A biomimetic modified valve material and its preparation method and application

A biological valve and valve technology, applied in the fields of medical formula, tissue regeneration, medical science, etc., can solve the problems of valve thrombosis, valve life shortening, calcification mechanical properties, etc., achieve anti-calcification ability promotion, simple preparation process, and extensive sources Effect

Active Publication Date: 2021-08-31
SICHUAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, clinical data also showed that GLU-treated BHVs could inhibit the adhesion and proliferation of endothelial cells due to the high toxicity of GLU, and GLU-treated BHVs showed disadvantages such as immunogenic response, calcification, etc.
Therefore, GLU-treated BHVs lead to problems such as valve thrombosis, difficult endothelialization, severe calcification, and shortened valve life (usually only 10-15 years) due to altered mechanical properties and impaired function.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A biomimetic modified valve material and its preparation method and application
  • A biomimetic modified valve material and its preparation method and application
  • A biomimetic modified valve material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A preferred embodiment of the present invention provides a method for preparing a bionic modified valve material, specifically a method for preparing red blood cell membrane-wrapped nano drug-loaded particles for bionic modification of porcine pericardial valves, which is obtained by the following steps:

[0045] 1) Preparation of drug-loaded PLGA nanoparticles (RAPA&AC@PLGA)

[0046] PLGA (10 mg, MW.50000, 50:50), RAPA (1 mg), AC (1 mg) were dissolved in 1 mL of dimethylsulfoxide (DMSO). Then the mixed solution was added dropwise to 3 mL of water and stirred gently. After 2h, use a dialysis bag (MWCO=3500da) to dialyze for 48h to prepare drug-loaded nanoparticles, such as figure 1 .

[0047] 2) Preparation of erythrocyte membrane vesicles

[0048] Whole blood was centrifuged at 4°C (2000rpm, 10min) to remove serum. Red blood cells were washed with phosphate buffered saline (PBS, 3 times) pH=7.4. Red blood cells were then resuspended in 0.25×PBS (pH=7.4) containing...

Embodiment 2

[0054] A preferred embodiment of the present invention provides a method for preparing a biomimetic modified valve material, specifically a method for preparing platelet membrane-wrapped nano drug-loaded particles for bionic modification of porcine pericardial valves, which is obtained by the following steps:

[0055] 1) Preparation of drug-loaded nanoparticles

[0056] PLGA (10 mg, MW.50000, 50:50), a hydrophobic anti-inflammatory drug (1 mg) was dissolved in 1 mL of dimethyl sulfoxide (DMSO). Then the mixed solution was added dropwise to 3 mL of water and stirred gently. After 2 hours, use a dialysis bag (MWCO=3500da) to dialyze for 48 hours to prepare drug-loaded nanoparticles.

[0057] 2) Preparation of platelet membrane

[0058] First, whole blood was centrifuged at 1600 rpm for 20 minutes to obtain platelets. Platelets were washed with phosphate buffered saline (PBS, 3 times) pH=7.4. Platelets were then resuspended in 0.25×PBS (pH=7.4) containing EDTAK2 at 4°C. Afte...

Embodiment 3

[0064] A preferred embodiment of the present invention provides a method for preparing a biomimetic modified valve material, specifically a method for preparing macrophage membrane-wrapped nano drug-loaded particles for bionic modification of porcine pericardial valves, which is obtained by the following steps:

[0065] 1) Preparation of drug-loaded nanoparticles

[0066] PLGA (10 mg, MW.50000, 50:50), hydrophobic anticoagulant drug (1 mg) was dissolved in 1 mL dimethyl sulfoxide (DMSO). Then the mixed solution was added dropwise to 3 mL of water and stirred gently. After 2 hours, use a dialysis bag (MWCO=3500da) to dialyze for 48 hours to prepare drug-loaded nanoparticles.

[0067] 2) Preparation of macrophage membrane

[0068] Macrophages are first cultured and collected. Then, macrophages were resuspended in 0.25×PBS (pH=7.4) at 4°C. After 30 min, subcellular organelles such as macrophage nuclei were removed by gradient density centrifugation, and macrophage membranes w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bionic modified valve material and its preparation method and application, comprising the following steps: A. synthesizing drug-loaded nanoparticles loaded with drugs; B. preparing cell membrane vesicles; C. combining drug-loaded nanoparticles with cell membrane vesicles Bubble mixing and extruding for multiple times to prepare cell membrane-wrapped drug-loaded nanoparticles; D. cross-linking cell membrane-wrapped drug-loaded nanoparticles to the surface of the biovalve to obtain the final product. The method of the present invention has the advantages of simple operation, mild reaction conditions, etc., and the bionic modified valve material prepared by the method of the present invention wraps nanometer drug-loaded particles, which can well solve the problems of easy thrombosis, calcification and Endothelialization difficulties and other problems. At the same time, the strategy of combining the cell membrane bionic drug delivery system with the valve provides a new generation of treatment mode for the safe and efficient treatment of valvular heart disease.

Description

technical field [0001] The invention belongs to the technical field of biomedical materials, and in particular relates to a bionic modified valve material and its preparation method and application. Background technique [0002] Valvular heart disease (VHD) currently affects more than 100 million people worldwide and primarily consists of valve stenosis or regurgitation. Degenerative valvular disease and rheumatic heart disease have become a growing problem among older populations in developing countries as the population ages. In recent years, the medical treatment for heart valve dysfunction is still being explored, and the lack of understanding of the pathophysiology and progression of VHD greatly limits the development of its medical treatment. In the case of severe valve dysfunction, replacing the damaged valve with an artificial valve (mainly including mechanical and biological valves) is the most effective solution. By 2050, more than 850,000 patients are expected t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/36A61L27/54
CPCA61L27/3604A61L27/3687A61L27/54A61L2300/412A61L2300/42A61L2300/602A61L2300/622A61L2400/12A61L2430/20
Inventor 王云兵胡成罗日方
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com