Unlock instant, AI-driven research and patent intelligence for your innovation.

Wastewater treatment agent ands preparation method and application thereof

A technology of wastewater treatment agent and flocculant, which is applied in the direction of processing wastewater treatment, water/sewage treatment, adsorption water/sewage treatment, etc. It can solve the problems of wastewater treatment difficulty, increase treatment cost, high content of suspended solids, etc., and achieve purification effect Prominent, stable structure, enhanced flocculation effect

Active Publication Date: 2021-06-25
珠海市建滔环保科技有限公司 +1
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the treatment agents need to adjust the pH value of the wastewater to near the neutral value before putting them in, otherwise the effect will not be good
Adding acid and alkali will inevitably increase new pollution and increase treatment costs
At the same time, the high content of suspended solids in papermaking wastewater brings great difficulty to wastewater treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wastewater treatment agent ands preparation method and application thereof
  • Wastewater treatment agent ands preparation method and application thereof
  • Wastewater treatment agent ands preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A wastewater treatment agent consisting of the following components:

[0041]

[0042]

[0043] The macroporous resin model is YKHCN-2 (purchased from Tianjin Yunkai Resin Technology Co., Ltd.), with a diameter of 0.3-1.25mm, and the iron ion flocculant is polyferric sulfate.

[0044] A preparation method for waste water treatment agent, comprising the following steps:

[0045] (1) Weigh 50g graphene and 500g diatomite, stir for 3h at a stirring rate of 250 rpm to make it fully mixed; then roast at a temperature of 650°C for 3h, after cooling, carry out crushing treatment, and then Grinding and passing through an 80-mesh sieve to obtain graphene-modified diatomite;

[0046] (2) Then disperse 80g of polyacrylamide in water, add the graphene-modified diatomite prepared in step (1), stir for 3h at a stirring rate of 300 rpm, make it fully mixed; then let it stand 5h, dried at 60°C for 3 hours to obtain modified diatomite.

[0047] (3) Take 200g modified diatomite,...

Embodiment 2

[0049] A wastewater treatment agent consisting of the following components:

[0050]

[0051] The type of macroporous resin is YKHCN-2, the diameter is 0.3-1.25mm, and the iron ion flocculant is polysilicate ferric chloride.

[0052] A preparation method for waste water treatment agent, comprising the following steps:

[0053] (1) Weigh 50g of graphene and 500g of diatomite, stir for 3h at a stirring rate of 250 rpm to make it fully mixed; then roast at a temperature of 650°C for 3h, and carry out crushing after cooling, and then Grinding and passing through an 80-mesh sieve to obtain graphene-modified diatomite;

[0054] (2) Then disperse 80g of polyacrylamide in water, add the graphene-modified diatomite prepared in step (1), stir for 3h at a stirring rate of 300 rpm, make it fully mixed; then stand 5h, dried at 60°C for 3 hours to obtain modified diatomite.

[0055] (3) Get 280g of modified diatomite, 60g of nano-zinc oxide, 60g of nano-silicon oxide, stir for 2h at a s...

Embodiment 3

[0057] A wastewater treatment agent consisting of the following components:

[0058]

[0059] The type of macroporous resin is YKHCN-2, the diameter is 0.3-1.25mm, and the iron ion flocculant is polyferric sulfate.

[0060] A preparation method for waste water treatment agent, comprising the following steps:

[0061] (1) Weigh 50g of graphene and 500g of diatomite, stir for 3h at a stirring rate of 250 rpm to make it fully mixed; then roast at a temperature of 650°C for 3h, and carry out crushing after cooling, and then Grinding and passing through an 80-mesh sieve to obtain graphene-modified diatomite;

[0062] (2) Then disperse 80g of polyacrylamide in water, add the graphene-modified diatomite prepared in step (1), stir for 3h at a stirring rate of 300 rpm, make it fully mixed; then stand 5h, dried at 60°C for 3 hours to obtain modified diatomite.

[0063] (3) Get 350g of modified diatomite, 60g of nano-zinc oxide, 40g of nano-silicon oxide, stir for 2h at a stirring ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of wastewater treatment, and discloses a wastewater treatment agent and a preparation method and application thereof. The wastewater treatment agent comprises modified diatomite, an iron ion flocculant, a nano oxide and macroporous resin; the modified diatomite is prepared by modifying graphene and polyacrylamide together; the nano oxide comprises nano silicon oxide and nano zinc oxide. The diatomite is jointly modified by graphene and polyacrylamide, so that the modified diatomite is more stable in structure, is not influenced by acid-base property and is high in adsorption capacity. The modified diatomite is compounded with the iron ion flocculant and the macroporous resin, so that the flocculation and adsorption effects are enhanced, and the treatment agent has a good treatment effect and particularly has an outstanding purification effect on suspended solids in wastewater.

Description

technical field [0001] The invention belongs to the technical field of wastewater treatment, and in particular relates to a wastewater treatment agent and its preparation method and application. Background technique [0002] The papermaking process includes key steps such as pulping, modulation, papermaking, and cutting. A large amount of waste liquid will be produced in papermaking, especially in the pulping process, including pulping cooking waste liquid, washing waste water, bleaching waste water and paper machine white water. Papermaking waste liquid has complex components and poor biodegradability, mainly including the following pollutants: (1) settleable suspended matter and non-settled suspended matter, mainly fibers and fiber fines; (2) easily biodegradable organic matter, such as hemicellulose, Methanol, acetic acid, formic acid, sugars, etc.; (3) Refractory organic matter: lignin and macromolecular carbohydrates contained in fiber raw materials; (4) Toxic substanc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/52C02F1/56C02F1/28C02F103/28C02F101/30
CPCC02F1/288C02F1/5236C02F1/56C02F2101/30C02F2103/28
Inventor 孔庆健余劲梁海涛周堃贺鹏辉
Owner 珠海市建滔环保科技有限公司