Recycled concrete aggregate reinforced by using construction waste micro powder and preparation method of recycled concrete aggregate

A technology for recycling concrete and construction waste, applied in the field of building materials, can solve the problems of unsatisfactory application effect of recycled aggregates, limiting the utilization rate of building materials resources, and being difficult to degrade at will, so as to promote resource utilization and promote processing problems. , the effect of low cost

Pending Publication Date: 2021-11-16
SUN YAT SEN UNIV +1
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The site selection of construction waste dumps is largely random and difficult to degrade, and the dust generated during the removal and stacking of construction waste has caused environmental pollution.
At present, the comprehensive utilization rate of construction waste resources in my country is less than 10%, mainly concentrated in recycled concrete aggregates, and construction waste micropowder is a problem that cannot be ignored in the recycling of waste concrete, accounting for about 5%-20% of the total waste concrete. Its main mineral components are silica, calcium hydroxide, ettringite and calcium aluminosilicate, etc. These components have potential activation properties, and at the same time, a large amount of carbon dioxide waste gas is produced in the cement industry production
These factors lead to the unsatisfactory application effect of recycled aggregate in concrete, which limits the utilization rate of its building material resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The present invention also provides a method for preparing recycled concrete aggregate reinforced with construction waste micropowder, said method comprising the following steps:

[0030] S1 Stir the recycled aggregates in a horizontal mixer to remove loose mortar particles and some dust impurities on the surface of the recycled aggregates. After taking them out, sieve the dust and impurities to obtain spare recycled concrete aggregates;

[0031] S2 Stir the construction waste micropowder, cement, water reducing agent and water evenly in a certain proportion to prepare a strengthened slurry with a water-binder ratio of 0.35 and a slurry-bone ratio of 0.5;

[0032] S3 Put the recycled concrete aggregate pretreated in step S1 into the reinforced slurry prepared in step S2 and stir evenly in a horizontal mixer, take out the drained slurry and air-dry the surface of the aggregate naturally, and make a reinforced slurry on the surface of the recycled concrete aggregate wrapp...

Embodiment 1

[0075] The present embodiment comprises the following steps:

[0076] (1) Stir the raw materials of the recycled concrete aggregate in a horizontal mixer, remove the loose mortar particles and some dust impurities on the surface of the recycled concrete aggregate, remove the dust and impurities after taking them out, and obtain the spare recycled concrete aggregate;

[0077] (2) Add 5.037kg of cementitious material (0.504kg of construction waste micropowder and 4.533kg of cement) and 18g of water reducer to 1.763kg of water and stir evenly to prepare a reinforced slurry;

[0078] (3) Put 13.6 kg of spare recycled concrete aggregate into the reinforced slurry and stir evenly in the mixer, take out the drained slurry and air-dry the surface of the aggregate naturally, and make a reinforced slurry coating on the surface of the recycled concrete aggregate (mass fraction approx. 5%);

[0079] (4) Put the recycled concrete aggregate wrapped in the strengthening slurry into the carb...

Embodiment 2

[0081] The present embodiment comprises the following steps:

[0082] (1) Stir the raw materials of the recycled concrete aggregate in a horizontal mixer, remove the loose mortar particles and some dust impurities on the surface of the recycled concrete aggregate, remove the dust and impurities after taking them out, and obtain the spare recycled concrete aggregate;

[0083] (2) Add 5.037kg of cementitious material (1.007kg of construction waste micropowder and 4.03kg of cement) and 18g of water reducer to 1.763kg of water and stir evenly to prepare a reinforced slurry;

[0084] (3) Put 13.6 kg of spare recycled concrete aggregate into the reinforced slurry and stir evenly in the mixer, take out the drained slurry and air-dry the surface of the aggregate naturally, and make a reinforced slurry coating on the surface of the recycled concrete aggregate (mass fraction approx. 6%);

[0085] (4) Put the recycled concrete aggregate wrapped in the strengthening slurry into the carbo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a recycled concrete aggregate reinforced by using construction waste micro-powder, the recycled concrete aggregate is composed of a matrix, a modified wrapping layer and a surface reinforced layer, the matrix is a recycled aggregate, the modified wrapping layer is reinforced slurry, and the surface reinforced layer is carbide; wherein the recycled aggregate accounts for 80%-95% by mass, the reinforced slurry accounts for 4%-15% by mass, and the carbide accounts for 1%-5% by mass. The invention also provides a preparation method of the recycled concrete aggregate. According to the method, the raw materials are easy to obtain, the waste concrete aggregate and the micro powder thereof are utilized to the maximum extent, waste utilization and environmental protection are achieved, the cost is low, the technological process is simple, engineering practice application is facilitated, and the prepared modified recycled concrete aggregate is excellent in physical and mechanical property and wide in application prospect.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a recycled concrete aggregate strengthened by construction waste micropowder and a preparation method thereof. Background technique [0002] With the acceleration of my country's urbanization process, the annual production of construction waste in the country can reach 2 billion tons, with an average annual growth rate of 10%. The amount of construction waste in my country has accounted for 30-40% of the total urban waste. The site selection of construction waste dumps is largely random and difficult to degrade, and the dust generated during the removal and stacking of construction waste has caused environmental pollution. At present, the comprehensive utilization rate of construction waste resources in my country is less than 10%, mainly concentrated in recycled concrete aggregates, and construction waste micropowder is a problem that cannot be ignored in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B20/12C04B20/10C04B18/16C04B28/04
CPCC04B20/12C04B20/1077C04B18/16C04B28/04C04B2111/00017C04B2103/302C04B20/1055C04B20/1018Y02W30/91
Inventor 赵计辉李忠丁晓平王葆霞丁继鹏
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products