Method for continuously preparing 3, 3, 3-trifluoro-2-(trifluoromethyl)-1-propylene in gas phase

A technology of trifluoromethyl and fluoromethyl, which is applied in the field of continuous preparation of 3,3,3-trifluoro-2--1-propene in the gas phase, which can solve the problem of low single-pass yield, low yield, high single-pass yield, etc. question

Active Publication Date: 2021-05-14
泉州宇极新材料科技有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are following problems in this route: the temperature of second step reaction is too high, can produce a large amount of waste solid metal fluorides, and the productive rate of product is lower
This route has the following disadvantages: (1) raw materials are difficult to obtain; (2) a large amount of waste ammonium salts will be produced
This route has the following problems: (1) the liquid phase process is adopted, and a large amount of solvent is used, which will generate a large amount of waste liquid and waste solid, which seriously pollutes the environment; (2) raw materials are difficult to obtain
This route has the following problems: (1) raw materials are difficult to obtain; (2) the second step reaction uses a large amount of KOH as a dehydrochlorination reagent, which will produce a large amount of waste solids, and the intermediate 3-chloro-3,3-difluoro-2- The yield of trifluoromethyl-1 propene is too low, resulting in too low single-pass yield of the whole route for the synthesis of 3,3,3-trifluoro-2-(trifluoromethyl)-1-propene
This route has the following problems: (1) the total yield is too low; (2) the gas phase continuous method has certain industrial value, but the effective metering of sulfur is a technical challenge, and it is easy to block the pipeline, so the pipeline and measuring instruments Insulation is important
This route has the following problems: (1) raw materials are difficult to obtain, and the yield is low; (2) SF 4 is a highly toxic substance
This route has the following defects: (1) The second and fourth steps use a large amount of solvent and a large amount of solid strong base, which will produce a large amount of liquid waste and solid waste, which seriously pollutes the environment; (2) The first and third steps The hydrogenation reaction is a batch process, and the yield of the product is low
[0024] So far, there is no 3,3,3-trifluoro-2-(trifluoromethyl)-1-propene in the open literature that satisfies the characteristics of easy availability of raw materials, high yield per pass, and easy realization of continuous gas phase production. synthetic route

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for continuously preparing 3, 3, 3-trifluoro-2-(trifluoromethyl)-1-propylene in gas phase
  • Method for continuously preparing 3, 3, 3-trifluoro-2-(trifluoromethyl)-1-propylene in gas phase
  • Method for continuously preparing 3, 3, 3-trifluoro-2-(trifluoromethyl)-1-propylene in gas phase

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0061] 1. Preparation of hydrogenation catalyst:

[0062] (1) Preparation of the carrier of the hydrogenation catalyst: Dissolve aluminum trichloride in water, add concentrated ammonia water dropwise for precipitation, adjust the pH value to 7.5, then age for 24 hours, wash with water, filter, and dry in an oven at 120°C for 15 hour, the gained solid is pulverized, pressed into tablets, and the precursor of the carrier is obtained, and the precursor 10mL of the carrier is packed into a tubular reactor with an internal diameter of 1 / 2 inch and a length of 30cm. ℃ roasting for 12 hours, nitrogen space velocity is 200h -1 , and then cooled to 300 °C, and at the same time, a mixed gas composed of hydrogen fluoride and nitrogen with a mass ratio of 1:2 was introduced, and the total air velocity of the gas was 220h. -1 , activated for 12 hours, stop the above gas mixture, and produce aluminum fluoride.

[0063] Other supports can be prepared by substituting other soluble metal sal...

Embodiment 1

[0070] 2%Pd / 98%AlF is filled in a tubular reactor made of Incon alloy with an inner diameter of 1 / 2 inch and a length of 30cm 3 Catalyst 10mL. The reaction conditions are as follows: the reaction temperature is 50°C, the mass ratio of octafluoroisobutene to hydrogen is 1:10, the contact time is 60s, and the reaction pressure is 0.1MPa. After running for 10 hours, the reaction product was washed with water, washed with alkali and dried, and the gas phase organic phase was taken for GC analysis. The reaction results are: the conversion rate of octafluoroisobutene is 73.4%, and the selectivity of 1,1,1,3,3,3-hexafluoro-2-(difluoromethyl)propane is 99.8%.

Embodiment 2

[0072] 2%Pd / 98%AlF is filled in a tubular reactor made of Incon alloy with an inner diameter of 1 / 2 inch and a length of 30cm 3 Catalyst 10mL. The reaction conditions are as follows: the reaction temperature is 100°C, the mass ratio of octafluoroisobutene to hydrogen is 1:10, the contact time is 60s, and the reaction pressure is 0.1MPa. After running for 10 hours, the reaction product was washed with water, washed with alkali and dried, and the gas phase organic phase was taken for GC analysis. The reaction results are: the conversion rate of octafluoroisobutene is 93.8%, and the selectivity of 1,1,1,3,3,3-hexafluoro-2-(difluoromethyl)propane is 99.6%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
boiling pointaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for continuously preparing 3, 3, 3-trifluoro-2-(trifluoromethyl)-1-propylene in a gas phase, and the method comprises the following steps: by taking octafluoroisobutylene as a raw material, carrying out hydrogenation-dehydrofluorination-hydrogenation-dehydrofluorination four-step gas phase continuous reaction to obtain the 3, 3, 3-trifluoro-2-(trifluoromethyl)-1-propylene. The hydrogenation catalyst and the dehydrofluorination catalyst have the characteristics of high activity and long service life; according to the present invention, by using the gas phase independent circulation process, the incomplete reaction material is subjected to independent circulation so as to completely convert the initial raw material into the 3, 3, 3-trifluoro-2-(trifluoromethyl)-1-propylene, and finally the product 3, 3, 3-trifluoro-2-(trifluoromethyl)-1-propylene is efficiently and continuously and circularly extracted from the process system in the gas phase; therefore, liquid waste and waste gas are not generated, and green production is realized.

Description

technical field [0001] The invention relates to a method for continuously preparing 3,3,3-trifluoro-2-(trifluoromethyl)-1-propene in a gas phase, in particular to a method for taking octafluoroisobutene as a starting material, which is subjected to gas phase hydrogenation, gas phase A method for synthesizing 3,3,3-trifluoro-2-(trifluoromethyl)-1-propene by four steps of dehydrofluorination, gas-phase hydrogenation, and gas-phase dehydrofluorination. Background technique [0002] At present, the existing synthetic routes of 3,3,3-trifluoro-2-(trifluoromethyl)-1-propene mainly include the following seven kinds: [0003] Route 1: Starting from hexafluoropropylene and difluoromethane [0004] [0005] The literature "Journal of Fluorine Chemistry 108 (2001) 15-20" and patent EP1175380 reported the synthesis of 3,3,3-trifluoro- The technical route of 2-(trifluoromethyl)-1-propene: (1) The first step reaction: under the action of antimony pentafluoride, react hexafluoropropen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07C17/25C07C21/18C07C17/354C07C19/08
CPCC07C17/25C07C17/354C07C21/18C07C19/08
Inventor 张呈平贾晓卿董利权恒道
Owner 泉州宇极新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com