Alkyd paint for ship cabin and its production process

An alkyd resin and paint technology, applied in the direction of biocide-containing paints, coatings, antifouling/underwater coatings, etc., can solve the problems of harmful substances in paints, environmental pollution, etc., and improve temperature resistance and mechanical properties. , the effect of large heat absorption

Inactive Publication Date: 2006-08-02
梁新方
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the shortcomings of the paint in the prior art that contains harmful substances to the human body, to develop a safe, low-toxic, non-polluting paint, and to solve the problem of smoke and gas released by the paint film when it is baked or burned at a high temperature. The harm of toxic substances to the human body and the pollution of the environment, improve the safety performance and temperature resistance of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Embodiment 1: the preparation of silicone resin

[0054] Add 412 parts of water, 30 parts of butanol and 41 parts of xylene to the reaction kettle and start stirring. Mix 62.5 parts of phenyltrichlorosilane and 165.0 parts of methyldichlorosilane and 165 parts of xylene in a container and mix them evenly in a container. Hours added. Cool the jacket of the reaction kettle with cold water to control the temperature of the liquid material in the kettle not to exceed 22°C. After the dropwise addition, stop stirring and let it stand for 1 hour to separate the liquid in the kettle, release the water layer, and then add clean water to stir for washing . Set aside to settle and separate layers, turn on water, and wash until neutral, and the acid value is less than 1mgKOH / g. Finally, put the silicone resin liquid into the distillation pot for vacuum distillation to remove water and part of the solvent, control the temperature not to exceed 70°C, concentrate until the non-vola...

Embodiment 2

[0055] Embodiment 2: the preparation of alkyd resin

[0056] Add 53 parts of soybean oil and 8 parts of linseed oil or tung oil into the reaction kettle, stir to raise the temperature, and introduce CO 2, heat up to 120°C, add 0.02-0.04 parts of lithium hydroxide, continue to heat up to 240°C, add 15.5 parts of pentaerythritol, keep warm at 230-240°C for alcoholysis reaction, take a sample to measure the tolerance after one hour. The method for measuring tolerance is: mix 1 volume of sample with 5 volumes of 95% ethanol in a 100ml beaker, and the solution becomes clear and transparent at about 25°C, indicating that the alcoholysis is complete. After the alcoholysis is completed, cool down to 160°C, add 26.9 parts of phthalic anhydride and 6 parts of xylene, heat up to 200±2°C for 1 hour, then raise the temperature to 220°C for reflux dehydration, keep warm at 230°C, and take samples for determination according to The following method is used to measure the acid value and visc...

Embodiment 3

[0067] Embodiment 3: Preparation of silicone resin modified alkyd resin

[0068] Add 25 parts of the silicone resin produced in step 1.1 and 75 parts of the alkyd resin produced in step 1.2 into the reaction kettle, raise the temperature to 173-175°C, azeotropically separate water, drain the water and raise the temperature to 190 ~200℃ heat preservation reaction. Take the sample and xylene and dissolve it evenly in a weight ratio of 6:4. Use a Grignard tube to measure the viscosity at 25°C. When the viscosity reaches 2.5 to 3 seconds, stop heating, cool below 140°C, dissolve with solvent gasoline and dilute to a solid content of 55± 2% resin solution, filtered.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
acid valueaaaaaaaaaa
flash pointaaaaaaaaaa
Login to View More

Abstract

The present invention discloses one kind of paint for steel structure surface of ship and its production process. The paint has the main components including organic silicon resin modified alkyd resin, phenolic resin modified alkyd resin, pigment, nanometer zinc oxide, superfine aluminum hydroxide, superfine barium sulfate, nanometer silica, paint drier, No. 200 solvent gasoline and methyl ethyl ketoxime. The production process includes dispersing all the materials except paint drier and methyl ethyl ketoxime in a cylinder for 15 min, sand grinding to fineness superior to 40 microns, regulating with resin and paint drier to acid value not greater than 11 mgKOH / g and viscosity of 200-400 sec at 25 deg.c, filtering, packing while adding methyl ethyl ketoxime. The present invention solves the problem of paint film to release fume and toxic matter and has high safety performance and heat resistance.

Description

technical field [0001] The invention relates to a paint and a manufacturing method thereof, in particular to a paint for a ship and a steel structure surface with safety and health requirements on land and a manufacturing method thereof. Background technique [0002] In the current paint manufacturing process, benzene series solvents are often used as solvents, which not only cause harm to the human body during construction, but also produce harmful chemical substances when subjected to high temperature baking or fire. Contents of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the paint in the prior art that contains harmful substances to the human body, to develop a safe, low-toxic, non-polluting paint, and to solve the problem of smoke and gas released by the paint film when it is baked or burned at a high temperature. The harm of toxic substances to the human body and the pollution of the environment can be improved, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D183/00C09D5/16
Inventor 梁新方
Owner 梁新方
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com