A frosted glass and production process technology, applied in glass manufacturing equipment, manufacturing tools, glass furnace equipment and other directions, can solve the problems of reducing the self-cutting effect of glass size, improper effect of time and infiltration, and increasing the success rate of frosted glass. , to achieve the effect of improving processing effect, fast heating speed and improving yield

Pending Publication Date: 2021-12-17
DONGGUAN YINTAIFENG OPTICAL TECH CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a frosted glass manufacturing process, which has the advantages of self-adjusting the size of the cut glass according to the needs, and also improves the success rate of the pickling process of the plate body, and solves the problems in the traditional situation. Frosted glass is generally used in pickling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Embodiment one:

[0025] A manufacturing process of frosted glass, comprising the following steps:

[0026] 1) Put the raw materials in the above ratio, including quartz sand, feldspar, barite, manganese powder, calcium oxide and glass fiber, into the inside of the mill and grind them into powder. The circulating air of the internal blower is brought into the inside of the pulverizer for secondary sorting, and the materials that are too fine will fall back for regrinding. It is necessary to ensure that the grinding diameter of each raw material is less than or equal to 500 mesh, and then the glass that has been sieved Raw materials are taken out;

[0027] 2) Place the mixed and polished glass raw materials in a furnace filled with nitrogen, raise the temperature of the furnace to about 1300°C-1400°C, and then raise the temperature of the furnace to 1460°C-1560°C again to ensure The mixed glass raw materials can be fully heated and melted, and the inside of the furnace...

Example Embodiment

[0032] Embodiment two:

[0033] A manufacturing process of frosted glass, comprising the following steps:

[0034] 1) Put the raw materials in the above ratio, including quartz sand, feldspar, barite, manganese powder, calcium oxide and glass fiber, into the inside of the mill and grind them into powder. The circulating air of the internal blower is brought into the inside of the pulverizer for secondary sorting, and the materials that are too fine will fall back for regrinding. It is necessary to ensure that the grinding diameter of each raw material is less than or equal to 600 mesh, and then the glass that has been sieved Raw materials are taken out;

[0035] 2) Place the mixed and polished glass raw materials in a furnace filled with nitrogen, raise the temperature of the furnace to about 1350°C-1450°C, and then raise the temperature of the furnace to 1460°C-1560°C again to ensure The mixed glass raw materials can be fully heated and melted, and the inside of the melting...

Example Embodiment

[0040] Embodiment three:

[0041] A manufacturing process of frosted glass, comprising the following steps:

[0042] 1) Put the raw materials in the above ratio, including quartz sand, feldspar, barite, manganese powder, calcium oxide and glass fiber, into the inside of the mill and grind them into powder. The circulating air of the internal blower is brought into the inside of the pulverizer for secondary sorting, and the materials that are too fine will fall back for regrinding. It is necessary to ensure that the grinding diameter of each raw material is less than or equal to 700 mesh, and then the glass that has been sieved Raw materials are taken out;

[0043] 2) Place the mixed and polished glass raw materials in a melting furnace filled with nitrogen, raise the temperature of the melting furnace to about 1400°C-1500°C, and then raise the temperature of the melting cellar to 1460°C-1560°C again to ensure The mixed glass raw materials can be fully heated and melted, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of glass manufacturing, and discloses a manufacturing process of frosted glass, which is prepared from the following raw materials in parts by weight: 40 to 50 parts of quartz sand, 30 to 40 parts of feldspar, 26 to 30 parts of barite, 8 to 12 parts of manganese powder, 6 to 8 parts of calcium oxide, 5 to 10 parts of glass fiber, 3 to 6 parts of clarifying agent, 2 to 4 parts of mirabilite and 1 to 2 parts of coloring agent. According to the manufacturing process of the frosted glass, in the manufacturing process of the glass, various different raw materials are mixed and fully ground into fine powder, so that bubbles in a product can be well reduced when the raw materials are heated to a molten state, mixing is more uniform, the heating speed is higher, and the effect of improving the glass processing rate is achieved; meanwhile, the manufacturing process can also uniformly spread the glass solution on the surface of the tin liquid, so that the glass can be helped to be cooled and formed more quickly.

Description

technical field [0001] The invention relates to the technical field of glass production, in particular to a production process of frosted glass. Background technique [0002] Glass is an amorphous inorganic non-metallic material, generally made of various inorganic minerals (such as quartz sand, borax, boric acid, barite, barium carbonate, limestone, feldspar, soda ash, etc.) of. Its main components are silicon dioxide and other oxides. The chemical composition of ordinary glass is Na2SiO3, CaSiO3, SiO2 or Na2O·CaO·6SiO2, etc. The main component is silicate double salt, which is an amorphous solid with an irregular structure. It is widely used in buildings to prevent wind. Translucent, belongs to the mixture. There are also colored glass that is mixed with certain metal oxides or salts to show color, and tempered glass made by physical or chemical methods. Sometimes some transparent plastics (such as polymethyl methacrylate) are also called plexiglass. [0003] However,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C15/00C03B1/00C03B5/16C03B18/02C03C17/32
CPCC03C15/00C03B1/00C03B5/16C03B18/02C03C17/32
Inventor 李锦亮文妙清魏先钊汤占刚王本初
Owner DONGGUAN YINTAIFENG OPTICAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap