Process for synthesis of nano mordenite molecular sieve

A synthesis method, the technology of denzeolite, which is applied in the field of synthesis of nano-mordenite molecular sieves, can solve the problems of high cost, slow progress, and environmental pollution, and achieve the effect of reducing synthesis cost, less pollution, and good catalytic performance

Inactive Publication Date: 2006-09-27
NANKAI UNIV
View PDF1 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This synthesis method requires the use of organic ammonium ion compounds as templates, which is costly and pollutes t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for synthesis of nano mordenite molecular sieve
  • Process for synthesis of nano mordenite molecular sieve
  • Process for synthesis of nano mordenite molecular sieve

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] First take 5 ml of silica sol solution (SiO 2 : 30wt%, Qingdao Marine Chemical Co., Ltd. provides), 2 milliliters of deionized water, 0.7 milliliters of concentration is (8.036mol / l) sodium hydroxide solution mixes evenly and stirs 1.5 hours; Then get the same sodium hydroxide solution of 0.81 milliliters of concentrations, 1 ml of deionized water and 0.325 g of sodium metaaluminate (Al 2 o 3 : 41wt%, Na 2 (2: 30wt%) and mix evenly, add the sodium metaaluminate solution to the evenly dispersed silica sol solution, then add 5.3 milliliters of deionized water, stir vigorously continuously for 1 hour, add 3.48 grams of sodium chloride, and continue stirring until after 1 hour , add 0.163g mordenite molecular sieve powder as crystal seed, continue to stir for 45 minutes and measure the pH value at about 13, the molar composition of the crystallization reaction system is:

[0027] Na 2 O:NaCl:Al2 o 3 : SiO 2 :H 2 O=3:30:1:15:390 Stirring and aging at room temperature ...

Embodiment 2

[0029] First take 5 ml of silica sol solution (SiO 2 : 30wt%, provided by Qingdao Ocean Chemical Co., Ltd.), 2 milliliters of deionized water, 1 milliliter of concentration is (8.036mol / l) sodium hydroxide solution mixes evenly and stirs 1.5 hours; Then get the same sodium hydroxide solution of 1.12 milliliters of concentrations, 1 ml of deionized water and 0.325 g of sodium metaaluminate (Al 2 o 3 : 41wt%, Na 2 (2: 30wt%) and mix evenly, add the sodium metaaluminate solution to the uniformly dispersed silica sol solution, then add 2.2 ml of deionized water, stir vigorously for 1 hour, add 3.48 grams of sodium chloride, and continue stirring until after 1 hour , add 0.131g mordenite molecular sieve powder as the seed crystal, continue stirring for 60 minutes and then measure the pH value at about 13.5, the molar composition of the crystallization reaction system is:

[0030] Na 2 O:NaCl:Al 2 o 3 : SiO 2 :H 2 O = 4.2: 30: 1: 15: 270 Stirring and aging at room temperatur...

Embodiment 3

[0032] First take 5 ml of silica sol solution (SiO 2 : 30wt%, Qingdao Marine Chemical Co., Ltd. provides), 2 milliliters of deionized water, 0.7 milliliters of concentration is (8.036mol / l) sodium hydroxide solution mixes evenly and stirs 1.5 hours; Then get the same sodium hydroxide solution of 0.81 milliliters of concentrations, 1 ml of deionized water and 0.244 g of sodium metaaluminate (Al 2 o 3 : 41wt%, Na 2 (2: 30wt%) and mix evenly, add the sodium metaaluminate solution to the uniformly dispersed silica sol solution, then add 3.2 ml of deionized water, stir vigorously for 1 hour, add 4.64 grams of sodium chloride, and continue stirring until after 1 hour , add 0.141g mordenite molecular sieve powder as the seed crystal, continue to stir for 45 minutes and measure the pH value at about 12.5, the molar composition of the crystallization reaction system is:

[0033] Na 2 O:NaCl:Al 2 o 3 : SiO 2 :H 2 O=3:40:1:20:330 Stir and age at room temperature for 4 hours, tran...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The inventon discloses a method of Nanomercerization zeolite molecular sieve. Containing steps as follows: magnetic stirring and dispersing the silicasol in strong caustic lye for a period of time, mixing the even dispersed silicon fountain and aluminium fountain to glue in room temperature, taking common mercerization zeolite molecular sieve powder as seed crystal, natrii chloridum or sulfuric acid disodium metal salt as additive, strong magnetic stirring aging for 2-6h in room temperature, low temperature ageing for 3-24h in 100Deg C, and then crystallization in 130-150Deg C, the crystallization time is 22-80h, the pH value of reaction system>12, finally collecting naonodimension mercerization zeolite molecular sieve from reaction product.

Description

technical field [0001] The invention relates to the synthesis of zeolite molecular sieves, in particular to a synthesis method of nanometer mordenite molecular sieves. Specifically, it is a method for synthesizing nanometer mordenite molecular sieves by adding metal salts as nucleation accelerators and adjusting synthesis conditions without using organic ammonium as a template. Background technique [0002] Nanotechnology is a high-tech technology born in the 1980s. Nanoparticles refer to particles with a particle diameter ranging from 0.1 to 100nm. The ratio of the number of atoms on the surface of nanomaterials to the total number of atoms in the bulk increases sharply with the decrease of particle size, showing obvious volume effect, surface effect and quantum size effect. It is a new material with unique physical and chemical properties. . [0003] As a new type of nanomaterial, nano zeolite has attracted much attention. This is mainly due to the fact that nano molecu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B39/26B82B3/00
Inventor 邢淑建项寿鹤
Owner NANKAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap