A technology of diisopropyl diethyl carboxylate and diisopropyl malonate, which is applied in the preparation and application fields of diisopropyl diethyl carboxylate, can solve the problem of environmental pollution and long process , Affect the popularization and application of citrate plasticizers, and achieve the effect of mild reaction conditions and simple post-treatment process

Inactive Publication Date: 2007-06-06
JINGGANGSHAN UNIVERSITY
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional synthesis method of citrate plasticizers is to use citric acid and corresponding alcohols in the presence of sulfuric acid as a catalyst. Currently, the raw material citric acid is mainly prepared by microbial fermentation. This method has a long process, especially for producing A large amount of organic pol...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Prepn and application of diisopropyl diethyl carboxylate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 1) Add diisopropyl malonate into ethanol solution of 19.5% sodium ethoxide by mass percentage under stirring, the molar ratio of diisopropyl malonate to sodium ethoxide is 1:2.05, heat up to 85°C and react for 20 minute;

[0028] 2) add catalyst potassium iodide, the mass ratio of potassium iodide and diisopropyl malonate is 1: 160;

[0029] 3) Ethyl bromoacetate was added dropwise, the molar ratio of ethyl bromoacetate to diisopropyl malonate was 2.02:1, the addition time was 20 minutes, reacted at 85°C for 3 hours, and cooled to room temperature;

[0030] 4) adding water to dissolve the separated inorganic salts, separating the oil layer and distilling under reduced pressure to collect products in the boiling point range, while reclaiming unreacted raw materials and solvent ethanol. The yield was 88% based on diisopropyl malonate.

Embodiment 2

[0032] 1) Add the methanol solution of 19.0% sodium methoxide to diisopropyl malonate under stirring, the molar ratio of diisopropyl malonate to sodium methoxide is 1:2.08, heat up to 80°C and react for 20 minute;

[0033] 2) adding catalyst elemental iodine, the mass ratio of elemental iodine to diisopropyl malonate is 1: 150;

[0034] 3) Ethyl chloroacetate was added dropwise, the molar ratio of ethyl chloroacetate to diisopropyl malonate was 2.01:1, the time for the addition was 25 minutes, reacted at 80°C for 10 hours, and cooled to room temperature;

[0035] 4) filter the separated out inorganic salt, distill under reduced pressure, collect the product of boiling point range, reclaim unreacted raw material and solvent methanol simultaneously. The yield was 84% ​​based on diisopropyl malonate.

Embodiment 3

[0037] 1) Add diisopropyl malonate into methanol solution with a mass percent concentration of 20.5% sodium methoxide under stirring, the molar ratio of diisopropyl malonate to sodium methoxide is 1:2.10, heat up to 82°C for 15 minute;

[0038] 2) adding catalyst element potassium iodide, the mass ratio of potassium iodide and diisopropyl malonate is 1: 100;

[0039] 3) Ethyl chloroacetate was added dropwise, the molar ratio of ethyl chloroacetate to diisopropyl malonate was 2.00:1, the time for the addition was 15 minutes, reacted at 82°C for 9 hours, and cooled to room temperature;

[0040] 4) filter the separated out inorganic salt, distill under reduced pressure, collect the product of boiling point range, reclaim unreacted raw material and solvent methanol simultaneously. The yield was 85% based on diisopropyl malonate.

[0041] Examples of the application of DDPTC as a plastic plasticizer are as follows:

[0042] After mixing polyvinyl chloride (PVC) powder, DDPTC, co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention is preparation process and application of diisopropyl diethyl carboxylate. Diisopropyl malonate and ethyl chloroacetate as the initial material are one-step reacted under the action of strong alkali and catalyst to synthesize diisopropyl diethyl carboxylate. After reaction, the reaction product is filtered, water washed to eliminate inorganic salt and decompression distilled to obtain the product. Diisopropyl diethyl carboxylate is colorless or yellowish transparent liquid, and has structure similar to that of triisopropyl acetyl citrate, plasticizing efficiency and cold resistance similar to that of DOP and compatibility higher than that of DOP. The present invention is used as plasticizer.

Description

technical field [0001] The invention relates to a preparation method and application of diisopropyl diethyl carboxylate. Background technique [0002] With the improvement of environmental protection awareness in various countries in the world, plastic products such as medicine and food packaging, daily necessities, toys, etc. have put forward higher purity and sanitation requirements for the main plasticizer dioctyl phthalate DOP. DOP has a potential carcinogenic risk, and international measures have been taken to limit the scope of use of DOP: the U.S. Environmental Protection Agency has stopped the use of six phthalate plasticizers according to the research results of the National Cancer Institute. Industrial production; the Swiss government has decided to ban the use of DOP in children's toys; Germany has banned the use of DOP in all plastic products related to the human body and hygienic food; in Japan, DOP as a plastic additive is limited to industrial plastic products...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C07C69/34C07C67/00C07C67/333C08K5/11
Inventor 曾锡瑞隋岩李新发方小牛
Owner JINGGANGSHAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap