be further processed before reinstallation
[0004] The following problems exist in the raw material belt: 1. For the current new deep pipe thread is relatively sharp, the raw material belt is cut and damaged during installation, which affects the installation and sealing effect of the product; 2. Due to the current large-diameter thread pitch depth and height , the sealing effect of using raw material tape is also difficult to meet the sealing requirements and winding is also very inconvenient; 3. The residues during the use of raw material tape are difficult to degrade in nature, causing environmental pollution
[0005] In contrast, the thread sealing wire can avoid the above-mentioned problems and deficiencies, but the existing thread sealing wire still has the following deficiencies: 1. The viscose glue is unevenly glued on the fiber thread; Insufficient combined force affects construction efficiency; 3. The wettability of the adhesive decreases with time, and the ideal use effect cannot be achieved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Deep thread sealing slurry line and manufacturing method and device thereof
  • Deep thread sealing slurry line and manufacturing method and device thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] as attached figure 1 As shown, it is a schematic structural diagram of a manufacturing device for a deep thread sealing slurry line provided by an embodiment of the present invention. The manufacturing device includes:

[0033] Extrusion die 4, used for extruding and sizing chemical fiber filaments;

[0034] Pay-off mechanism 1, used to send chemical fiber filaments to the extrusion die 4;

[0035] The slurry feeding mechanism 5 is used to deliver the slurry to the extrusion die 4 to sizing the chemical fiber filaments being extruded.

[0036] Wherein, the slurry supply mechanism 5 can include a slurry supply barrel and a plunger pump, and the slurry supply barrel can be communicated with the extrusion die 4 through the plunger pump and the slurry supply high-pressure pipe 3; Guide wheels 2 can also be provided between them, so that the chemical fiber filaments can be stably sent to the extrusion die 4 for extrusion and sizing.

[0037] In addition, the manufacturing...

Embodiment 2

[0039] This embodiment provides a method for manufacturing a deep thread sealing slurry line using the manufacturing device provided in the above embodiment 1, which includes the following steps:

[0040] S1. Weigh 42.5kg of simethicone oil, 3.25kg of talcum powder, 0.75kg of white carbon black, and 0.75kg of hydroxypropyl methylcellulose, and set aside. Among them, the viscosity of simethicone oil at 25°C is 10000cSt, the appearance is a colorless transparent oily liquid, and the relative density is 0.971~0.976; 2 o 3 Calculation) ≤ 0.02%, loss on ignition (1000°C) ≤ 6.00%, magnet extract ≤ 0.04%, moisture ≤ 0.5%, particle size 5000 mesh, whiteness > 93, pH value 8 ~ 10; in white carbon black SiO 2 Content (dry product) ≥ 90%, sieve residue (45μm) ≤ 0.5%, heating loss 4.0-8.0%, ignition loss (dry product) ≤ 7.0%, pH value 5.0-8.0, total copper content ≤30mg / kg, total manganese content ≤50mg / kg, total iron content ≤1000mg / kg, DBP absorption value 2.00~3.50cm / g; particle siz...

Embodiment 3

[0045] This embodiment provides a method for manufacturing a deep thread sealing slurry line using the manufacturing device provided in the above embodiment 1, which includes the following steps:

[0046]S1. Weigh 4 kg of simethicone oil, 3.5 kg of talcum powder, 1 kg of white carbon black, and 1 kg of hydroxypropyl methylcellulose, and set aside. Among them, the viscosity of simethicone oil at 25°C is 8000cSt, the appearance is a colorless transparent oily liquid, and the relative density is 0.971~0.976; 2 o 3 Calculation) ≤ 0.02%, loss on ignition (1000°C) ≤ 6.00%, magnet extract ≤ 0.04%, moisture ≤ 0.5%, particle size 5000 mesh, whiteness > 93, pH value 8 ~ 10; in white carbon black SiO 2 Content (dry product) ≥ 90%, sieve residue (45μm) ≤ 0.5%, heating loss 4.0-8.0%, ignition loss (dry product) ≤ 7.0%, pH value 5.0-8.0, total copper content ≤30mg / kg, total manganese content ≤50mg / kg, total iron content ≤1000mg / kg, DBP absorption value 2.00~3.50cm / g; particle size of hyd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
loss on ignitionaaaaaaaaaa
relative humidityaaaaaaaaaa
Login to view more

Abstract

The invention is applicable to the field of deep pipeline thread sealing materials, and provides a deep thread sealing slurry line and a manufacturing method and device thereof. The manufacturing method of the deep thread sealing slurry line comprises the following step that slurry is extruded to be applied to chemical fiber filaments, and thus the deep thread sealing slurry line is obtained; wherein the slurry is prepared from the following components in parts by weight: 40-45 parts of dimethyl silicone oil, 30-35 parts of talcum powder, 5-10 parts of white carbon black and 5-10 parts of hydroxypropyl methyl cellulose. The thread sealing slurry line with high viscosity, high strength and excellent sealing performance is prepared by coating the chemical fiber filaments with corresponding slurry, has the characteristics of wear resistance, self-lubricating property, high and low temperature resistance, aging resistance and corrosion resistance, can be used for a long time within a widetemperature range, and is not cured within the temperature range, so that the original viscosity and self-lubricating property are maintained, and the better adhesion is realized in the mounting process.

Description

technical field [0001] The invention belongs to the field of deep pipeline thread sealing materials, and in particular relates to a deep thread sealing slurry line, a manufacturing method and a manufacturing device thereof. Background technique [0002] At present, the widely used sealing materials in pipeline thread sealing are anaerobic pipeline thread sealant, polytetrafluoroethylene raw material tape and thread sealing line. [0003] However, the anaerobic thread sealant has the following deficiencies in the actual installation process: 1. The anaerobic adhesive only cures the metal; Cooling with lubricating oil or water will cause impurities of lubricating oil or water to adhere to the teeth. The installation of anaerobic adhesive needs to clean the oil, which will increase the workload and affect the installation efficiency; 3. The installation of anaerobic thread sealant requires up to 24 hours to fully cure (If the temperature is low, the curing time will be longer)...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643D06M15/09D06M11/74D06M11/79D06B3/18
CPCD06M15/643D06M15/09D06M11/74D06M11/79D06B3/18D06M2200/40
Inventor 钟远锋
Owner 四会市昊天密封材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap