Slow-release urea fertilizer containing alginate oligosaccharide and preparation method
A technology of brown algae oligosaccharide and slow-release urea, applied in the direction of urea compound fertilizer, nitrogen fertilizer, organic fertilizer, etc., can solve the problems of reducing fertilizer nitrogen utilization rate, increasing soil pH value, easy leaching of nitrate nitrogen, etc. The effect of application amount, improving utilization rate and stimulating growth and development
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0016] Example 1:
[0017] Uroa is a nitrogen source, the preparation of slow-release urea fertilizer containing molar olegose is: the raw material is based on 92 parts of urea particles, 4 yellow oligosaccharides, 0.5 parts of polyteenine, 0.05 serviles (N- Butyl thiophosphorctamine, Nbpt), 5 parts of ethylcellulose copolymer, industrial ethanol solution 500ml; wherein the nitrogen having a nitrogen in urea particles is 50%, the particle size is 0.5 mm; the molecular weight is: 4000, structural formula C4H6NO3 polyteenine.
[0018] Preparation:
[0019] 1) Formulated a suspension solution: 5 parts of the copolymer of ethylcellulose dissolve into 500 mL of industrial ethanol solution, and then 4 drown oligosaccharides, 0.5 parts of polyteenine, 0.05 serviles (N-butyl) The phosphorimide, NBPT) is mixed and uniformly added, and the mixed copolymer is stirred into a mixed suspension solution and standby.
[0020] 2) Use fluidized bed coating technology to place a well-prepared mixed ...
Example Embodiment
[0021] Example 2:
[0022] The urea is a nitrogen source, and it is prepared to prepare a slow-release urea fertilizer containing tweet oligosaccharide: the raw material is based on 92 servinals, and 4 nitrose oligosaccharides, 0.5 parts of polyteenine, 0.05 parts nitrification inhibitor (3, 4-dimethylpyrazole phosphate, DMPP), 5 parts of an ethylcellulose copolymer, industrial ethanol solution 500ml; wherein the nitrogen having a nitrogen in urea particles is 50%, the particle size is 0.5 mm; the molecular weight is: 4000, Polyteenine of structural formula C4H6NO3.
[0023] Preparation:
[0024] 1) Formulated suspension: 5 parts of the copolymer of ethylcellulose dissolve into 500 ml of industrial ethanol solution, and then 4 drown ol oligosaccharides, 0.5 parts of polyteenine, 0.05 parts nitrification inhibitor (3, 4- Dimethylpyrazole phosphate, DMPP) mixed and uniformly added, stirred and uniform copolymers composition mixed suspension solution, to be used.
[0025] 2) Use flui...
Example Embodiment
[0026] Example 3:
[0027] Uroa is a nitrogen source, the preparation of slow-release urea fertilizer containing molar olegose is: the raw material is based on 92 parts of urea particles, 4 yellow oligosaccharides, 0.5 parts of polyteenine, 0.05 serviles (N- Butyl thiophosphorimine, Nbpt) and nitrification inhibitor (3,4-dimethylpyrazolium phosphate, DMPP) mixture, 5 parts of ethylcellulose copolymer, industrial ethanol solution 500ml; urea particles The nitrogen is 50%, the particle size is 0.5 mm; the molecular weight is: 4000, the polyteenine of the structural formula C4H6NO3.
[0028] Preparation:
[0029] 1) Formulated a suspension solution: 5 parts of the copolymer of ethylcellulose dissolve into 500 mL of industrial ethanol solution, and then 4 drown oligosaccharides, 0.5 parts of polyteenine, 0.05 serviles (N-butyl) The mixture of phosphorimine, NBPT) and nitrification inhibitors (3,4-dimethylpyrazolic acid salts, DMPP) were mixed, and the uniform copolymer was stirred, an...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap