A kind of thermal insulation coating and preparation method thereof

A thermal insulation and coating technology, which is applied in the direction of anti-corrosion coatings, fireproof coatings, coatings, etc., can solve the problems of poor adhesion between thermal insulation coatings and coke oven bodies, and achieve low thermal conductivity, strong adhesion, excellent The effect of thermal insulation performance

Active Publication Date: 2022-04-12
江苏龙冶节能科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The problem solved by the invention is that the existing thermal insulation paint has poor adhesion to the coke oven body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of thermal insulation coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0044] Another object of the present invention is to provide a method for preparing the above-mentioned thermal insulation coating, the preparation method comprising the following steps:

[0045] S1: preparing an organosilicon modification solution;

[0046] S2: preparing nano hollow microbeads;

[0047] S3: preparing fumed silica gel;

[0048] S4: According to parts by weight, add 25-35 parts of nano-hollow microbeads to 15-20 parts of organosilicon modification solution, and mix uniformly to obtain solution A;

[0049] S5: In terms of parts by weight, add 10 to 20 parts of nano silicate inorganic binder, 10 to 15 parts of fumed silica gel, 5 to 15 parts of inorganic hollow fiber powder, 2 -8 parts of nano-rare earth oxide, 1-5 parts of additives, and 0.5 parts of water are uniformly mixed to obtain a thermal insulation coating.

[0050] For the thermal insulation coating provided by this application, firstly, the prepared nano hollow microspheres are fully mixed with the ...

Embodiment 1

[0067] This embodiment provides a method for preparing a thermal insulation coating, comprising the following steps:

[0068] S1: In parts by weight, 1.5 parts of methyl monomer and 1 part of tetrafluoroethylene monomer were polymerized at 85° C. to obtain a silicone modified solution;

[0069] S21: According to parts by weight, mix 1 part of BN-1000 stabilizer with 5 parts of ethanol to obtain solution B;

[0070] S22: According to parts by weight, 15 parts of nano-ceramic hollow microspheres are added to solution B, and mixed uniformly to obtain solution C;

[0071] S23: Add 1 part of neodymium nitrate and 5 parts of nickel nitrate to the solution C in parts by weight, heat to 30° C., and mix uniformly to obtain a dispersed liquid;

[0072] S24: After filtering, cleaning and drying the dispersed liquid in sequence, sintering at 600° C. for 5 hours to obtain nano hollow microspheres; the nano hollow microspheres are nano hollow microspheres coated with neodymium nitrate and ...

Embodiment 2

[0081] This embodiment provides a method for preparing a thermal insulation coating, comprising the following steps:

[0082] S1: In parts by weight, 1.5 parts of methyl monomer and 1 part of tetrafluoroethylene monomer were polymerized at 85° C. to obtain a silicone modified solution;

[0083] S21: According to parts by weight, mix 5 parts of BN-1000 stabilizer with 1 part of ethanol to obtain solution B;

[0084] S22: According to parts by weight, 25 parts of nano-ceramic hollow microspheres are added into solution B, and mixed evenly to obtain solution C;

[0085] S23: Add 5 parts of neodymium nitrate and 1 part of nickel nitrate to the solution C in parts by weight, heat to 35° C., and mix uniformly to obtain a dispersed liquid;

[0086] S24: After filtering, washing and drying the dispersed liquid in sequence, sintering at 900° C. for 3 hours to obtain nano hollow microspheres; the nano hollow microspheres are nano hollow microspheres coated with neodymium nitrate and ni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a thermal insulation coating and a preparation method thereof. The thermal insulation coating comprises 10 to 20 parts of nano silicate inorganic binder and 15 to 20 parts of organosilicon modified Solution, 10-15 parts of fumed silica gel, 25-35 parts of nano hollow microspheres, 5-15 parts of inorganic hollow fiber powder, 2-8 parts of nano-rare earth oxide, 1-5 parts of auxiliary agent, 0.5 parts of water. The thermal insulation coating provided by the present invention, through the synergistic effect of the organosilicon modification solution and other components, makes the thermal insulation coating have excellent thermal insulation performance, and also has low thermal conductivity, corrosion resistance, impact resistance, and fire prevention. It has the advantages of waterproof, simple construction, and strong adhesion to the coke oven body.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a thermal insulation coating and a preparation method thereof. Background technique [0002] Coke oven is a complex industrial furnace with huge energy consumption. The heat utilization efficiency of each coke oven is about 76%, so 24% of the heat is not used; among them, the heat wasted by the surface heat dissipation of the coke oven accounts for about 11% of the unused heat; It not only causes a waste of energy, but also causes heat pollution. [0003] On the one hand, the surface heat dissipation of the coke oven is caused by the operation process, such as the heat dissipation caused by the roof area, combustion chamber area, furnace bottom area and regenerator area of ​​the coke oven and the opening of the furnace door during the coke pushing operation; On the one hand, it is caused by the heat dissipation of the coke oven body; after the heat insulation of the coke oven ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/04C09D7/61C09D7/62C09D5/08C09D5/18
CPCC09D183/04C09D7/61C09D7/70C09D7/62C09D5/08C09D5/18C08K2201/011C08K2003/221C08K2003/2213C08K3/34C08K7/26C08K9/10C08K7/24C08K3/22
Inventor 孟晓东丁毅汪琴沈华军周有恒
Owner 江苏龙冶节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com