Modified paint

A coating and modification technology, applied in coatings and other directions, can solve problems such as poor air permeability, damage to the health of construction workers and users, and cumbersome construction, and achieve the effects of improving anti-aging, excellent leveling, and excellent capacity.

Inactive Publication Date: 2005-12-28
闫俊杰 +1
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the traditional coating is a single film that adheres to the surface of the material, has poor air permeability and is easy to peel
Also, each paint is only suitable for one material medium
Replacing the material requires changing the paint, and the construction is cumbersome
Most of the traditional organic coatings are toxic and damage the health of construction workers and users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] 16 kg of acrylate, 10 kg of water, 0.1 kg of toluidine red, 50 kg of titanium dioxide, 4 kg of polyhydroxylate, 5 kg of water-soluble polyacrylic acid-methacrylic acid, 2 kg of ethylene glycol, 1.7 kg of fatty acid ester, Silicone 10 kg, pentachlorophenol 2.5 kg, ammonia water 0.1 kg, propylene glycol 0.1 kg.

[0037] The above-mentioned components are weighed according to the quantity and set aside. Water, toluidine red, and titanium dioxide are dispersed and beaten at high speed at 2000 rpm. 2000 rpm high-speed grinding slurry to a particle size of 1 nanometer. Add acrylate, polyhydroxy acid salt, ethylene glycol, silicone, pentachlorophenol, water-soluble polyacrylic acid-methacrylic acid, ammonia water, propylene glycol at a constant speed, and stir at a constant speed of 800 rpm until it is liquid and uniform.

Embodiment 2

[0039] 6 kg of acrylate, 60 kg of water, 0.5 kg of light chrome yellow, 20 kg of pearl powder, 0.7 kg of potassium tripolyphosphate, 10 kg of non-ionic polyether oligomers, 0.1 kg of propylene glycol, 0.7 kg of emulsified silicone oil, butyl acetate 1.69 kg of acid cellulose, 0.2 kg of trichloroethylene, 0.01 kg of 2-amino-2-methyl-1-propanol, and 0.1 kg of propylene glycol.

[0040] The above-mentioned components are weighed according to the quantity and set aside. Disperse water, light chrome yellow, and pearl powder at high speed at 2000 rpm to form a slurry. Grind the slurry at high speed to a particle size of 0.1 nm. Add acrylate, potassium tripolyphosphate, non-ionic polyether oligomer, propylene glycol, emulsified silicone oil, cellulose acetate butyrate, trichloroethylene, 2-amino-2-methyl-1-propanol, propylene glycol at a uniform speed , Stir at a constant speed of 800 rpm until it is liquid and uniform.

Embodiment 3

[0042] Acrylate 25 kg, water 25 kg, molybdenum red 2.5 kg, aluminum powder 12 kg, polyacrylic acid sodium salt 5 kg, urethane modified polyether oligomer 0.2 kg, ethylene glycol monobutyl ether 10 kg, tributyl phosphate 1.3 kg, silicone 5 kg, sodium benzoate 4 kg, sodium bicarbonate 5 kg, propylene glycol 5 kg.

[0043] The above-mentioned components are weighed according to the quantity and set aside. Water, molybdenum chrome red, and aluminum powder are dispersed and beaten at high speed at 2000 rpm. Grind the slurry at high speed to a particle size of 0.5 nm. Add acrylate, polyacrylic acid sodium salt, urethane modified polyether oligomer, ethylene glycol monobutyl ether, tributyl phosphate, silicone, sodium benzoate, sodium bicarbonate, propylene glycol at a uniform speed, 800 rpm Stir at a constant speed until the liquid becomes uniform.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

A modified coating consists of acrylate 6-60wt%, water 10-60wt%, aggregate 12-50wt%, wetting disperser 0.01-5wt%, thickener 0.2-10wt%, film forming agent 0.1-10wt%, anti-bubbling agent 0.07-1.7wt%, anti-shrinking leveling agent 0.1-10wt%, fungicidal bactericide 0.02-4wt%, pH regulator 0.01-5wt%, propanediol 0.1-5wt%, pigment and dye. Particle diameter of mixed components is 0.1-1 nanometer. The process is carried out by proportioning the components. Its advantages include simple, non-toxic, good anti-aging and pollution preventive performances, and better air permeability.

Description

technical field [0001] The invention relates to a paint, more specifically, to a paint that can be applied to various materials and optimize the surface of the original material. Background technique [0002] At present, the traditional coating is a single film that adheres to the surface of the material, has poor air permeability and is prone to peeling. Also, each paint is only suitable for one material medium. To change the material, the paint needs to be changed, and the construction is cumbersome. Most of the traditional organic coatings are poisonous and damage the health of construction workers and users. Contents of the invention [0003] The purpose of the invention is to overcome the deficiencies in the prior art and provide a non-toxic and easy-to-use modified coating which can be applied to various material media. [0004] The present invention realizes through following technical scheme: [0005] A modified paint, comprising the following components by wei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D191/00
Inventor 闫俊杰全玉兰
Owner 闫俊杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap