Floor tile made of oil field sludge and its production process

A production method and technology for oilfield sludge, applied in sludge treatment, chemical instruments and methods, water/sludge/sewage treatment, etc. The curing strength does not meet the requirements of building bricks, etc.

Inactive Publication Date: 2005-08-24
UNIV OF JINAN
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the existing technology, on the one hand, the curing strength cannot meet the requirements of building bricks, on the other hand, it cannot meet the requirements of ecological building materials, and its alkalinity, toxicity test, and radioactivity test do not meet the building material standards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Floor tile made of oil field sludge and its production process
  • Floor tile made of oil field sludge and its production process
  • Floor tile made of oil field sludge and its production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] The ratio of raw materials in this embodiment is 30% of oilfield sludge, 40% of river sand, 26% of cement, and 4% of curing agent.

[0064] Wherein, the curing agent is mixed with the raw materials in the following weight ratio:

[0065] Sulfoaluminate: 22% Calcium Stearate: 5%

[0066] Calcium Chloride: 20% Calcium Acetate: 0

[0067] Fluorite: 0 Gelatin: 5%

[0068] Gypsum: 20% Lime: 18%

[0069] Acrylic resin 0

[0070] Core material: 10%

[0071] CaO

[0072] The production method is:

[0073] a) Colored cement is used for the color surface, and it is fully mixed with white gravel at a ratio of 1:2.5, and water is added to mix evenly according to the water-cement ratio of 0.5 to make a slurry; inject the slurry into the mold with a thickness of 1-2cm, and place it for half an hour ;

[0074] b) Mix the above-mentioned oilfield sludge, river sand, cement, fly ash, and curing agent evenly, inject it into the above-mentioned mold, vibrate on the vibrat...

Embodiment 2

[0079] The raw material ratio of the matrix in this embodiment is 40% of oilfield sludge, 20% of river sand, 20% of cement, 19% of fly ash, and 2% of curing agent.

[0080] Wherein, the curing agent is mixed with the raw materials in the following weight ratio:

[0081] Sulfoaluminate: 15% Calcium Stearate: 2%

[0082] Calcium Chloride: 10% Calcium Acetate: 15%

[0083] Fluorite: 10% Gelatin: 9%

[0084] Gypsum: 10% Lime: 25%

[0085] Acrylic 4%

[0086] The production method is the same as in Example 1, and the floor tiles are made.

[0087] The performance test results are: the average compressive strength is 22.28, the water absorption rate is 7.34%, and the bulk density is 1.96g / cm 3 . Its mechanical properties can still meet the relevant national standards. Other properties are substantially the same as in Example 1.

Embodiment 3

[0089] The ratio of raw materials in this embodiment is 55% of oilfield sludge, 20% of river sand, 18% of cement, and 7% of curing agent.

[0090] Wherein, the proportioning of curing agent is:

[0091] Sulfoaluminate: 20% Calcium Stearate: 5%

[0092] Calcium Chloride: 15% Calcium Acetate: 10%

[0093] Fluorite: 0 Gelatin: 5%

[0094] Gypsum: 15% Lime: 10%

[0095] Acrylic resin 0 Monoethylene glycol 5%

[0096] Sucrose 5%

[0097] Core material: 10%

[0098] Wherein the core material is made up of the following raw materials in weight percentage:

[0099] CaO

MgO

Fe 2 o 3

SiO 2

Al 2 o 3

Al 2 (SO 4 ) 4

Na 2 CO 3

FeSO 4

MgSO 4

5

5

6

15

12

20

20

7

10

[0100] The production method is the same as in Example 1, and floor tiles are obtained.

[0101] The performance test results are: the average compressive strength is 28.28, the water absorption rate i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
water absorptionaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The present invention relates to floor tile, and is especially floor tile made of oil field sludge and curing agent and its production process. The floor tile has the main material comprising oil field sludge 30-60 wt%, river sand 15-40 wt%, cement 15-30 wt%, flyash 0-35 wt% and curing agent 1-8 wt%. The floor tile of the present invention has high strength and no pollution and reaches the requirement of protecting ecological environment. The present invention solves the problem of pollution caused by oil field sludge, and the floor tile producing process is simple.

Description

(1) Technical field [0001] The invention relates to a floor tile and a production method thereof, in particular to a floor tile made from oil field sludge and a production method thereof. (2) Background technology [0002] Oil well mud is the blood of oil drilling engineering. With the development of the petroleum industry, the output of oil well mud is increasing, and these numerous oil well muds generally contain a large amount of heavy metals, oils, alkalis and chemicals (including organic matter) substances that are extremely harmful to humans, animals and the environment. If mud is discarded after use, if it is not treated, these substances will seriously pollute the environment, endanger people's life and health, and affect the growth and development of animals and plants. [0003] The treatment and application of oily sludge is a difficult problem in the process of oily sewage treatment. Western Europe and the United States have used biotechnology, physical and chem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B28B1/08C02F11/00C04B18/04C04B18/08C04B22/14C04B24/28C04B28/02
CPCC04B2103/10C04B2111/60C04B2111/00612C04B28/02Y02W30/91C04B7/323C04B14/068C04B18/0418C04B18/08C04B22/064C04B22/124C04B22/126C04B22/143C04B24/04C04B24/085C04B24/14C04B24/2641C04B40/0067C04B18/049C04B22/0093
Inventor 岳云龙杨中喜吴波陶文宏宋廷寿隋肃
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com