Method for preparing conductive polyaniline electromagnetic interference screening paint

An electromagnetic interference shielding, conductive polyaniline technology, applied in conductive coatings, polyester coatings, reflective/signal coatings, etc., can solve problems such as decreased electromagnetic interference shielding effectiveness, large proportion of metal fillers, and difficulty in melting

Inactive Publication Date: 2006-08-30
XI AN JIAOTONG UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many deficiencies in the metal-based electromagnetic interference shielding coatings widely used at present
First, the skin depth of metal materials is shallow, so that the shielding effect is mainly due to reflection loss, which limits their application in absorption-based occasions, such as military applications; second, the metal fillers used in coatings (such as powder, Flake or fibrous silver, nickel, copper, etc.) are expensive, and the manufacturing process is complicated and difficult to process; third, the metal filler has a large proportion, and there are certain difficulties in the transportation and long-term storage of the coating; fourth, the metal filler is prone to Migration or corrosion will cause a sharp drop in EMI shielding effectiveness, which is not conducive to the miniaturization of electronic products; fifth, the density of metal fillers is high, and the resulting coating will significantly increase the weight of the product, which limits its application in aerospace and other fields
[0004] Polyaniline is a conductive polymer material with low density (about 1.3g / cm 3 ), simple synthesis, good environmental stability, etc., but its application is limited due to its poor solubility and difficulty in melting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Example 1: Add 10 parts by mass of aniline monomer to 400 parts by mass of hydrochloric acid solution with a concentration of 20% by mass, and stir for 5 minutes; at 20°C, under constant stirring, gradually add 100 parts by mass of A hydrochloric acid solution of ammonium persulfate with a concentration of 15%, continue to react for 0.5h after adding, filter and wash to remove water-soluble impurities, and dry at 40°C to obtain a dry powder; place the above-mentioned dry powder in a concentration of 5% by mass Treat in ammonia water for 1 hour, add the amount of ammonia water so that the pH value of the treatment solution is 9, filter and wash until the filtrate is neutral, and dry at 50°C to obtain polyaniline or polyaniline-wrapped composite particles; take the above-mentioned 100 parts of particles, mixed with 30 parts of p-toluenesulfonic acid solution with a concentration of 0.5M, stirred for 3 hours, filtered, and dried under vacuum at 40°C to obtain conductive pol...

Embodiment 2

[0012] Example 2: Add 15 parts by mass of aniline monomer to 600 parts by mass of sulfuric acid solution with a mass percent concentration of 30%, and stir for 10 minutes; Micron polyacrylic acid resin powder is added to the above system; under uniform stirring, gradually add 80 parts by mass of potassium dichromate nitric acid solution with a concentration of 3% by mass, continue to react for 4 hours after adding, filter and wash to remove water-soluble Drying at 46°C to obtain a dry powder; place the above obtained dry powder in ammonia water with a concentration of 1% by mass for 1.5 hours, add the amount of ammonia water so that the pH of the treatment solution is 8, filter and wash after the end Until the filtrate is neutral, dry at 46°C to obtain polyaniline or polyaniline-wrapped composite particles; take 100 parts of the above particles by mass, mix with 60 parts of acetic acid with a concentration of 0.5M, stir for 2 hours, and filter after the end. Dry under vacuum c...

Embodiment 3

[0013] Example 3: Add 15 parts by mass of aniline monomer to 500 parts by mass of nitric acid solution with a concentration of 50% by mass, and stir for 20 minutes; Add micron polymethacrylic resin powder into the above system; under uniform stirring, gradually add 60 parts of sulfuric acid solution of potassium permanganate with a concentration of 10% by mass, continue to react for 2.0h after adding, filter and wash to remove water-soluble Impurities were dried at 42°C to obtain a dry powder; the above-mentioned dry powder was placed in ammonia water with a mass percentage concentration of 6% for 1.3 hours, and the amount of ammonia water was added to make the pH value of the treatment solution 8. After the end, it was filtered and washed to The filtrate is neutral, and dried at 48°C to obtain polyaniline or polyaniline-wrapped composite particles; take 100 parts of the above particles in parts by mass, mix with 2 parts of perchloric acid with a concentration of 0.5M, and stir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

Disclosed is a method for preparing a conducting polyanion electromagnetic disturbance shielding coating, which uses conducting high molecular polyanion as the main conducting component, thermoplasticity resin as the mains film forming substance. The polyanion electromagnetic disturbance shielding coating has solved problems existing in that belongs to metal system,with advantages like light weigh,low prince good stability,convenient strange and constrction. Bsides,it does not need to used polyanion solution,making the application of conducting polyanion easier, more convenient and have lower cost. Mixing polyanion with different conductivity and inorganic filler can realize electromagnetic disturbance shielding with wider range of frequency, with higher shielding effect.

Description

technical field [0001] The invention relates to a preparation method of an electromagnetic interference shielding paint, in particular to a preparation method of a conductive polyaniline electromagnetic interference shielding paint. Background technique [0002] At present, the problem of electromagnetic interference (EMI) (also called electromagnetic pollution) caused by the widespread use of more and more electronic instruments, computers and radio communication equipment is becoming more and more serious. The harm caused by EMI is mainly manifested in the following aspects: (1) It is easy to cause various electronic equipment to malfunction, distort signals such as images or sounds, or even fail to work; (2) Shorten the service life of electronic equipment or cause electronic equipment (3) Common electrical appliances such as mobile phones, computers, game consoles, microwave ovens, televisions and other sources of electromagnetic radiation, the strong radiation formed po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D179/02C09D167/00C09D5/24C09D5/33
Inventor 井新利王杨勇
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com