Method for improving brazing strength of tungsten-copper part

A technology of brazing and parts, which is applied in the direction of explosion generating devices, abrasives, manufacturing tools, etc., can solve the problems that the brazing rate is difficult to exceed 80%, the surface quality of materials is poor, and the wettability is not good, so as to avoid welding defects, Increased welding area and high productivity

Active Publication Date: 2021-06-18
SHAANXI SIRUI ADVANCED MATERIALS CO LTD
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, since tungsten-copper material is a kind of porous structure composite material, which is infiltrated by copper into the tungsten skeleton, the processing technology of this material is easy to bring about the porous characteristics of the material surface, and the tungsten-copper material itself has poor wettability to solder. , and with the increase of tungsten content in tungsten-copper alloy, the wettability is lower, and the surface quality of the material obtained by ordinary metallurgical methods is also worse.
Therefore, during the brazing process of tungsten copper alloy with stainless steel or Kovar alloy, pores are prone to appear, and the brazing rate is difficult to exceed 80%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving brazing strength of tungsten-copper part
  • Method for improving brazing strength of tungsten-copper part
  • Method for improving brazing strength of tungsten-copper part

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A method for improving the brazing strength of tungsten-copper parts, comprising the following steps:

[0033] S1 pressed tungsten billet: press 100g tungsten powder into 10g / cm 3 tungsten billet;

[0034] S2 Forming: Put the pressed tungsten billet into the graphite crucible, put the copper block that needs to be infiltrated on the tungsten billet, the mass of the copper block is 50g, lay a layer of corundum powder in the graphite crucible in advance, and then use 160-220 mesh The corundum powder is buried and compacted, and the thickness of the corundum powder covered on the top and bottom of the tungsten billet is 2cm. The thickness of the corundum powder covered by the tungsten billet from the front and rear edges of the graphite crucible and the left and right edges is the same, and the thickness is 2cm. The pre-sintered part, the corundum powder It is white corundum, and the mass of corundum powder is 8 times that of tungsten billet;

[0035] S3 sintering: put t...

Embodiment 2

[0039] This embodiment is basically the same as Embodiment 1, except that the density of the tungsten billet is different, so the quality of copper that can penetrate into the tungsten billet is different, and the quality of the copper added under the same quality tungsten billet is also different. At the same time, the amount of corundum powder added also changed.

[0040] S1 pressed tungsten billet: press 100g tungsten powder into 13g / cm 3 tungsten billet;

[0041] S2 Forming: Put the pressed tungsten billet into the graphite crucible, put the copper block that needs to be infiltrated on the tungsten billet, the mass of the copper block is 30g, lay a layer of corundum powder in the graphite crucible in advance, and then use 220-260 mesh The corundum powder is buried and compacted, and the thickness of the corundum powder covered on the top and bottom of the tungsten billet is 3cm. The thickness of the corundum powder covering the tungsten billet from the front and rear edge...

Embodiment 3

[0046] This embodiment is basically the same as Embodiment 1, except that the density of the tungsten billet is different, so the quality of copper that can penetrate into the tungsten billet is different, and the quality of the copper added under the same quality tungsten billet is also different. At the same time, the amount of corundum powder added also changed.

[0047] S1 pressed tungsten billet: press 100g tungsten powder into 15g / cm 3 tungsten billet;

[0048] S2 Forming: Put the pressed tungsten billet into the graphite crucible, put the copper block that needs to be infiltrated on the tungsten billet, the mass of the copper block is 15g, lay a layer of corundum powder in the graphite crucible in advance, and then use 260-320 mesh The corundum powder is buried and compacted, and the thickness of the corundum powder covered on the top and bottom of the tungsten billet is 4cm. The thickness of the corundum powder covering the tungsten billet from the front and rear edges ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for improving the brazing strength of a tungsten-copper part. The method comprises the following steps of S1, pressing of a tungsten blank; S2, forming, wherein the pressed tungsten blank is placed in a graphite crucible, a copper block needing infiltration is placed on the tungsten blank, then emery powder is adopted for filling and is tamped, and a pre-sintered part is obtained; S3, sintering, wherein the formed pre-sintered part is put into an atmosphere protection molybdenum wire furnace to be sintered at a high temperature, and a tungsten-copper alloy is obtained; S4, sand blasting, wherein after the sintered tungsten-copper alloy is discharged out of the furnace, sand blasting is carried out to remove the emery powder on the surface, and a copper-clad layer of 0.01-0.1 mm is naturally formed on the surface of the tungsten-copper alloy; and S5, vacuum brazing, wherein vacuum brazing is conducted on the tungsten-copper alloy obtained after sand blasting and stainless steel or a Kovar alloy. According to the method, the ultrathin copper-clad layer of 0.01-0.1 mm is infiltrated on the surface of the tungsten blank, the welding strength between the tungsten-copper alloy and the stainless steel or the Kovar alloy is effectively improved, the brazed rate is increased, and the welding defect caused by non-infiltration of a tungsten-copper material is effectively avoided.

Description

technical field [0001] The invention relates to the technical field of tungsten-copper alloy brazing, in particular to a method for improving the brazing strength of tungsten-copper parts. Background technique [0002] Tungsten has a high melting point, low coefficient of linear expansion and high strength, while copper has good electrical and thermal conductivity. Therefore, tungsten-copper composite materials combine many excellent properties of tungsten and copper, so they have good thermal conductivity, arc corrosion resistance, It has the characteristics of anti-welding resistance, high temperature resistance and anti-oxidation, and has been widely used in electric power, electronics, machinery, metallurgy and other industries. [0003] In the 1990s, with the development of large-scale integrated circuits and high-power electronic devices, tungsten copper materials began to be used as electronic packaging and heat sink materials on a large scale as an upgraded product. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00B24C1/08B24C11/00B24C5/02C22C1/04C22C27/04B22F3/10B22F3/26
CPCB22F3/1035B22F3/26B23P15/00B24C1/08B24C5/02B24C11/00C22C1/045C22C27/04
Inventor 周宁周兴杨瑞刘向阳邵红颜刘萍王万刚
Owner SHAANXI SIRUI ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com