Modified sulfydryl-containing liquid silicone resin, non-toxic, colorless and odorless light-cured liquid silicone rubber and preparation method and application thereof
A liquid silicon and light-curing technology, which is applied in the field of non-toxic and tasteless light-curing silicone materials, can solve the problems of bad smell and high toxicity, and achieve the effects of moderate viscosity, fast curing speed and high application value
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0046] Provides a method for preparing a photocurable liquid silicone rubber solution is prepolymerized in some specific aspect of the invention, the following production method comprising:
[0047] S1-1) Preparation of the vinyl-modified silica
[0048]
[0049] Vinyl-modified silica was prepared as shown in formula (1).
[0050] Take silica dissolved in a vessel containing solvent, after ultrasonic dispersion, was added vinyl dimethylchlorosilane and trimethylchlorosilane composition under heating, after completion of the reaction was dried under reduced pressure to give a vinyl surface modified silica powder.
[0051] Wherein the solvent is n-hexane, cyclohexane, ethyl acetate, butyl acetate, a mixture of one or more of toluene; preferably, the solvent is n-hexane and ethyl acetate, the mixing volume ratio of 1: 1 .
[0052] Preferably, the silica is a fumed silica, precipitated silica, airgel of one or a mixture of two or more; when used in combination, the mixing ratio is n...
Example Embodiment
[0074] Example 1
[0075] Liquid silicone and the corresponding mercapto containing a modified non-toxic, colorless and odorless photo-curable liquid silicone rubber, were prepared by the following methods:
[0076] Preparing a liquid silicone-modified thiol group-S1)
[0077] Preparation of the vinyl-modified silica S1-1)
[0078] Take 5.0g 0.4g of fumed silica with trimethylsilyl chloride and vinyl dimethylchlorosilane 0.1g was added to 50g compositions of hexane and ethyl acetate 1: 1 mixed solvent, after ultrasonic dispersion 10min, at 40 ℃ for 4h, after suction and dried in vacuo to give the modified silica powder.
[0079] S1-2) Preparation of mercapto group-containing liquid silicone modified
[0080] 8g taken mercaptopropyl trimethoxysilane, 2g mercaptopropyl methyl dimethoxy silane, 8g dimethyl dimethoxysilane, 2g trimethoxysilane, 4.0g of ultrapure water, 20g hexamethyldisilazane after ether (MM), 0.1g of concentrated hydrochloric acid the reaction was stirred at 50 ℃, s...
Example Embodiment
[0084] Example 2
[0085] Liquid silicone and the corresponding mercapto containing a modified non-toxic, colorless and odorless photo-curable liquid silicone rubber, were prepared by the following methods:
[0086] Preparing a liquid silicone-modified thiol group-S1)
[0087]S1-1) Preparation of vinyl modified white carbon black
[0088] 5.0 g of gas-phase white carbon black and 0.4 g of trimethyl chloride and 0.1 g of vinyl dimethylcmesilane composition were added to 1: 1 mixed solvent of 50 g of n-hexane and ethyl acetate, ultrasonic dispersion 10min, at 50 The reaction was reacted at ° C for 3 h, and the modified white carbon black powder was obtained after evacuation.
[0089] S1-2) Preparation of modified mercapto-based liquid silicone resin
[0090] Take 6.0 g of mercaptopyltrimethoxysilane, 4.0 g of mercaptomethyl dimethoxysilane, 5.0 g of dimethyl dimethoxysilane, 5.0 g of trimethoxysilane, 5.0 g of ultra-pure water, 30g six Methyl silica ether (mm), 0.05 g of concentrate...
PUM
Property | Measurement | Unit |
---|---|---|
Specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap