Preparation process of electromagnetic shielding material for constructing hydrophobic coating on surface of wood-based material

A technology of electromagnetic shielding materials and hydrophobic coatings, which is applied in metal material coating technology, magnetic field/electric field shielding, coatings, etc., can solve the problems of reducing the magnetic properties of chemical coatings, unsuitability, and poor bonding of wood substrates to achieve high-efficiency electromagnetic coatings. Effects of shielding properties, simple operation, and excellent superhydrophobic properties

Active Publication Date: 2021-03-12
NORTHEASTERN UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, after electroless plating under acidic conditions, medium and high phosphorus coatings are obtained, and the bonding force with the wood substrate is poor.
In addition, if the phosphorus content is too high (>8wt%), it will also reduce the magnetic properties of the electroless coating, so it is not suitable for electromagnetic shielding materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of electromagnetic shielding material for constructing hydrophobic coating on surface of wood-based material
  • Preparation process of electromagnetic shielding material for constructing hydrophobic coating on surface of wood-based material
  • Preparation process of electromagnetic shielding material for constructing hydrophobic coating on surface of wood-based material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Step 1: Cut paulownia wood chips with a thickness of about 1.5mm into 50cm×50cm and place them in a drying oven, and dry them at 100°C for 24 hours to remove all moisture. Thereafter, the prepared wood was placed in an ethanol solution for ultrasonic treatment for 20 minutes, and then placed in an ultrapure aqueous solution at about 60 ° C for 20 minutes, so that it was treated three times alternately.

[0034] Step 2: Place the pretreated wood in the configured sensitizing solution (concentration of stannous chloride solution is 20g / L, 30% dilute hydrochloric acid 12mL / L), sensitize for 10min, and then use deionized water repeatedly Rinse for about 10 minutes.

[0035] Step 3: Place the sensitized wood in the prepared activation solution (concentration of palladium chloride solution is 0.5g / L, 30% dilute hydrochloric acid 25mL / L), activate for 10min, and then rinse repeatedly with deionized water About 10 minutes.

[0036] Step 4: Place the activated wood in the 500m...

Embodiment 2

[0040] Step 1: Place the cut 500cm×500×10cm fir block in a drying oven, and dry it at 120°C for 72 hours to remove the adsorbed water.

[0041] Step 2: Dip the dried Chinese fir pieces repeatedly in normal temperature ethanol solution and 70°C ultrapure water solution until the cleaning solution no longer has yellow turbid substances overflowing.

[0042] Step 3: Place the fir block through the degreasing treatment in the prepared 200mL sensitization solution (concentration of stannous chloride solution is 15g / L, 30% dilute hydrochloric acid 10mL / L), sensitize for 10min, and then use Rinse with deionized water for about 10 minutes.

[0043] Step 5: Place the sensitized wood in the prepared 200mL activation solution (concentration of palladium chloride solution is 0.3g / L, 30% dilute hydrochloric acid 20mL / L), activate for 10min, then use deionized water repeatedly Rinse for about 10 minutes.

[0044] Step 6: Place the activated wood in 500mL chemical plating solution (green s...

Embodiment 3

[0048] Step 1: Place the cut 200cm×200×5cm fir block in a drying oven, and dry it at 120°C for 72 hours to remove the adsorbed water.

[0049] Step 2: Put the dried Chinese fir block into a tube furnace for vacuum carbonization, the heating temperature is 600°C, the heating time is 2h, the heating rate is 5°C / min, and the protective atmosphere is argon.

[0050] Step 3: sensitization and activation are the same as in Example 2.

[0051] Step 4: Place the activated wood in 500mL chemical plating solution (green solution), configure the concentration of nickel sulfate solution to be 30g / L, the concentration of nickel chloride solution to be 60g / L, and the concentration of sodium hypophosphite solution to be 20g / L L, the concentration of sodium citrate solution is 80g / L, and the concentration of ammonium chloride solution is 40g / L. Use a dropper to take an appropriate amount of ammonia water and add it dropwise to the plating solution. The color changes from green to blue. Use a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of electromagnetic wave functional materials, and discloses a preparation process of an electromagnetic shielding material for constructing a hydrophobic coating onthe surface of a wood-based material. Related raw materials comprise wood and a chemical plating solution, the commercial wood serves as a base material, the surface of the wood has certain activity through oil removal, sensitization and activation treatment, a micron-scale nickel-phosphorus plating layer is generated on the surface of the wood in situ through chemical plating, and an existing micro-nano coarse structure is beneficial to hydrophobic performance. The method is simple in process and easily achieves large-scale preparation, wherein the wood is any one of paulownia wood, China fir, manchurian ash, sophora japonica, teak wood, rosewood, red sandalwood, lauan, oak wood, American white poplar, West African doussie, West African pear wood and beech. The magnetic wood provided by the invention has high shielding effectiveness and good heat insulation and self-cleaning performance.

Description

technical field [0001] The invention belongs to the field of electromagnetic wave functional materials, and relates to a preparation process of an electromagnetic shielding material for constructing a hydrophobic coating on the surface of a wood-based material. Background technique [0002] With the rapid development of the electronics industry, the electromagnetic radiation it brings is becoming increasingly serious, which not only affects the efficient operation of electronic equipment and communication systems, but also has harmful effects on the human body. Therefore, it is extremely important to prepare high-efficiency electromagnetic wave shielding materials. In addition, the environment in which electromagnetic shielding materials are applied is becoming more and more complex. While meeting high shielding performance, they must also have certain lightweight and self-cleaning properties. [0003] As a green material with abundant sources, easy processing, sustainable,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C18/36C23C18/28C23C18/30C23C18/20H05K9/00
CPCC23C18/36C23C18/285C23C18/30C23C18/2006H05K9/0084
Inventor 张雪峰郑芸李逸兴
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com