Water-repellent and oil-repellent anhydride-based fluorine-containing acrylate resin, preparation method and application

An acrylate and oil-repellent technology, applied in biocide-containing paints, antifouling/underwater coatings, coatings, etc., to achieve good water and oil repellency and antifouling performance, and to achieve thermal curing effects

Active Publication Date: 2022-04-15
广东聚微新材料科技有限公司
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the existing anhydride-based resins on the market are mainly general-purpose styrene-co-maleic anhydride / maleic acid ester copolymers and modified products (see CN1295085A, CN1251846A, CN104788597 A, CN106519097A), or Malay Anhydride-modified alkyd resins (CN 110484109 A), etc., rarely use long-chain alkenyl fluorine-containing monomers to polymerize non-fluorine monomers, unsaturated anhydrides and other functional monomers to prepare novel structures, water and oil repellency Anhydride-based modified fluorine-containing acrylate resin and a report on its use in the preparation of coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-repellent and oil-repellent anhydride-based fluorine-containing acrylate resin, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Synthesis of water-repellent and oil-repellent anhydride-based fluorine-containing acrylate resin MPFA-1

[0030]First, weigh 50.0g of perfluorooctyl ethyl methacrylate, 14.5g of butyl acrylate, 10.0g of vinyl phenyl ether, 25.0g of maleic anhydride, and 0.5g of acrylic acid in parts by mass, and stir to obtain A total of about 100g of the mixture is recorded as oil phase monomer A; then, weigh 3.0% by mass of A, about 3.0g of benzoyl peroxide and mix with A, and use a 100W ultrasonic cleaning machine for ultrasonic dispersion for 30 minutes , to obtain transparent liquid B; then divide B into two parts (I) and (II), of which (I) is about 33.3g, and (II) is about 66.7g.

[0031] Next, weigh 0.5 g of the molecular weight modifier mercaptoacetic acid according to A mass parts, and mix it with (II) evenly, and record the obtained mixture as (III) for future use.

[0032] In a three-necked bottle equipped with a thermometer, a condenser, and a stirrer, add 25% of the o...

Embodiment 2

[0037] (1) Synthesis of water-repellent and oil-repellent anhydride-based fluorine-containing acrylate resin MPFA-2

[0038] First, 10.0g perfluoropolyether acrylate with Mn of about 1000, 35.0g hexafluorobutyl methacrylate, 33.0g styrene, 20.0g 2-methylene succinic anhydride, 2.0g For methacrylic acid, stir and mix to obtain a total of 100g of the mixture, which is recorded as oil phase monomer A; then, weigh 2.5% and about 2.5g of AIBN according to the mass of A and mix with A, and use a 100W ultrasonic cleaning machine for ultrasonic Disperse for 30 minutes to obtain transparent liquid B; then divide B into two parts (I) and (II), of which (I) is about 30g, and (II) is about 70g.

[0039] Next, weigh 0.5 g of the molecular weight modifier mercaptoacetic acid according to A mass parts, mix with (II), and record the obtained mixture as (III) for future use.

[0040] In the three-necked bottle that device has thermometer, condenser, agitator, add 66.67% by mass parts of oil p...

Embodiment 3

[0045] (1) Synthesis of water-repellent and oil-repellent anhydride-based fluorine-containing acrylate resin MPFA-3

[0046] First, weigh 10.0g dodecafluoroheptyl methacrylate, 40.0g stearyl methacrylate, 30.0g benzyl vinyl ether, 15.0g 2-octenyl succinic anhydride, 3.5g 4- Octenoic acid, 1.0g allyl chloride, 0.5g γ-methacryloxypropyltrimethoxysilane KH-570, stir and mix to obtain a total of 100.0g mixture, which is recorded as oil phase monomer A; then, Weigh 2.0% and about 2.0g of BPO according to the mass of A, mix it with A, and use an ultrasonic cleaner with a power of 100W at 30°C for 30 minutes to obtain a transparent liquid B; then divide B into (I) and (II) Two servings, of which (I) is about 25g, and (II) is about 75g

[0047] Next, weigh 2% and about 2.0 g of molecular weight modifier dodecyl mercaptan according to A mass parts, and mix it with (II) evenly, and the resulting mixture is recorded as (III) for future use.

[0048] In a three-necked bottle equipped wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a water-repellent and oil-repellent anhydride-based fluorine-containing acrylate resin and a method for preparing a water-repellent and oil-repellent coating and a coating based on the resin. For this reason, the present invention first carries out free radical copolymerization of fluorine-containing alkenyl monomers and polymerizable non-fluorine monomers, unsaturated acid anhydrides containing double bonds in the structure, and other functional monomers in a solvent, and first synthesizes A new type of fluorine-containing acrylate resin MPFA with hydrocarbon groups, anhydride groups and other functional groups; then, the resin is used as a film material, and then the resin is ground and blended with nano-scale pigments and fillers, dispersants, etc. Under the action of epoxy compound or polyamino compound curing agent, cross-linking heat curing not only produces a resin coating with flexibility, impact resistance and good water repellency, but also the anti-fouling level of the coating can reach 0‑2.

Description

technical field [0001] The invention belongs to the field of functional resin coatings, and in particular relates to a preparation method of anhydride-based fluorine-containing acrylate resin and its application in coatings and coatings. Background technique [0002] Fluorine-containing acrylate resin, low surface energy, excellent water and oil repellency, used in the treatment of glass, metal or fiber substrates, etc., can not only improve the surface properties of the substrate, but also endow the substrate with ideal water and oil repellency and Antifouling performance, so it is widely used in the field of functional coatings and coatings. [0003] Copolymerize fluorine-containing acrylate or fluorine-containing alkenyl compound with aliphatic acrylate, functional monomer, etc., to synthesize organic fluorine resin with excellent water and oil repellency, which can be found in patent documents CN102443099, CN101538342, CN101759835, CN1166709, CN1315886 and so on. Howev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/24C08F216/16C08F220/18C08F222/06C08F220/06C09D133/16C09D7/61C08F283/06C08F212/08C08F222/04C09D133/10C09D151/08C08F220/04C08F230/08C08F214/14C08F212/14C08F210/14C09D5/16
CPCC08F220/24C09D133/16C08F283/065C09D151/08C09D143/04C08F220/1812C08F220/1818C09D5/1662C09D5/1687C08K2201/011C08K2003/2241C08F220/1804C08F216/165C08F222/06C08F220/06C08K3/22C08F212/08C08F222/04C08F220/04C08F230/085C08F214/14C08F220/1806C08F212/18C08F210/14
Inventor 安秋凤焦岚姣陈雅葛萍黄良仙薛朝华
Owner 广东聚微新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap