High-temperature-resistant anti-corrosion potassium silicate coating and preparation method thereof

An anti-corrosion, high-temperature-resistant technology, applied in anti-corrosion coatings, alkali metal silicate coatings, fire-resistant coatings, etc., can solve problems such as surface corrosion, cracking or falling off, affecting popularization and application, and achieve strong bonding, crack prevention and Good effect of falling off and stabilizing performance

Inactive Publication Date: 2021-01-12
江苏康祥实业集团有限公司 +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a high temperature resistant and anti-corrosion potassium silicate coating and its preparation method, to solve the problem that the surface of the existing architectural coatings in the rainy and humid places in the south will appear when they are used for a long time in the above background technology. Corrosion, cracking or falling off, its anti-corrosion performance and high temperature resistance are not very good, which affects the promotion and application of the problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1, a kind of potassium silicate paint of high temperature resistance and anticorrosion, by mass, present embodiment is made up of following specific components:

[0015] The high temperature resistant solute is composed of the following specific components: epoxy resin 10kg, palm oil 8kg, precipitated barium sulfate 2.3kg, quartz stone powder 5.7kg, butyl acetate 3.2kg, asbestos powder 12kg, methylhydrogen siloxane 12kg, organic soil 11kg; the anti-corrosion solute is composed of the following specific components: fluorine-containing rust emulsion 28kg, talc powder 8kg, high titanium powder 3.8kg, water-based epoxy emulsion 7kg, high chlorinated polyethylene resin 4.5kg, organosiloxane 4.3 kg, diatomaceous earth 12kg; the coupling solvent consists of the following specific components: potassium silicate solution 40kg, silane coupling agent 10kg, defoamer 1.5kg, wetting agent 1.2kg, leveling agent 1.8kg; The following specific components are composed: fungicid...

Embodiment 2

[0021] Embodiment 2, a kind of potassium silicate paint of high temperature resistance and anticorrosion, by mass, present embodiment is made up of following specific components:

[0022] The high temperature resistant solute is composed of the following specific components: epoxy resin 12kg, palm oil 10kg, precipitated barium sulfate 3kg, quartz stone powder 6.3kg, butyl acetate 5.2kg, asbestos powder 14.5kg, methylhydrogen siloxane 14.8kg, organic Soil 12.3kg; the anti-corrosion solute is composed of the following specific components: fluorine-containing rust emulsion 32kg, talcum powder 9.8kg, high titanium powder 6.7kg, water-based epoxy emulsion 8.2kg, high chlorinated polyethylene resin 5.1kg, organic Siloxane 4.9kg, diatomaceous earth 13.2kg; coupling solvent consists of the following specific components: potassium silicate solution 42.5kg, silane coupling agent 11.2kg, defoamer 1.6kg, wetting agent 1.6kg, leveling The solvent is 2.1kg; the blending solvent is composed ...

Embodiment 3

[0028] Embodiment 3, a kind of potassium silicate paint of high temperature resistance and anticorrosion, by mass, present embodiment is made up of following concrete components:

[0029] The high temperature resistant solute is composed of the following specific components: epoxy resin 15kg, palm oil 17kg, precipitated barium sulfate 4.5kg, quartz stone powder 9.2kg, butyl acetate 6.8kg, asbestos powder 18.4kg, methylhydrogen siloxane 19.5kg, 15.7kg of organic soil; the anti-corrosion solute is composed of the following specific components: 36.2kg of fluorine-containing rusty emulsion, 12.5kg of talcum powder, 9kg of high titanium powder, 10kg of water-based epoxy emulsion, 6.3kg of high chlorinated polyethylene resin, organic Siloxane 5.9kg, diatomaceous earth 16.5kg; coupling solvent consists of the following specific components: potassium silicate solution 46kg, silane coupling agent 13.6kg, defoamer 2kg, wetting agent 1.5kg, leveling agent 2.3 kg; the blending solvent is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-temperature-resistant anti-corrosion potassium silicate coating which is prepared from the following four components in percentage by weight: a high-temperature-resistant solute, an anti-corrosion solute, a coupling solvent and a blending solvent, wherein the high-temperature-resistant solute is composed of the following components: 10-15% of epoxy resin, 8-17% of palm oil, 2.3-4.5% of precipitated barium sulfate, 5.7-9.2% of quartz stone powder, 3.2-6.8% of butyl acetate, 12-18.4% of asbestos powder, 12-19.5% of methylhydrosiloxane and 11-15.7% of organic soil.The anti-corrosion solute is prepared from the following components: 28.7-36.2% of fluorine-containing emulsion with rust, 8-12.5% of talcum powder, 3.8-9% of high titanium powder, 7-10% of waterborneepoxy emulsion, 4.5-6.3% of high chlorinated polyethylene resin, 4.3-5.9% of organosiloxane and 12-16.5% of diatomite; the coupling solvent is prepared from the following components: 40-46 percent ofpotassium silicate solution, 10-13.6 percent of silane coupling agent, 1.5-2 percent of defoamer, 1.2-1.5 percent of wetting agent and 1.8-2.3 percent of leveling agent; the blending solvent is composed of the following components: 1%-2% of a bactericide, and 10-14% of water, a potassium silicate solution which is good in viscosity and is used as a main component improves the stability of the whole coating, and the viscosity and adhesive force of each component are enhanced.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a high-temperature-resistant and anti-corrosion potassium silicate coating and a preparation method thereof. Background technique [0002] Paint is a material that can be well bonded to the base material and form a complete and tough protective film on the surface of an object, called a paint. Paint and paint are the same concept. Paint is a customary name that people have used for a long time. After it was introduced into my country, it has been used in the construction industry. The effect of coating can be summarized into three aspects: protective effect, decorative effect, special functional effect. The general composition of coatings: including film-forming substances, pigments and fillers, solvents, and additives. Coatings are one of the indispensable materials for the development of the national economy. Due to the many special functions of coatings, there ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/04C09D163/00C09D5/08C09D7/61C09D7/63C09D7/65C09D7/20C09D1/04
CPCC08K2003/0881C08K2003/3045C08K2201/014C08L2201/08C08L2205/025C08L2205/035C09D1/04C09D5/08C09D5/18C09D201/04C09D7/20C09D7/61C09D7/63C09D7/65C09D7/70C08L63/00C08L23/286C08L91/00C08K13/04C08K7/12C08K3/36C08K3/34C08K5/5419C08K5/101C08K3/08
Inventor 朱雪松季成平刘仕通孙明于海洋
Owner 江苏康祥实业集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products