Water PVDC latex specially for painting special cloth and its preparing method

A special fabric and coating technology, applied in textiles and papermaking, etc., can solve the problem of inability to meet the requirements of non-woven fabrics, and achieve the effects of good elasticity, good water resistance and uniform diameter

Inactive Publication Date: 2007-06-27
ZHEJIANG SENLANDE PACKAGING TECH
View PDF1 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high hygroscopicity of the emulsion after drying, it cannot meet the requirements of non-woven fabric treatment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Name Quantity (kg)

[0038]

[0039] Kettle material:

[0040] Deionized water 80

[0041] Sodium alkylsulfonate 0.5

[0042] A small amount of co-reducing agent

[0043] Organic peroxide 0.004

[0044]

[0045] Mixed monomer:

[0046] Vinylidene chloride (VDC) 85

[0047] Methacrylic acid (MAA) 1

[0048] 2-ethylhexyl acrylate (2EHA) 14

[0049] Emulsifier: OP-10 6

[0050] soft water 20

[0051]

[0052] Initiator:

[0053] Initiator A: tert-butyl hydroperoxide 0.080

[0054] Deionized water 10

[0055] Initiator B: carved white powder 0.070

[0056] Deionized water 10

[0057] The specific operation process: first add 80 kg of deionized water, a small amount of co-reducing agent, and 500...

Embodiment 2

[0059] Repeat Example 1, the difference between this embodiment and Example 1 is that the components of the mixed monomers are:

[0060] (1) Vinylidene chloride (VDC), the dosage is 80kg;

[0061] (2) methacrylic acid (MAA), consumption is 2kg;

[0062] (3) 18 kg of isooctyl acrylate.

Embodiment 3

[0064] Repeat Example 1, the difference between this embodiment and Example 1 is that the components of the mixed monomers are:

[0065] (1) Vinylidene chloride (VDC), the dosage is 80kg;

[0066] (2) methacrylic acid (MAA), consumption is 4.5kg;

[0067] (3) 15.5 kg of isooctyl acrylate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to water-thinned PVDC latex, and is especially a kind of water-thinned PVDC latex for painting special cloth and its preparation process. The water-thinned PVDC latex is prepared with mixed monomer through emulsion polymerization in the presence of emulsifier and initiator. The mixed monomer includes vinylidene chloride 75-90 %, acrylate monomer 8-20 % and unsaturated fatty acid 1-5 %. The water-thinned PVDC latex is used in treating non-woven fabric, and the treated non-woven fabric is hard, elastic, waterproof, heat resistant and crease resistant and may be used widely. In addition, the water-thinned PVDC latex has excellent compatibility with acrylic acid emulsion.

Description

technical field [0001] The invention relates to a water-based PVDC latex, in particular to a special water-based PVDC latex for coating on special cloth and a preparation method thereof. Background technique [0002] At present, in the treatment agent of non-woven fabrics, a single acrylic emulsion treatment agent is mainly used. This type of treatment agent has excellent adhesion, durability and softness. However, as the market changes, the requirements of users are also different. In the past, the treated non-woven fabric was required to be relatively soft, but now it is gradually turning to be relatively hard, full of good elasticity, and also has good water resistance and heat resistance. properties and wrinkle resistance. For example, it is mainly used for the treatment of tent cloth, the coating of the back of the carpet and the treatment of other non-woven fabrics. [0003] Chinese invention patent (publication number is CN1715559A) discloses a kind of latex for tis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F214/08C08F2/24C08F4/34C08F4/40D06N3/06C08F220/10
Inventor 应忠芳何祥麟阮国富王婧季国华陈荣黄建柳继禹邓焕青
Owner ZHEJIANG SENLANDE PACKAGING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products